长柄扁桃核壳活性炭的制备及表征

以长柄扁桃核壳为原料采用磷酸活化法制备活性炭,分别研究了温度、时间、浸渍比和磷酸浓度对活性炭吸附性能的影响;进而采用氮气吸附曲线和SEM对最佳工艺条件下的活性炭进行了表征。结果表明,长柄扁桃核壳是一种优质的活性炭原料;当温度为400℃,活化时间2 h,浸渍比2：1,磷酸浓度60%时,得到产率为46.46%,碘吸附值和亚甲基蓝吸附值分别为1 073 mg/g、255 mg/g,比表面积高达1 740 m²/g,中孔率为73.12%的孔隙发达的高中孔率活性炭。     

复合沸石滤料的制备及其性能测试

以活化后的天然斜发沸石为主要原料,添加粘合剂、成孔剂等制备出孔隙率高、比表面积大的球型复合沸石滤料。通过正交实验得到最优工艺组合条件为ω沸石粉∶ω粘合剂∶ω成孔剂=55%∶35%∶10%,活化温度为150℃,活化时间为3 h。制备的成品堆积密度为674 kg/m3,筒压强度为4.32 MPa,显气孔率59.02%。较陶粒相比,该滤料用于曝气生物滤池在挂膜启动与稳定运行阶段,均具有较高的氨氮去除效果,且挂膜微生物量高,更适宜作为曝气生物滤池的载体。     

中子活化分析环境样品干扰元素的分离

环境样品使用中子活化法分析,在γ多道测量过程中,常有干扰发生。若将铜载体加入松叶分解液中,可与CH_3CSNH_2反应形成硫化物沉淀,在共沉淀过程中可去除干扰元素。在不同的pH条件下,松叶中各种被测元素的回收率不同。使用放射性核素示踪方法测量,当pH增大时,Ag、Cd和Cu的回收率随之增大,而Sb和As的回收率将减小,Hg的回收率变化不大。     

木浆造纸黑液活化磷矿矿浆生产普钙的研究

利用木浆造纸黑液活化磷矿矿浆,降低矿浆流动起点水分,既简化普钙生产流程,降低普钙生产成本,又能消除造纸黑液污染。试验结果表明：木浆造纸黑液活化磷矿矿浆最佳黑液投入量为0.027mL/g矿粉,当矿浆含水率控制在26％～28％之间时,矿浆粘度可降至0.70Pa·s以下,所生产的鲜钙能满足质量要求。为造纸黑液活化磷矿矿浆生产普钙提供了理论和技术依据     

Adsorption of benzene and toluene from waste gas using activated carbon activated by ZnCl2

A series of activated carbons with high surface area were prepared from walnut shell using chemical activation with ZnCl2. In this research the carbonization stage was carried out at 500℃. The performance of the synthesized carbons evaluated in adsorption of benzene and toluene from waste gas. The influence of impregnation ratio on the characteristics of synthesized activated carbons as well as their adsorption capacity was investigated. The ratio of activation agent to walnut shell was selected in the range of 0.5-2.0 wt/wt. The synthesized activated carbons were characterized using XRD, SEM, BET and FTIR techniques. The highest activated carbon production yield was obtained at impregnation ratio of 1.5 wt/wt. The XRD analysis illustrated that peaks intensity decreased with increasing impregnation ratio showing that amorphous property of samples was increased. The SEM analysis revealed successful pore development in synthesized activated carbons obtained at high impregnation ratios. The surface area of the activated carbons increased with increasing impregnation ratio and its maximum value reached 2643 m2.g 1 at impregnation ratio of 2/1. FTIR analysis indicated that the relative amount of different acidic surface groups on synthesized carbons was a function of impregnation ratio. Experimental results for benzene and toluene adsorption showed a high potential of employing synthesized impregnated activated carbon for treatment of waste gas. Generally, the amount of VOC adsorbed on the surface was affected by physicochemical properties of synthesized activated carbons.     

Cellular response of mouse splenocytes to heavy metals exposure

Among the environmental contaminants recognised for their toxicity and their global presence, heavy metals are certainly a major concern. They can elicit a number of immunomodulatory effects leading ultimately to an enhanced susceptibility (sensitivity) of immune cells to microbial agents and the appearance of neoplastic diseases and autoimmune phenomena. Heavy metals also provoke changes in the function(s) of immune cells. A striking biological effect of heavy metals is the induction of intracellular thiols (cysteine, glutathione, metallothioneins). Thiols are involved in many physiological processes, including protection from free radical damage and detoxification of chemicals. The purpose of this study was to assess the differences of susceptibility (sensitivity) in both pre-activated (concanavalin A was used) and non-pre-activated cells in the presence of heavy metals. Five were evaluated on murine splenocytes. The lymphoblastic proliferation test was performed for lymphocytes and a phagocytosis test for macrophages. Data showed that the levels of thiols in the pre-activated cells are greater than non-pre-activated cells following exposure to various heavy metals; macrophages were more resistant than lymphocytes to the toxic effects of heavy metals, and pre-activated cells were more resistant than cells at rest. One possible explanation is that macrophages produce more thiols than lymphocytes and this provides an increased protection from the deleterious effects of heavy metals.     

Advanced techniques in air pollution†

Specific usage of neutron activation analysis, charged particle analysis, y photons analysis, G.C.M.S. coupling, stable isotope dilution techniques, are discussed.

Dust collected on filters, oxygenated compounds in exhaust gases from car engines, nitrogen oxides, have thus been determined.

Special calibration methods for ozone, and remote detection by Lidar Raman are also described.     

Neutron activation and atomic absorption analysis of Ulva Lactuca and Gracilaria Verrucosa from Thermaikos Gulf,Greece

NAA and AAS have been applied to determine the content of As, Br, Ca, Cd, Co, Cr, Cu, Fe, K, La, Mn, Na, Ni, Pb, Sb, Sc, Sm and Zn in Ulva lactuca and Gracilaria verrucosa from Thermaikos Gulf, Greece. The analytical data has been subjected to cluster and stepwise discriminant analysis. Thus the influence of some industrial sources on the pollution of water in the Gulf is detected and correlation between Zn‐Co‐Cr‐La; Br‐K; Cu‐Ni; Cd‐Sb‐Mn in the investigated algae is established.     

Bioleaching of copper from pre and post thermally activated low grade chalcopyrite contained ball mill spillage

Bioleaching of a low grade chalcopyrite (ball mill spillage material) was tested for copper recovery in shake flasks. The original samples (as received) were thermally activated (600°C, 30 min) to notice the change in physico-chemical and mineralogical characteristics of the host rock and subsequently its effect on copper recovery. A mixed culture of acidophilic chemolithotrophic bacterial consortium predominantly entailing Acidithiobacillus ferrooxidans strain was used for bioleaching studies and optimization of process parameters of both original and thermally activated samples. Mineralogical characterization studies indicated the presence of chalcopyrite, pyrite in the silicate matrix of the granitic rock. Field emission scanning electron microscopy coupled with Energy dispersive spectroscopy (FESEM-EDS) and X-ray Fluorescence (XRF) analysis indicated mostly SiO₂. With pH 2, pulp density 10% w/v, inoculum 10% v/v, temperature 30°C, 150 r·min^-1, 49% copper could be recovered in 30 days from the finest particle size (-1+ 0.75 mm) of the original spillage sample. Under similar conditions 95% copper could be recovered from the thermally activated sample with the same size fraction in 10 days. The study revealed that thermal activation leads to volume expansion in the rock with the development of cracks, micro and macro pores on its surface, thereby enabling bacterial solution to penetrate more easily into the body, facilitating enhanced copper dissolution.