壳聚糖-g-聚丙烯酸/海泡石复合物对Pb2+的去除性能研究

制备了一种壳聚糖接枝聚丙烯酸/海泡石复合吸附剂,考察了吸附剂对Pb2+吸附的pH依赖性、吸附等温线、吸附动力学以及吸附剂的重复使用性能.结果表明,聚丙烯酸成功接枝到壳聚糖骨架上,形成有机-无机复合吸附剂.吸附剂表面呈现粗糙多孔、凹凸不平的形貌,有利于吸附体系更快达到吸附平衡.在pH=6.00、吸附时间30 min、Pb2+溶液初始浓度0.02 mol.L-1和吸附剂用量0.10 g的条件下,复合吸附剂对Pb2+的平衡吸附量达到638.9 mg.g-1,约为海泡石的3倍.重复吸附-脱附5次,复合吸附剂对Pb2+的吸附量下降到489.2 mg.g-1,仍可达初始吸附量的76.6%,而海泡石使用3次之后即对Pb2+丧失吸附性能.与海泡石相比,复合吸附剂具有更高的吸附容量、更快的吸附速率和更好的重复使用性能.     

Heavy metals removal from aqueous solution using carbonaceous K_2S-impregnated adsorbent

A novel carbonaceous adsorbent for heavy metal removal was prepared from raw coal by one-step simple sulfur impregnation using K_2S. Raw coal was mixed with K_2S powder and then heated at 800℃ for 30 min in nitrogen to produce K_2S char. The sulfur content and form in K_2S char were determined, and the ability of K_2S char to adsorb Zn~(2+), Cd~(2+) and Pb~(2+) was examined. The K_2S impregnation was effective at impregnating sulfur into coal, especially in the form of elemental, thiophenic and sulfatic sulfur. The sulfur content of K_2S char was higher than those of raw coal and pyrolysis char. The Zn~(2+) removal in 2.4 mmol/L of Zn~(2+) solution by K_2S char was higher than raw coal with the removal rate of 100%. K_2S char adsorbed Pb~(2+) and Cd~(2+) in 24 mmol/L of Pb~(2+) and Cd~(2+) solution with the removal rate of 97 % and 35 %, respectively. The elution extents of adsorbed Pb~(2+) and Cd~(2+) were zero in distilled water and 27% in 0.1 mol/L HCl solution. These results indicated that an effective adsorbent for heavy metal ions was prepared from coal using K_2S sulfur impregnation, and that the adsorbed metals were strongly retained in K_2S char.     

颗粒海藻酸镧对饮用水中氟的吸附去除

以氯化镧与海藻酸钠为原料,采用滴球法制备了粒径为1～1.5mm的海藻酸镧小球,经过水洗、干燥后得到镧负载量25%(质量分数)的海藻酸镧颗粒吸附剂,应用该吸附剂进行饮用水除氟研究.通过间歇吸附实验,分别进行了吸附速率、pH值影响、吸附等温线、共存离子影响等吸附性能评价,并对吸附前后吸附剂表面与溶液组成变化进行研究.结果表明,该颗粒的吸附速率很快,反应2h后出水氟浓度即逐渐趋于稳定,吸附速率曲线符合拟二级反应速率方程;吸附效果受pH影响显著,在pH=4附近吸附量最大;吸附等温线数据对Langmuir方程拟合较好,其最大吸附量高达197.2mg·g-1;在常见无机干扰离子中,磷酸根与碳酸根对吸附有较大负面影响.SEM照片显示吸附前、后颗粒表面形态差异明显;吸附前、后颗粒表面EDX成分分析及溶液中离子浓度测量结果显示,吸附过程中溶液中F-同时与颗粒表面Cl-及OH-发生离子交换作用.     

Phosphine functionalised multiwalled carbon nanotubes: A new adsorbent for the removal of nickel from aqueous solution

Synthesised triphenylphosphine-linked multiwalled carbon nanotubes (Tpp-MWCNTs) were used to study the adsorption of nickel in aqueous solutions and their adsorption capabilities were compared with purified MWCNTs. The adsorption capacity increased with an increase in pH for all adsorbents. The adsorption equilibrium was reached in 40 and 30 min for purified MWCNTs and Tpp-MWCNTs, respectively. Both Freundlich and Langmuir isotherms used to investigate the adsorption process fitted the experimental data well with the correlation coefficient R² close to 1 for all adsorbents. On the other hand, the experimental data fitted well with a pseudo second-order model. The speciation of nickel also influenced the adsorption on the purified and Tpp-MWCNTs. The adsorbents used in this study showed superior adsorption capacity when compared to other adsorbents reported in the literature.     

硅改性制备疏水性沸石分子筛蜂窝体

通过氢型沸石分子筛粉体与粘结剂、助剂和水混合成面团状后挤压成型,干燥焙烧,再通过四氯化硅疏水改性处理,制备了一种蜂窝状复合沸石分子筛吸附剂.通过低温N2吸附、XRD、吸苯等手段对所制备的分子筛蜂窝体进行表征和评价.结果表明所制备的复合沸石分子筛蜂窝体经过硅改性处理后,硅铝比由4提高至22,比表面和总孔容略降,P/P0=0.95时吸苯量比改性前稍高,达18.05%.相对湿度80%RH条件下（P/P0=0.95）苯的饱和吸附量还能达到15%,与改性前相比增加了1倍多,疏水性优良.     

Bactericidal effects of adsorbent on Escherichia coli for use in disinfection of drinking water

A synergistic action of silver (Ag) and groundnut husk carbon was shown, which markedly enhanced inactivation of Escherichia coli. The purpose of this study was to assess the feasibility of using a silver-impregnated groundnut husk carbon adsorbent (AdSG) for drinking water disinfection and evaluate % disinfection of E. coli. The results showed that contact of bacterial cells with AdSG resulted in a transfer of Ag ion to the cell, as evidenced by bactericidal activity. It is also possible that Ag produced generation of reactive oxygen species in the cell that led to bactericidal activity of the adsorbent. Data indicated that AdSG was effective as a bactericidal agent and may prove to be economically beneficial in drinking water disinfection.     

丁二酰亚胺基修饰的吸附树脂对苯胺的吸附热力学性能

有效去除废水中苯胺及其衍生物是重要的环境问题. 由氯甲基聚苯乙烯树脂与丁二酰亚胺反应,合成大孔交联聚(对乙烯基苄基丁二酰亚胺)树脂(简称丁二酰亚胺树脂),测定了丁二酰亚胺树脂对正庚烷溶液中苯胺的吸附性能. 结果表明:丁二酰亚胺树脂对正庚烷溶液中苯胺的吸附量大于原料树脂. 吸附等温线符合Freundlich等温吸附方程,相关系数大于0.99. 利用热力学函数计算了等量吸附焓变、吸附自由能变和吸附熵变. 树脂对正庚烷中苯胺的等量吸附焓变在20～30 kJ/mol,推测吸附过程为氢键吸附;同时,通过比较树脂对正庚烷溶液中苯胺和N,N-二甲基苯胺的吸附性能的差别,进一步论证了丁二酰亚胺树脂对正庚烷中苯胺的吸附是基于氢键作用的机理.      

钛硅分子筛催化双氧水氧化水中间甲酚

探索催化双氧水氧化去除间甲酚对开发炼油厂碱渣废水处理新技术意义重大。采用钛硅分子筛催化双氧水氧化水中间甲酚,考察了反应时间、反应温度、双氧水加入量、催化剂加入量和初始溶液pH对间甲酚去除率的影响。实验结果表明：钛硅分子筛对双氧水氧化间甲酚具有显著的催化作用;在反应时间为90 min、反应温度为80 ℃、n（H₂O₂）∶n（间甲酚）为4、催化剂加入量为1.5 g/L、初始溶液pH为1.0~11.0的条件下,间甲酚去除率约为94%,间甲酚溶液的BOD₅/COD从氧化前的0.26提高到氧化后的0.38,可生化性显著提高。     

硼泥陶粒处理钢铁高浊度废水的探究

以硼泥、膨润土、粉煤灰、锯末为原材料制备硼泥陶粒吸附剂,应用于高浊度废水的处理,以浊度的去除率为指标,通过对pH值、流速、填料高度、锯末量、粒径、处理时间等因素的考察,确定合适的工艺条件。结果表明：对于浊度为795～820 NTU的废水,在pH为12、流速在1 200 s.L-1、填料高度50 cm、粒径4 mm、锯末量为40 g、处理时间60 min,废水的除浊率达到94%。实现了对硼泥的资源化利用,为制备吸附剂的来源及吸附剂处理废水的应用开辟了新途径。     

Synergistic suppression effects of flame retardant,porous minerals and nitrogen on premixed methane/air explosion

A novel composite inhibitor based on porous mineral materials and conventional flame retardant of ammonium polyphosphate (APP) is prepared to suppress the premixed methane/air explosion. Taking advantages of gas and powder inhibitor, N₂ and the prepared composite inhibitor are combined to use. The suppression performance of N₂-composite inhibitor on methane explosion is investigated on a 20-L spherical experimental explosion apparatus and the characteristic pressure data are obtained. The combined inhibition effects of N₂ and the prepared composite inhibitor are greater than either acting alone. Thermal decomposition behavior and gaseous products of composite inhibitor are analyzed with thermogravimetric analysis and thermogravimetric-mass spectrometry, respectively. Based on physical and chemical actions, the inhibition mechanisms of N₂-composite inhibitor system are proposed. This work provides a reference to prepare high-performance gas explosion inhibitor based on the synergism of binary or multiple components.