Iron-doped Mn-Ce/TiO2 catalyst for low temperature selective catalytic reduction of NO with NH3

The catalysts of iron-doped Mn-Ce/TiO 2(Fe-Mn-Ce/TiO 2) prepared by sol-gel method were investigated for low temperature selective catalytic reduction(SCR) of NO with NH 3.It was found that the NO conversion over Fe-Mn-Ce/TiO 2 was obviously improved after iron doping compared with that over Mn-Ce/TiO 2.Fe-Mn-Ce/TiO 2 with the molar ratio of Fe/Ti = 0.1 exhibited the highest activity.The results showed that 96.8% NO conversion was obtained over Fe(0.1)-Mn-Ce/TiO 2 at 180°C at a space velocity of 50,000 hr 1.Fe-Mn-Ce/TiO 2 exhibited much higher resistance to H 2 O and SO 2 than that of Mn-Ce/TiO 2.The properties of the catalysts were characterized using X-ray diffraction(XRD),N 2 adsorption,temperature programmed desorption(NH 3-TPD and NOx-TPD),and Xray photoelectron spectroscopy(XPS) techniques.BET,NH3-TPD and NOx-TPD results showed that the specific surface area and NH3 and NOx adsorption capacity of the catalysts increased with iron doping.It was known from XPS analysis that iron valence state on the surface of the catalysts were in Fe3+ state.The doping of iron enhanced the dispersion and oxidation state of Mn and Ce on the surface of the catalysts.The oxygen concentrations on the surface of the catalysts were found to increase after iron doping.Fe-Mn-Ce/TiO2 represented a promising catalyst for low temperature SCR of NO with NH3 in the presence of H2 O and SO2.     

浸渍液pH值对V-Mo/Ti脱硝催化剂性能的影响研究

为提升V-Mo/Ti催化剂的脱硝性能,在催化剂制备过程中调节浸渍工艺参数,制备了一系列不同浸渍液pH值的催化剂,采用XRD、N2-吸附脱附、拉曼光谱、UV-Vis、H2-TPR、NH3-TPD等手段对催化剂进行表征,考察了pH值的变化对催化剂物理化学性能的影响,采用固定床微型反应器对催化剂的脱硝性能进行评价。结果表明,降低浸渍液pH值,可以抑制催化剂上VOx物种的聚合,提升催化剂的还原性能,有利于提升催化剂的脱硝效率,降低脱硝反应过程中N2O生成量。同时,浸渍液pH值的变化,也会影响催化剂的酸性性能。当浸渍液pH值低于3.64时,催化剂酸性性能显著降低,造成催化剂脱硝性能降低;当浸渍液pH值控制在3.64时,催化剂的还原性能和酸性性能匹配较好,从而显示了较高的脱硝性能。     

耦合式SCR还原剂供给调节装置及控制技术的研究与应用

阐述了SCR喷氨调节控制常用的方法及存在的问题,提出了一种新型耦合式SCR还原剂供给调节装置及控制技术,并通过电厂实际案例对该调节装置与控制技术进行了说明。研究结果表明:该调节装置及控制技术可使脱硝效率相对稳定、出口NO_x的浓度不超标、喷氨不过量。     

Bi/Fe_3O_4催化NaBH_4还原水中对硝基苯酚

以磁性Fe_3O_4为载体负载Bi(NO_3)_3,再用NaBH_4还原Bi~(3+)制备了Bi/Fe_3O_4催化剂。采用XRD和紫外-可见光谱对催化剂进行表征。考察了Bi负载量、NaBH_4加入量和Bi/Fe_3O_4加入量对Bi/Fe_3O_4催化NaBH_4还原对硝基苯酚(4-NP)效果的影响。表征结果显示:当催化剂中Bi含量较少时,Bi分散良好;当Bi含量较多时,会形成纳米颗粒。实验结果表明:当反应温度为25℃,初始4-NP浓度为4.0 mmol/L时,在Bi负载量为5%(w)、Bi/Fe_3O_4催化剂加入量为500 mg/L,NaBH_4加入量为6.0 g/L的条件下,反应速率常数为0.581 min~(-1),4-NP的去除率为99.7%;Bi/Fe_3O_4催化剂稳定性好,重复使用15次后,活性基本不变。     

SO2和H2O对Mn-Ce/TiO2催化剂低温SCR活性的影响

采用溶胶凝胶法制备Mn-Ce/TiO_2低温SCR催化剂并考察其活性,研究了SO_2和H_2O对Mn-Ce/TiO_2低温脱硝催化剂的影响,并运用XRD、BET、SEM和FT-IR对中毒前后的催化剂进行表征。结果表明,催化剂在无SO_2和H_2O条件下具有良好的脱硝性能,在140℃时NO_x去除率达到84%。但若向模拟烟气中加入SO_2和H_2O,则随其体积分数增大对催化剂活性产生明显抑制作用。当H_2O的体积分数为5%、SO_2为700×10-6时,反应4 h后,NO_x去除率降为53%。H_2O对催化剂的抑制作用随H_2O的除去而消除,H_2O主要通过与NO_x的竞争吸附来抑制催化剂的活性。低浓度的SO_2对催化剂活性影响较小,SO_2体积分数为100×10~(-6)时,稳定后NO_x去除率仍能维持在80%以上,但较高体积分数的SO_2引起的催化剂失活不可自行恢复。SO_2毒化作用主要是引起了硫酸铵盐覆盖催化剂的表面活性位,以及造成活性组分MnO_x的晶化,并破坏了MnO_x与TiO_2间的强相互作用。H_2O和SO_2共同存在时,H_2O可以弱化SO_2对催化剂的毒化作用,主要因为H_2O与SO_2的竞争吸附作用而使SO_2对催化剂活性的影响减弱。     

Two-step fast microwave-assisted pyrolysis of biomass for bio-oil production using microwave absorbent and HZSM-5 catalyst

A novel technology of two-step fast microwave-assisted pyrolysis(f MAP) of corn stover for bio-oil production was investigated in the presence of microwave absorbent(Si C) and HZSM-5catalyst. Effects of f MAP temperature and catalyst-to-biomass ratio on bio-oil yield and chemical components were examined. The results showed that this technology, employing microwave, microwave absorbent and HZSM-5 catalyst, was effective and promising for biomass fast pyrolysis. The f MAP temperature of 500°C was considered the optimum condition for maximum yield and best quality of bio-oil. Besides, the bio-oil yield decreased linearly and the chemical components in bio-oil were improved sequentially with the increase of catalyst-to-biomass ratio from 1:100 to 1:20. The elemental compositions of bio-char were also determined. Additionally, compared to one-step f MAP process, two-step f MAP could promote the bio-oil quality with a smaller catalyst-to-biomass ratio.     

Bi2O3-TiO2复合光催化剂协同处理铬-邻苯二甲酸酯复合污染

以硝酸铋和钛酸丁酯为前驱体,采用水热法制备了Bi_2O_3-TiO_2复合半导体材料,并利用X射线衍射(XRD)、紫外-可见吸收光谱(UVVis)、能谱分析(EDS)、X射线光电子能谱(XPS)等手段对复合材料的结构进行了表征.同时,考察了Bi_2O_3-TiO_2复合材料对重金属Cr(Ⅵ)和难降解邻苯二甲酸二丁酯(DBP)复合污染的处理性能,并探讨了复合催化剂协同处理复合污染的作用机制.结果表明:该复合催化剂在可见光下能同时降低重金属Cr(Ⅵ)和有机物DBP的浓度,抑制电子和空穴复合,表现出比对单一Cr(Ⅵ)及DBP污染物更高的处理效率.当Bi_2O_3含量为4%时,复合催化剂表现出最佳的光催化活性.     

Regeneration of commercial selective catalyst reduction catalysts deactivated by Pb and other inorganic elements

The regeneration of commercial SCR(Selective Catalyst Reduction) catalysts deactivated by Pb and other elements was studied.The deactivated catalyst samples were prepared by chemical impregnation with mixed solution containing K_2SO_4,Na_2SO_4,CaSO_4,Pb(NO_3)_2and NH_4H_2PO_4.A novel method combining Ethylenediaminetetraacetic acid disodium salt(EDTA-2Na) and H_2SO_4solution(viz.catalysts treated by dilute EDTA-2Na and H_2SO_4 solution in sequence) was used to recover the activity of deactivated samples,and the effect was compared with single H_2SO_4,oxalic acid,acetic acid,EDTA or HNO_3 solutions.The surface structure,acidity and reducibility of samples were characterized by N_2adsorption–desorption,inductively coupled plasma optical emission spectrometer(ICP-OES),scanning electron microscopy(SEM),X-ray diffraction(XRD),X-ray fluorescence(XRF),H-2-temperature programmed section(H_2-TPR),NH3-temperature programmed desorption(NH3-TPD) and in situ DRIFTS.Impurities caused a decrease of specific surface area and surface reducibility,as well as Br?nsted acid sites,and therefore led to severe deactivation of the SCR catalyst.The use of an acid solution alone possibly eliminated the impurities on the deactivated catalyst to some extent,and also increased the specific surface area and Br?nsted acid sites and promoted the surface reducibility,thus recovered the activity partially.The combination of EDTA-2Na and H_2SO_4 could remove most of the impurities and improve the activity significantly.The removal of Pb should be an important factor for regeneration.Due to a high removal rate for Pb and other impurities,the combination of EDTA-2Na and H_2SO_4 solutions provided the best efficiency.     

废弃SCR脱硝催化剂无害化处理的研究进展

鉴于废弃SCR脱硝催化剂中含有多种痕量重金属以及可回收利用物质,从处理工艺包括重金属的去除、有价金属的回收等方面综述了废弃SCR脱硝催化剂无害化处理的现状,总结了现阶段的研究重点以及工业化应用的瓶颈。目前主要关注废弃SCR脱硝催化剂中钒、钨、钛的回收工艺,但工业化成本昂贵,难以实现效益均衡化。根据现行废弃SCR脱硝催化剂的处置规范,烟气飞灰中重金属的存在是废催化剂处置工艺复杂化的关键。研究重金属的去除以及有价金属的回收,方能最终实现针对废弃SCR脱硝催化剂无害化处理工艺的综合研发。     

改性Y沸石催化降解聚苯乙烯的研究

用热重分析方法研究了HY沸石与改性Y沸石(UHY)作为催化降解聚苯乙烯的催化剂对聚苯乙烯催化降解的作用及影响,对聚苯乙烯的催化降解与热降解反应产物进行了比较。结果表明,催化剂的存在能显著地降低聚苯乙烯的降解温度,催化剂的酸量和孔结构对聚苯乙烯的降解温度、活化能、积炭的生成量及裂解产物有很大的影响。