硅胶表面TEOS疏水化改性及吸附VOCs特性

以正硅酸乙酯（TEOS）为疏水改性剂,通过硅胶表面的羟基接枝反应,得到具备一定疏水性的改性硅胶;利用BET、FT-IR、XRD和TG-DTG等手段对改性硅胶的结构及稳定性进行了表征;在此基础上考察了改性硅胶对各类有机废气的吸附性能.结果表明,TEOS成功接枝在了硅胶表面,改性硅胶不仅具备一定的疏水性,而且机械强度增加到原来的66.85%,稳定性也都得到了提高; 550℃空气下焙烧后的改性硅胶仍具有疏水性且吸附容量是焙烧之前的2倍;在高湿度高浓度的废气治理中,TEOS改性硅胶表现出更高的吸附能力和优良的热再生性能.高浓度下改性硅胶的吸附容量是低浓度下的10倍且不受水汽的影响;改性硅胶循环10次的吸附/脱附几乎不变,且在一定条件下,15~30min就达到90%的脱附率.     

几种氨氮吸附剂的对比实验研究

为给人工快速渗滤系统提供可行的填料,研究了煅烧贝壳、沸石、麦饭石、蛭石、中砂和细砂对氨氮的吸附效果。实验采用100 mg／L的氯化铵溶液作为初始溶液,结果表明,6种填料均具有快速吸附,缓慢平衡的吸附特点。经过11 h的吸附,煅烧后的贝壳对于氨氮的吸附量为0．993 mg／g。各个氨氮初始浓度梯次下,沸石的最大吸附量均超过其它5种填料,具有明显的氨氮吸附效果。     

改性活性炭纤维吸附炸药废水中TNT实验研究

本文研究了改性活性炭纤维对炸药废水中TNT的吸附行为。研究表明:1 mol/L HNO3改性的活性炭纤维吸附效果最好,其对炸药废水中TNT的最佳吸附条件为:吸附剂用量为0.6 g/25 m L,吸附平衡时间为60 min,升温有利于吸附进行。Langmuir和Freundlich吸附等温线均能较好地描述活性炭纤维对TNT的吸附,吸附动力学分析表明,吸附过程遵循准二级动力学规律。     

碳氮结构空心管材料及其对钍离子的吸附性能研究

目的合成碳氮结构空心管材料,用于稀土矿山开采中放射性钍离子的吸附去除,方法通过三聚氰胺和三聚氰酸超分子自组装,经水热碳化及高温热解,制备碳氮结构空心管材料.采用SEM、XRD等对材料进行表征.在不同热解温度和pH值下进行钍离子吸附实验,比较不同钍离子的初始浓度和吸附时间下吸附容量的差异.结果600℃时,材料形貌为均匀的中空管状结构;pH=3.5,热解温度为800℃时,材料最大吸附容量达到133.87 mg/g,吸附过程符合Langmuir等温吸附模型且遵从准二级动力学规律.结论碳氮结构空心管材料对钍离子具有良好的吸附效果,有望用于稀土开采过程中产生的放射性废钍离子的去除.     

黑碳吸附/解吸对微生物降解苯酚的影响

本文以黑碳为吸附介质,苯酚为吸附质,研究了黑碳上吸附的苯酚以及液相中的苯酚对微生物降解的影响。苯酚降解微生物选择假单胞菌,它能够以苯酚为唯一碳源和能源。通过实验得出,Freundlich吸附模型能够较好地描述苯酚在黑碳上的吸附;在实验浓度和时间条件下,假单胞杆菌降解苯酚呈现零级反应,在有黑碳的体系中,苯酚降解速度为5.77 mg.L-1.h-1,在无黑碳的体系中,苯酚降解速度为2.67 mg.L-1.h-1,黑碳促进了细菌降解苯酚,加大苯酚的降解速度。实验在有黑碳的体系中可以得出黑碳上苯酚的脱附速率跟不上细菌的降解速率,当液相中的苯酚降解完成后,黑碳的苯酚脱附是细菌降解苯酚的限制条件。     

火焰原子吸收分光光度法测定水中锶

研究了用空气/乙炔火焰原子吸收分光光度法测定水中锶时酸的影响,以及铝和钙的干扰及消除,线性范围0.05～5.00mg/l,最低检测浓度为0.04mg/l,回收率为98.2％～101.4％。     

Adsorption characteristic of bensulfuron-methyl at variable added Pb^2＋ concentrations on paddy soils

The combined pollution of heavy metal Pb²⁺ and bensulfuron-methyl (BSM), originating from chemical herbicides, in agroecological environments has become commonplace in southern China. The adsorption of BSM on three paddy soils in the presence of Pb²⁺ was examined using high-performance liquid chromatograph (HPLC). Results indicated that adsorption of BSM could accurately be described by a Freundlich isotherm equation with correlation constant (R) > 0.98, irrespective of the presence of spiked Pb²⁺. Of the various factors influencing BSM sorption, soil pH appeared to be the most influential. The constant K_f of Freundlich isotherm equation tended to increase with increasing Pb²⁺ concentration in soil which indicated that the spiked of Pb²⁺ in paddy soils would promote the sorption of BSM. ΔG^θ of BSM in three paddy soils was less than 40 kJ/mol in all treatments, indicating the adsorption of BSM is mainly physical in nature. The elution of soil dissolved organic matter (DOM) enhanced the adsorption of BSM in paddy soils. The mechanisms involved in the promotion effects of the spiked Pb²⁺ on BSM adsorption might be the modified surface characteristics of paddy soil solids due to the soil acidification and the increase of soil organic matter concentration because of DOM binding.     

IN SITU MEASUREMENT OF ADSORPTION AND BIOTRANSFORMATION AT A HAZARDOUS WASTE SITE1

ABSTRACT: A three well injection-production test was performed at the United Creosoting Company (UCC) site in Conroe, Texas, to estimate the effective in situ retardation factors for adsorption and to evaluate the significance of biotransformation in limiting the transport of polycydic aromatics present in the shallow aquifer. The field test was also used as a model to determine if this type of testing would be feasible at other hazardous waste sites. During the test, chloride, a non-reactive tracer and two organic compounds, naphthalene and paradichlorobenzene (pDCB), were injected into a center well for 24 hours followed by clean ground water for six days. Ground water was continuously produced from two adjoining wells and monitored to observe the breakthrough of these compounds. Data from the test were analyzed by comparing the statistical moments of the chloride and organics distributions. Retardation factors for naphthalene and pDCB were estimated to be 1.03 and 0.97 by comparison of the statistical moments. A significant loss of naphthalene and pDCB was also observed during the three well test, apparently due to biotransformation. These results suggest that biotransformation is the major process limiting the transport of naphthalene and similar compounds at the UCC site.     

改性多壁碳纳米管对水中Cd~（2＋）的去除

为了增加多壁碳纳米管（multiwall carbon nanotubers,MWNTs）对水中Cd2＋的吸附量,使用混酸对多壁碳纳米管进行氧化处理,采用红外光谱进行结果表征,并探讨了吸附时间、pH值和MWNTs的使用量、Cd2＋的浓度及干扰离子对镉离子吸附的影响。结果表明,吸附时间为1.5 h、pH为5.3、吸附效果最佳,随MWNTs量的增加Cd2＋去除量增加,共存的阳离子会降低对Cd2＋的吸附效果,对Cd2＋的吸附符合Longmuir吸附定律。研究同时表明,pH小于2时Cd2＋能容易从碳纳米管上解吸。初步探讨了Cd2＋吸附机制。     

天然沸石铵吸附容量研究

以浙江缙云的天然斜发沸石为实验对象,测试其化学组成与物理形态特征,并通过静态实验研究其对铵离子的吸附特性,再根据数学分析,确定该沸石的铵吸附容量.