Adsorptive removal of basic dyes from aqueous solutions by surfactant modified bentonite clay (organoclay): Kinetic and competitive adsorption isotherm

Cationic surfactant (Hexadecyltrimenthylammonium chloride) modified bentonite clay was prepared and systematically studied for its adsorption behavior as an efficient adsorbent for the removal of basic dyes such as methylene blue (MB), crystal violet (CV) and Rhodamine B (RB) from aqueous phase. Organo modified clay shows better capacity for the removal of three dyes. The adsorption process was found to be dependent on pH and initial dye concentration. The maximum dye sorption was found to be at a pH of 9.0 (99.99% for MB, 95.0% for CV and 83.0% for RB). The adsorption capacity for the dyes was found to be 399.74, 365.11 and 324.36 μmol/g for MB, CV and RB, respectively at 30 °C. The equilibrium uptake was attained within 240 min. The kinetic studies were revealed that sorption follows a pseudo-second-order kinetic model which indicates chemisorption between adsorbent and adsorbate molecules. Adsorption isotherm indicates non-energetically adsorption sites which fit with Freundlich isotherm model. The fitness of kinetics and isotherm models was evaluated by using HYBRID error analysis function. Competitive adsorptions of dyes were studied by using binary component systems.     

利用Cu-Fe复合金属氧化物净化水中的磷

研究了利用Cu-Fe复合金属氧化物净化水中磷的过程。实验结果表明,在吸附剂的制备过程中,加入Cu可以显著提高吸附剂对水中磷的净化效率,Cu的适宜加入量为Cu/Fe摩尔比1∶2。在磷净化过程中,p H值对Cu-Fe复合金属氧化物的净化效率有显著影响,较低的p H值有利于磷的净化;水中磷的净化率随吸附剂用量的增加而增加,适宜的投加量为0.2 g/100 m L;吸附剂对水中磷的净化速度较快,磷的吸附率在5 min内达到87.08%,吸附2 h达到平衡,磷的净化率为98.85%;Cu-Fe复合金属氧化物净化水中磷的吸附等温线符合Langmuir方程,磷的最大吸附量为11.36 mg/g。     

常见离子对蛋壳粉吸附溶液中磷的影响

研究了水体中常见离子对蛋壳粉吸附溶液中磷的影响.实验结果表明,SO2-4、Cl-和NO-3的存在,对天然蛋壳粉吸附磷过程产生协同作用,但协同作用不明显;HCO-3表现出吸附抑制作用;Ca2+和Mg2+表现出较为显著的吸附协同作用,其中Ca2+最为显著;NH+4离子存在时,几乎不产生影响.富集系数和吸附平衡下降率均可有效表述常见离子对蛋壳粉吸附磷过程的影响程度.     

Mesoporous carbon adsorbents from melamine–formaldehyde resin using nanocasting technique for CO2 adsorption

Mesoporous carbon adsorbents, having high nitrogen content, were synthesized via nanocasting technique with melamine–formaldehyde resin as precursor and mesoporous silica as template. A series of adsorbents were prepared by varying the carbonization temperature from 400 to 700°C. Adsorbents were characterized thoroughly by nitrogen sorption, X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), thermogravimetric analysis (TGA), elemental (CHN) analysis, Fourier transform infrared (FTIR) spectroscopy and Boehm titration. Carbonization temperature controlled the properties of the synthesized adsorbents ranging from surface area to their nitrogen content, which play major role in their application as adsorbents for CO₂ capture. The nanostructure of these materials was confirmed by XRD and TEM. Their nitrogen content decreased with an increase in carbonization temperature while other properties like surface area, pore volume, thermal stability and surface basicity increased with the carbonization temperature. These materials were evaluated for CO₂ adsorption by fixed-bed column adsorption experiments. Adsorbent synthesized at 700°C was found to have the highest surface area and surface basicity along with maximum CO₂ adsorption capacity among the synthesized adsorbents. Breakthrough time and CO₂ equilibrium adsorption capacity were investigated from the breakthrough curves and were found to decrease with increase in adsorption temperature. Adsorption process for carbon adsorbent–CO₂ system was found to be reversible with stable adsorption capacity over four consecutive adsorption–desorption cycles. From three isotherm models used to analyze the equilibrium data, Temkin isotherm model presented a nearly perfect fit implying the heterogeneous adsorbent surface.     

生物活性炭吸附石化废水有机污染物实验研究

生物活性炭吸附石化二级废水有机污染物实验主要包括生物活性炭挂膜实验和生物活性碳影响因素实验。在实验中考察了水力负荷和活性炭滤层厚度两因素对有机污染物吸附作用。结果表明:在45 d左右挂膜基本成功,最佳水力负荷为0.25~0.75m3/(m2·h),活性炭滤层最佳厚度为90cm。     

改性小麦秸秆吸附Cu2+的动力学和热力学研究

本研究采用ZnCl2作为活化剂,用640W功率的微波照射5min的方法制备改性小麦秸秆。研究了改性小麦秸秆投加量、吸附时间、温度、pH对改性小麦秸秆吸附水溶液中Cu2+的影响,以及对其等温吸附特征、动力学和热力学进行了研究。试验结果表明:投加量为0.1g,pH为6,改性小麦秸秆对Cu2+有较好的吸附效果,吸附在10h后达到平衡。改性小麦秸秆对Cu2+吸附较好地符合Langmuir、Freundlich温吸附模型和准二级动力学方程,吸附过程中△G0,说明属于自发反应。     

洱海弥苴河河口沉积物磷吸附特性研究

以洱海主要入湖河流弥苴河的河口表层沉积物为实验对象,研究其磷吸附特性。研究结果表明,Elovich方程对沉积物吸磷动力学拟合较好,考虑沉积物原有吸附态磷的修正Langmuir方程能较好描述弥苴河河口表层沉积物等温吸附特性。弥苴河河口沉积物存在释磷风险,沉积物间隙水正磷浓度远高于临界磷平衡浓度。     

粉煤灰对阴离子水溶性混合染料的吸附动力学

以燃煤废弃物粉煤灰作为吸附剂,对活性红23与活性蓝4、活性黄4、酸性黑1、酸性蓝193的混合染料溶液进行吸附性能研究.结果表明,在不同的混合体系中,活性红23的脱色率基本保持在60%~70%;体系中酸性染料的脱色率均超过90%;活性蓝4的脱色率高达85%;活性黄4的脱色率仅为50%.准二级吸附动力学能够更好地描述粉煤灰对水溶性混合染料的吸附过程.染料在溶液中的外扩散系数均为10-4cm·s-1数量级,染料在粉煤灰颗粒的内扩散系数为10-8cm2·s-1数量级.根据BN数,水溶性染料在粉煤灰上的竞争吸附是外扩散控制的吸附过程.     

铁镧复合氧化物纳米吸附剂的制备、表征及As（Ⅲ）吸附性能研究

本研究采用共沉淀法制备了一种新型铁镧复合氧化物吸附剂(Fe-La),并对其表面特性及As(Ⅲ)吸附行为进行了系统研究.扫描电镜(SEM)和透射电镜(TEM)结果表明,铁镧复合氧化物具有纳米结构,初级粒子粒径范围为20~200 nm.X-射线衍射仪(XRD)表征结果表明,铁镧复合氧化物具有类似氢氧化镧的晶型结构.N2吸附BET法结果表明,铁镧复合氧化物的比表面积为99.3 m2·g-1.盐加入法测得吸附剂的等电点为7.8.As(Ⅲ)吸附实验结果分析表明,铁镧复合氧化物对As(Ⅲ)具有良好的吸附效果,最大吸附量(pH 7.0)为58.2 mg·g-1,Langmuir吸附等温线可较好地拟合铁镧复合氧化物对溶液中As(Ⅲ)的吸附(R2=0.95);吸附速率较快,240 min内可完成吸附容量的80%,Elovich模型能较好地描述吸附过程(R2=0.97);溶液pH对铁镧复合氧化物吸附As(Ⅲ)的影响较为明显;共存阴离子对吸附影响的大小顺序为SO2-4相似文献