选用活性白土对餐饮业废油脂进行脱色研究,对脱色率的影响因素进行了讨论。摸索出活性白土的最佳脱色条件：活性白土用量5％;初始脱色温度60C;终止脱色温度120C;脱色时间25min。     

利用硫酸渣生产铁精粉的新工艺研究

实验了一种新的工艺来处理硫酸渣,该方法能很好地脱除烧渣中的硫并富集其中的铁,解决了硫酸渣脱硫难的问题。经过处理后可以将其开发为有用的铁精粉作为炼铁原料或者是生产其他铁系产品,实现了废物的资源综合利用。     

不同配比安全点火药B/KNO_3的研究

为研究可靠点燃主装药,性能稳定的B/KNO3点火药,对不同配比的B/KNO3进行配制并对其性能进行测试。不同配比B/KNO3在火焰感度、静电火花感度、撞击感度、摩擦感度4项外界刺激中,除了对撞击非常钝感之外,对其他3项外界刺激敏感。在不同比例的药中,以B/KNO3比例为50:50,粘结剂为X的药火焰感度最高,稳定性好;静电火花感度随B/KNO3中B比例提高而降低,摩擦感度随B/KNO3中B比例提高而提高,但当中B比例从40%提高到50%时,这两感度改变不多。分析得出B/KNO3比例为50:50,粘结剂为X的药满足对主装药点火可靠,稳定性好。     

用废镍铝合金粉制备镍催化剂

研究了以废镍铝合金粉（废镍渣）为原料、H2SO4为浸出剂、尿素为沉淀剂制备镍催化剂的方法;考察了Ni浸出条件对其浸出率的影响,并通过催化加氢实验对镍催化剂的活性进行了评价。Ni的浸出条件：w（H2SO4）25％、酸浸时间3h、n（废镍渣）：n（H2SO4）=1．0：1．4。在该条件下,Ni的浸出率为92．85％。Ni的回收率在90％以上。催化加氢实验结果表明,在温度120～125℃、压力大于或等于1．2MPa、催化剂用量1％（质量分数）的条件下,可将异丙叉丙酮经一步液相催化加氢反应制备成甲基异丁基甲醇（MBC）,异丙叉丙酮转化率为100％,MIBC的收率达99．3％。     

膜电解法从模拟酸性蚀刻废液中回收铜粉

酸性蚀刻废液是一种印制电路板制作过程中产生的强酸、高铜的工业废水,对其回收利用具有较高的经济价值。采用膜电解法处理模拟酸性蚀刻废液,在阴极区回收铜粉。研究了铜粉的形成条件,考察了阴极液铜浓度、温度和电流密度对阴极电流效率的影响。结果表明,阴极液的铜浓度在20~25 g/L,温度为45~50℃,电流密度在11~12 A/dm2,阴极的电流效率最高。随着阴极液酸度的增加,铜粉的纯度提高,但阴极电效会降低。为保证较高的铜粉纯度及阴极电效,阴极液的酸度在0.32~0.36 mol/L为宜。     

许昌市发制品行业的清洁生产调查

发制品行业是以人发、人造纤维等为原材料进行假发加工的行业。许昌市发制品的生产过程大致可分为两个阶段:漂染和前后处理。漂染过程用水量大,产生的废水难以处理。其中过酸、氧化、染色配置的溶液使用一次后直接排放,不符合清洁生产要求,且所排放的溶液可考虑中和多次利用。漂染过程水资源消耗量大,废水产生量大,没有考虑废水综合利用。按清洁生产的要求在以上环节可通过技术革新和设备改造得以改进。     

LDO处理垃圾渗滤液中氮的实验研究

研究了复合金属氧化物（LDO）用于处理垃圾渗滤液中氮的可行性,并与传统吸附剂粉末活性炭（PAC）进行了比较,考察了投加量、振荡速度、吸附时间、吸附温度、pH等因素对处理效果的影响。结果表明,当垃圾渗滤液中总氮浓度为561mg/L、LDO投加量为6g/L、振荡速度为170r/min、吸附时间为60min、温度为25℃、pH值为11时,LDO对总氮的吸附量最高,达到41mg/g。在相同条件下,LDO对总氮的吸附量是PAC的2.5—3.5倍。     

Black Disease (Terpios hoshinota): A Probable Cause for the Rapid Coral Mortality at the Northern Reef of Yongxing Island in the South China Sea

The northern reef of Yongxing Island, the largest reef island of the Xisha Islands in the South China Sea, was in good condition with significant cover of scleractinian corals until 2002. Surveys in 2008 and 2010, however, found that coral coverage had declined rapidly and severely, implying that catastrophic coral mortality occurred during the past 8 years. A blackish mat was observed covering live and dead corals in both 2008 and 2010 that was identified as an encrusting sponge, Terpios hoshinota, by special surface morphology and spicule structure. In addition, spicule residues were found on the surface of long-dead corals, indicating a previous invasion of T. hosinota. T. hoshinota is referred to as the "black disease" because it rapidly overgrows and kills corals. Our evidence indicates that outbreaks of black disease are at least partially responsible for the massive coral mortality at the northern reef of Yongxing Island over the past 8 years, although human activities and heat-related coral bleaching cannot be discounted as minor causes for this coral decline.     

沸石粉在污泥生态床中的应用研究

研究了不同沸石粉投加比例对污泥脱水、沉降、干化时间、污泥生态床中植物根部干重的影响,最终选定沸石粉投加比例为6%。在此投加比例下,对污泥生态床中的氮磷含量进行了测定,结果表明,黄花鸢尾床与芦苇床,总磷含量下降分别为13.2%和12.2%;总氮含量下降分别为48.3%和49.2%;硝氮含量下降分别为67.2%和70.2%。     

利用废CRT屏玻璃为原料制备泡沫玻璃

以废阴极射线管(CRT)屏玻璃为主要原料,碳黑为起泡剂,采用粉末烧结法制备了低密度保温泡沫玻璃。通过扫描电镜(SEM)、导热系数测定仪等分析手段,研究了起泡剂的用量、发泡温度和发泡时间对泡沫玻璃泡径、密度、热学性能以及机械力学性能的影响。结果表明,在相同烧制工艺条件下,随起泡剂掺加量增加,烧制所得的泡沫玻璃密度成"V"型变化;当其掺加量为0.20%时,泡沫玻璃在密度、孔径分布以及力学性能上均达到最佳。随着发泡温度的提高和发泡时间的延长,密度会逐渐减小,泡沫玻璃的气泡会逐渐增大,以致产生连通现象。当发泡温度为820℃、发泡时间为30min时烧制的泡沫玻璃密度为0.180 g/cm3,导热系数为0.0695 W/(m.K)。