钛基IrO2-RuO2阳极电解处理亚甲基蓝溶液

采用钛基IrO2-RuO2为阳极材料,不锈钢为阴极材料,NaCl质量浓度为10 g/L的溶液为电解液,对亚甲基蓝溶液进行电化学处理。实验结果表明:处理初始质量浓度为25 mg/L的亚甲基蓝溶液,电解电流0.050 A,电解20 min后亚甲基蓝去除率达95%;处理初始质量浓度为100 mg/L的亚甲基蓝溶液,电解电流0.100 A,电解30 min后亚甲基蓝去除率达98%。随着电解时间和电解电流的增加,亚甲基蓝去除率均增大。     

Effect of Pretreatment with UV Radiation on Physical and Mechanical Properties of Photocured Jute Yarn with 1,6-Hexanediol Diacrylate (HDDA)

Jute yarns were grafted with a single impregnating monomer 1,6-hexanediol diacrylate (HDDA) in order to improve the physicomechanical properties. Jute yarns soaked for different soaking times (3, 5, 10, and 30 minutes) in HDDA+MeOH solutions at different proportions (1–10% HDDA in MeOH [v/v] along with photoinitiator Darocur-1664 [3%]) were cured under UV lamp at different UV radiation intensities (two, four, six, and eight passes). Concentration of monomer, soaking time, and intensity of UV radiation were optimized with extent of mechanical properties such as tensile strength, elongation at break, and modulus. Enhanced tensile strength (67%), modulus (108%), and polymer loading (11%) were achieved with 5% HDDA concentration, 5-minute soaking time, fourth pass of UV radiation. To further improve the mechanical properties, the jute yarns were pretreated with UV radiation (5, 10, 15, 30, and 50 passes) and treated with optimized monomer concentration (5%). UV-pretreated samples showed the enhanced properties. The tensile strength and modulus increase up to 84% and 132%, respectively, than that of virgin jute yarn. An experiment involving water absorption capacity shows that water uptake by treated samples was much lower than that of the untreated samples. During the weathering test, treated yarns exhibited less loss of mechanical properties than untreated yarns.     

Thermal and Mechanical Properties of Plastics Molded from Sodium Dodecyl Sulfate-Modified Soy Protein Isolates

Soybean protein is a potential material for manufacturing of biodegradable plastics. The objective of this investigation was to characterize the thermal and mechanical properties of plastics made from sodium dodecyl sulfate (SDS)-modified soy proteins. Soy protein isolate (SPI) was prepared from defatted soy flour, modified with various concentrations of SDS, and then molded into plastics. The temperatures of denaturation of the modified soy protein increased at low SDS concentration and then decreased at high SDS concentration. At the same SDS concentration, the plastics molded from the modified soy proteins showed a similar temperature of denaturation, but a lower enthalpy of denaturation compared to the modified soy protein. Young's modulus of the plastics decreased as SDS concentration increased, and the tensile strength and strain at break of the plastics reached a maximum value at 1% SDS modification. Two glass transition temperatures were identified corresponding to the 7S and 11S globulins in SPI by dynamic mechanical analysis, and they decreased as SDS concentration increased. The SDS modification increased the water absorption of the plastics.     

用改性赤泥吸附废水中的六价铬

用国内烧结法产生的赤泥作主要原料,以氯化铁为改性剂制得改性赤泥,用其吸附含铬废水中的重铬酸根阴离子。当废水中六价铬的质量浓度为80mg／L时,在环境温度为30℃、改性赤泥投加量为10g／L、pH为2左右的酸性环境中,2h达到吸附平衡,去除率可达96．18％。并且利用Langmuir等温式和Freundlich等温式对其吸附机理进行了探讨,结果表明,氯化铁改性赤泥对重铬酸根阴离子的吸附是通过物理吸附和化学吸附的协同作用来进行的。     

螯合型表面活性剂对垃圾焚烧飞灰改性的研究

以垃圾焚烧飞灰的高附加值资源化和稳定化为目标,研究了螯合型表面活性剂对垃圾焚烧飞灰改性活化和对重金属的稳定螯合效果.通过活化指数和红外光谱分析,在改性剂用量7.0mL/100g飞灰、改性时间15min和改性温度75℃的条件下,ACS1改性飞灰的活化指数可达95%以上.美国环保局固体废弃物浸出毒性试验表明,螯合型表面活性剂对飞灰中重金属具有较强的束缚能力.     

石英砂负载氧化铁的表征及其除锑吸附性能研究

通过SEM/EDAX以及Nova-1000表面分析仪对石英砂负载的氧化铁颗粒进行了表征,发现负载氧化铁的粒径为200 nm左右,其表面孔径及孔隙率分别为2×10-9～9×10-9m及0.11%,负载氧化铁的石英砂的比表面积为原砂的5倍.考察了石英砂负载氧化铁(IOCS)在不同的实验条件下(吸附时间,pH值,温度等)对水溶液中锑的去除效果,在pH为3～9范围内,其去除率均超过了98%.吸附动力学及吸附等温线实验数据分别符合二级反应动力学模型及Langmuir等温吸附模型.热动力学实验结果进一步表明:IOCS吸附锑的过程是自发的、吸热的化学吸附反应.     

小叶榕落叶改性条件优化及其处理含Cu~(2+)废水动力学研究

以废弃的小叶榕落叶作为吸附剂,通过正交试验选择制备改性小叶榕落叶的最佳条件,结果表明:当硝酸浓度为10moL/L,干燥温度为120℃和氢氧化钠浓度为1moL/L时,改性后的小叶榕落叶的活性最强,对废水中Cu2+的吸附率最高。利用改性后的小叶榕落叶进行了吸附去除水中Cu2+的研究,得出当pH为5.7,铜的最大吸附容量Qmax=0.59mg(Cu)/g(改性落叶)。并通过非线性回归,构建了影响因素同吸附率之间的数学模型和落叶吸附的动力学模型。     

宝钢焦化废水处理脱氮研究与实践

针对上海提高新排放标准中总氮(TN)≤35 mg/L的要求,对焦化废水进行了脱氮研究。选取现场缺氧-好氧-好氧(A-O-O)工艺中前两段的A-O生化沉淀池1出水,在SBR内进行反硝化脱氮实验,考察葡萄糖、葡萄糖+乙酸钠、甲醇和甲醇+乙酸钠单一或复合碳源及投加反硝化菌种对脱氮的影响,确定最佳碳源为甲醇+乙酸钠,最佳反硝化水力停留时间为16 h。当反硝化菌液投加浓度为1 mg/L时,SBR出水TN满足达标排放要求。结合实验结果对宝钢焦化废水原有AO-O工艺改造升级为A-O-A-O二段脱氮工艺,并对生化出水实施进一步的物化混凝处理。改造后,工艺长期运行稳定,最终出水完全达到上海市污水综合排放标准(DB 31/199-2009)TN≤35 mg/L的要求,并满足氰化物、氟化物以及COD的排放要求。     

石英砂滤料表面润湿改性

采用硅烷偶联剂、钛酸酯偶联剂和铝酸酯偶联剂对石英砂进行表面改性,以制备亲油疏水性滤料。研究得出,钛酸酯偶联剂改性石英砂的最佳工艺条件为:偶联剂用量15%,反应温度90℃,搅拌时间15 min;硅烷偶联剂和铝酸酯偶联剂改性石英砂的最佳工艺条件均为:偶联剂用量15%,反应温度110℃,搅拌时间15 min。水对钛酸酯偶联剂改性石英砂滤料的润湿重量由改性前的1.5589 g降低到0.0282 g,水对硅烷偶联剂改性石英砂滤料的润湿重量降低到0.0607 g,水对铝酸酯改性石英砂滤料的润湿重量降低到0.2664 g。静态吸附实验表明,硅烷偶联剂、钛酸酯偶联剂和铝酸酯偶联剂改性石英砂滤料对油的吸附容量分别增加了33.67%、42.87%和22.30%。XPS和FT-IR分析表明,偶联剂均以化学键的方式包覆在石英砂滤料表面,结合稳定。     

改性建筑垃圾作为橡胶填料的可行性研究

将废旧混凝土和废粘土砖经湿式表面改性后作为橡胶填料,辅以配合剂与丁苯橡胶进行混炼、硫化制得橡胶组合物,并将其与以等量轻质碳酸钙作为填料,按相同配比混炼、硫化制得的橡胶组合物的性能进行比较.结果表明,将加工成微米级别(0.5～12.0 μm)的建筑垃圾(废旧混凝土或废粘土砖)经水解双(三乙氧基硅基丙基)四硫化物(KH-8...