Atrazine, a widely used herbicide, is increasing the agricultural production effectively, while also causing great environmental concern. Efficient atrazine-degrading bacterium is necessary to removal atrazine rapidly to keep a safe environment. In the present study, a new atrazine-degrading strain ZXY-1, identified as Pseudomonas, was isolated. This new isolated strain has a strong ability to biodegrade atrazine with a high efficiency of 9.09 mg/L/hr.Temperature, p H, inoculum size and initial atrazine concentration were examined to further optimize the degradation of atrazine, and the synthetic effect of these factors were investigated by the response surface methodology. With a high quadratic polynomial mathematical model(R~2= 0.9821) being obtained, the highest biodegradation efficiency of 19.03 mg/L/hr was reached compared to previous reports under the optimal conditions(30.71°C, pH 7.14, 4.23%(V/V) inoculum size and 157.1 mg/L initial atrazine concentration).Overall, this study provided an efficient bacterium and approach that could be potentially useful for the bioremediation of wastewater containing atrazine.     

一种多介质层波形潜流人工湿地处理重污染河水试验

我国河流污染严重,城市黑臭水体的比率日益增加。人工湿地作为一种高效低耗能的绿色处理技术,已被广泛应用于污染河水的治理。通过对比分析分层装填复合填料的多介质层波形潜流人工湿地和单一砾石填料的普通人工湿地处理重污染河水的效果,研究了特种基质填料强化脱氮除磷作用以及不同水力负荷条件的影响。试验结果表明:在水力负荷为0.2 m~3/(m~2·d)时,普通湿地对COD、NH3-N、TN和TP的去除率分别达到55.95%、77.85%、39.80%和54.94%;多介质层湿地对COD、NH3-N、TN和TP的去除率分别达到58.52%、75.99%、67.08%和57.31%。在水力负荷为0.5 m~3/(m~2·d)时,普通湿地对COD、NH3-N、TN和TP的去除率分别达到68.46%、90.73%、42.13%和53.70%;多介质层湿地对COD、NH3-N、TN和TP的去除率分别达到69.61%、89.94%、77.58%和68.63%,其脱氮效果明显好于普通湿地。以复合填料包分层装填的波形潜流人工湿地系统具有良好的脱氮除磷效果,有很好的推广应用价值。     

多层阻尼复合板常温贮存5年性能研究

目的分析多层阻尼复合板常温贮存5年的性能变化。方法对多层阻尼复合板进行常温下贮存5年的减振性能研究,通过贮存前后的正弦扫描试验和随机振动试验,获得贮存前后多层阻尼复合板的减振性能和模态变化,进行对比分析。结果阻尼复合板常温贮存5年后,径向模态有较大的下降,法向模态变化较少,组件上的加速度响应基本无变化。结论该多层阻尼复合板常温贮存5年后仍然满足要求。     

Photocatalytic degradation of carbofuran in TiO2 aqueous solution：Kinetics using design of experiments and mechanism by HPLC/MS/MS

The photocatalytic degradation kinetics of carbofuran was optimized by central composite design based on response surface methodology for the first time. Three variables, TiO2 concentration, initial pH value and the concentration of carbofuran, were selected to determine the dependence of degradation efficiencies on independent variables. Response surface methodology modeling results indicated that the degradation efficiency of carbofuran was highly affected by the initial pH value and the concentration of carbofuran. Then nine degradation intermediates were detected by HPLC/MS/MS. The Frontier Electron Densities of carbofuran were calculated to predict the active sites on carbofuran attacked by hydroxyl radicals and photoholes. Point charges were used to elucidate the chemisorption pattern on TiO2 catalysts during the photocatalytic process. By combining the experimental results and calculation data, the photocatalytic degradation pathways of carbofuran were proposed, including the addition of hydroxyl radicals and the cleavage of the carbamate side chain.     

中心组合设计优化S-Cr-TiO2催化剂光降解工艺条件

在确定的温度和光照条件下,采用中心组合设计法研究了固相反应法合成的硫与铬共掺杂二氧化钛(S-Cr-TiO2)光催化剂与水溶苯胺蓝(ANB)可见光降解过程中的三个作用因子:催化剂的浓度、水溶苯胺蓝水溶液的pH值及其初始浓度之间的相互作用关系,得到了影响因子与降解速率之间的回归方程及因素之间相互作用的响应面图.结果表明,S...     

壳聚糖活性污泥复合吸附剂的制备研究

为了提高污泥细胞吸附重金属离子的应用能力,采用壳聚糖包埋固定活性污泥,制备了粒径2~3 mm的壳聚糖活性污泥复合吸附剂SCTS.以吸附溶液中CrO2-4的吸附率为指标,通过单因素实验对制备过程中采用的2种固化液及5种发泡剂进行比选,考察了固化液浓度、发泡剂量、交联剂量、活性污泥与壳聚糖用量比值及发泡温度对SCTS吸附能力的影响,由正交实验确定影响因素主次顺序及最优水平组合.结果发现,固化液浓度、发泡剂量、污泥与壳聚糖用量比值及发泡温度对SCTS吸附能力影响较强,影响次序为固化液浓度发泡剂量活性污泥与壳聚糖用量比值发泡温度.最优水平组合为4 g·L-1三聚磷酸钠(STPP)固化液、剂量为吸附剂质量10%的NH4HCO3发泡剂、活性污泥与壳聚糖用量比值0.5、发泡温度100℃,此时CrO2-4吸附率最高可达97.3%.该吸附剂的制备研究为污泥的资源化利用探索了新的途径.     

TiO2/膨润土复合材料对Hg2+的吸附性能研究

利用纳米TiO_2对膨润土进行复合改性,制备TiO_2/膨润土复合材料.采用电镜扫描、X-射线衍射表征改性前后膨润土的结构和形貌.通过室内模拟实验,以膨润土为对照,研究不同添加量、pH、吸附时间及初始Hg~(2+)浓度等条件下,TiO_2/膨润土复合材料对Hg~(2+)的吸附特性与性能,同时通过正交试验,探究TiO_2/膨润土复合材料吸附Hg~(2+)的最优条件.结果表明,改性后的膨润土颗粒明显变小,且颗粒疏松多空孔,层间距增大.相比于膨润土,TiO_2/膨润土复合材料吸附性能得到极大提高.TiO_2/膨润土复合材料对Hg~(2+)的吸附率均随着添加量、pH、吸附时间的增大而增大,添加量为1.5 g·L~(-1)、pH为7.0、吸附时间为120 min时,吸附率达98.0%以上.但TiO_2/膨润土复合材料对Hg~(2+)的吸附率随着初始Hg~(2+)浓度的增大而减小.通过4种动力学模型拟合发现,吸附过程符合假二级动力学方程,吸附以化学吸附为主.吸附等温线更符合Langmuir等温方程,属于典型的单分子层吸附,最大吸附量为20.66 mg·g-1.吸附Hg~(2+)的最优实验条件:添加量为2.0 g·L~(-1),pH为8.0,初始Hg~(2+)浓度为45 mg·L~(-1),吸附时间为16 h,此时吸附率99.9%,平衡浓度为0.034 mg·L~(-1).     

树脂基纳米钛锆氧化物复合吸附剂同步去除水中磷和氟

以大孔强碱性阴离子交换树脂D201为基体,负载纳米钛、锆氧化物,制备新型树脂基纳米钛锆氧化物复合吸附剂TiZr-D201.通过吸附等温线实验、pH影响实验、竞争吸附实验、动力学实验及柱吸附实验,并结合对吸附剂的表征,探讨了复合吸附剂对水中磷和氟的吸附性能和相应的吸附机制.结果表明,当pH值为5.8,温度为308K时,Ti-Zr-D201对磷和氟的Langmuir拟合最大吸附容量分别是34.9 mg·g~(-1)和35.1 mg·g~(-1),且吸附行为是自发进行的,温度越高,吸附效果越好;与磷相比,pH值对Ti-Zr-D201吸附氟的影响更为显著;选取SO_4~(2-)、NO_3~-和Cl~-作为竞争离子,Ti-Zr-D201较基体D201表现出很好的抗干扰能力;内扩散模型拟合结果表明Ti-Zr-D201在吸附平衡前存在两个不同的吸附阶段;柱吸附实验表明Ti-Zr-D201具有稳定的结构和良好的动态吸附性能,并且可再生循环使用,具备实际应用的潜力.     

磁性氮掺石墨烯活化过硫酸钾降解水中亚甲基蓝

活化过硫酸盐产生硫酸根自由基的高级氧化技术在水环境污染物治理中引起了广泛的关注和研究.本研究采用水热法制备磁性氮掺石墨烯(M-N-G)作为催化剂.利用SEM、BET、XRD和VSM等手段表征材料,系统研究了该材料活化过硫酸盐降解亚甲基蓝的效能.结果表明:M-N-G的比表面积为94.35 m2·g-1,磁性Fe3O4分布在材料表面,能有效的活化过硫酸钾降解亚甲基蓝.当催化剂的用量为200 mg·L~(-1),过硫酸钾浓度为0.4~0.5 mmol·L~(-1)时,在p H=3~6时对10 mg·L~(-1)亚甲基蓝的降解率达90%以上.体系温度在15~32℃时,降解速率常数在0.0227~0.0488 min-1,反应活化能为33.7 k J·mol-1.EPR分析及自由基漼灭实验证明了体系中有羟基自由基和硫酸根自由基产生.TOC分析结果表明:TOC去除率可达50%.M-N-G经过简单的稀硫酸和水洗后,可高效重复利用4次.该技术方法简单、高效、无二次污染,能为有机污染物废水处理提供一种新的方法选择.     

不同构造措施的钢管混凝土边框钢板剪力墙抗震性能试验研究

钢管混凝土边框钢板剪力墙是一种新型抗震剪力墙,为了比较不同构造措施对该新型剪力墙抗震性能的影响,进行了3个剪跨比为1.5的钢管混凝土边框钢板剪力墙低周反复荷载试验.其中,试验模型1为墙体钢板与边框柱钢管焊接,试验模型2为墙体钢板与边框柱钢管螺栓连接,试验模型3为墙体钢板开孔并与边框柱钢管焊接.通过试验研究,比较了各剪力...