Despite the widespread use of benzotriazoles as corrosion inhibitors in many household goods, studies on the occurrence of these compounds in indoor air are scarce. In this study, five benzotriazole derivatives were measured in 83 indoor air samples collected from various locations in Albany, New York, USA. Benzotriazoles were found in a majority of the indoor air samples, and the concentrations of their sum in bulk (vapor plus particulate phases) indoor air ranged from below the method limit of quantification to 492 ng·m^?3 (geometric mean: 5.8 ng·m^?3). The highest geometric mean concentration was found in air samples collected in parking garages (155 ng·m^?3), followed by barbershops (13.6), public places (11.5), auto repair shops (5.2), automobiles (4.5), homes (4.5), offices (3.7), and laboratories (2.8). Inhalation exposure to benzotriazoles was calculated on the basis of the measured geometric mean concentrations and air inhalation rate. The highest exposure dose was found for teenagers, with a geometric mean inhalation exposure dose of 79 ng·day^?1. The body-weight normalized exposure dose, however, was the highest for infants, at 3.2 ng·(kg bw)^?1·day^?1.     

重庆市大气污染对锌材料腐蚀的经济损失分析

简要介绍了材料大气腐蚀经济损失的估算方法,并以2002年为基准年,选择了重庆市主城中心的6个功能区作为代表性区域,运用腐蚀破坏剂量响应函数和使用寿命计算公式对锌材料的腐蚀经济损失进行了定量估算.结果表明,由大气污染腐蚀破坏锌材料造成的年直接经济损失约为4061.7万元,约为同期GDP的0.1%.其中,干沉降对经济损失总量的贡献率在71%～99%之间,均值为92%.     

2A12铝合金在模拟溶液中的周浸腐蚀行为

采用干湿周浸实验、失重法和电化学阻抗谱研究了2A12铝合金在0.6mol/L NaCl和0.6mol/L NaCl 0.02mol/L NaHSO3两种溶液中的腐蚀行为与规律, 利用扫描电镜(SEM)、能谱(EDX)和红外光谱(FTIR) 观察分析腐蚀产物表面形貌、结构和组成,测试了材料的力学性能.研究表明,随腐蚀时间的延长,腐蚀产物不断增多,失重增加,力学性能下降,阻抗模值逐渐减小;腐蚀产物形貌以团状和块状为主,在0.6mol/L NaCl溶液中腐蚀产物主要为铝的氯化物和氧化铝,在0.6mol/L NaCl 0.02mol/L NaHSO3溶液中腐蚀产物主要为氧化铝、铝的硫酸盐水合物和铝的氯化物;由于NaCl和NaHSO3共同作用,2A12合金在0.6mol/L NaCl 0.02mol/L NaHSO3溶液中腐蚀电流密度高,阻抗模值相对较小,腐蚀速率较高,腐蚀后失重大,力学性能下降幅度较大,腐蚀更严重.     

SO2在碳钢初期大气腐蚀中的作用

通过自建的模拟大气腐蚀系统,借助金相显微镜、扫描电镜(SEM/EDX)、X-射线衍射(XRD)和x-射线光电子能谱(XPS),研究了SO2对碳钢初期大气腐蚀行为的影响,并进一步用原子力显微镜从更微观的角度观察了在SO2环境中初期阶段腐蚀形貌变化.研究结果表明:在SO2污染大气环境中,随SO2浓度的升高碳钢腐蚀加快.在体积分数为5×10(-6)SO2的大气环境中,碳钢和耐候钢表面腐蚀主要以条状物生长,随着SO2浓度的升高,腐蚀产物的形貌发生改变,在体积分数为5×10(-5)SO2的大气环境中,条状锈和胞状锈同时生长.在锈层中S元素以FeSO4·4H2O的形式存在,腐蚀产物中还有γ-FeOOH.SO2在初期阶段加速了碳钢的腐蚀,降低了碳钢的耐蚀性.     

20^#钢板镀铬在海洋环境条件下的腐蚀行为分析

本文根据20^#钢板镀铬材料在我国海洋环境的暴露结果,对20^#钢板镀铬材料在我国海洋环境条件下的腐蚀速度及腐蚀原因进行分析。     

电子设备缓蚀剂对电子设备防护的应用研究

目的 研究DZ-1电子设备缓蚀剂用于电子设备防护的有效性.方法 参照MIL-PRF-81309G、MIL-L-87177A和Q/AVIC 03018中的试验方法,对自主研制的DZ-1电子设备缓蚀剂的性能进行全面评价.结果 DZ-1电子设备缓蚀剂没有闪点,在运输、储藏及使用过程中非常安全,使用性能良好,很容易去除,能够去...     

压气机叶片用耐冲刷防腐有机涂层的制备及性能研究

目的 提高压气机叶片有机涂层的耐冲刷和防腐性能.方法 以氨基改性环氧树脂为粘接剂,通过加入高硬度Al2O3填料以及其他着色、防锈颜料,并充分分散,制备一种具有耐冲刷防腐功能的有机涂层.通过摆杆硬度测试、磨耗测试、冲刷测试、腐蚀测试及其他力学性能测试,对耐冲刷防腐有机涂层的综合性能进行评价,对比高硬度Al2O3填料含量对...     

PHOSPHORUS MANAGEMENT TO PROTECT LAKE WATER QUALITY1

ABSTRACT: The Hallett Quarry gravel pit lakes are an active sand and gravel extraction operation located 0.4 km north of the City of Ames, Iowa. During periods of drought, these lakes serve as a supplemental water supply for Ames. A modified version of the Vollenweider input-output model was used to predict future water quality under various watershed land use, drainage, and lake configurations. The dominant factor controlling the future water quality of the lakes was found to be the nutrient input. It is recommended that a management plan to protect the future water quality should be oriented towards reducing the sources of phosphorus to the lakes.     

The impact of handpump corrosion on water quality in rural areas of West African sub-region

Water, even in its natural environment, contains some level of impurities. Water is nearly a universal solvent. It contains dissolved solids and gases, and hosts a number of micro-organisms. The exploitation of groundwater by means of boreholes for supplying small user groups and rural communities with water has been widely applied in certain parts of the world for several decades. In recent years this practice has spread all over the globe, and hundred of thousands of boreholes have beendrilled to tap low-yield aquifers. It is evident that such boreholes require pumps for lifting thewater. In developing countries these are usually handpumps, butsolar as well as other systems with submersible pumps are also used, depending upon the energy sources available and the financial means of the beneficiaries. This article gives a general overview of groundwater quality with regard to itsphysico-chemical composition. The results presented originatefrom the experience gained from handpump equipped boreholes within the UNICEF through German Centre for Technical EducationTransfer executed inter-regional UNDP-Handpumps Project inWest African Regions. Particular attention is paid to presenting corrosion onthe water quality of wells in terms of iron concentrationand other parameters. Furthermore, the corrosion attack ongalvanised iron, the effect of biofilms on the corrosionrate, and the difference between internal and externalcorrosion of rising mains are shown.     

Exposure Programme on Atmospheric Corrosion Effects of Acidifying Pollutants in Tropical and Subtropical Climates

Many national exposure programmes have been performed in tropical and subtropical climates during the last 50 years. However, ambitious programmes involving more than a few countries are scarce. In this paper a recently formed network of test sites is described involving 12 test sites in Asia (India, Vietnam, Thailand, Malaysia and China including Hong Kong) and four test sites in Africa (South Africa, Zambia and Zimbabwe). This effort is part of the 2001–2004 Swedish International Development Agency (SIDA) funded Programme on Regional Air Pollution in Developing Countries (RAPIDC). Corrosion attack after one (2002–2003) year of exposure (carbon steel, zinc, copper, limestone and paint coated steel) are presented together with environmental data (SO₂, NO₂, HNO₃, O₃, particles, amount and pH of precipitation, temperature and relative humidity) for all the test sites. The obtained corrosion values are substantially higher than expected for limestone, higher than expected for carbon steel and lower than expected for zinc compared to values calculated using the best available dose–response functions.