热带海洋大气环境下X70管线钢的缝隙腐蚀行为研究

目的研究X70管线钢在热带海洋大气实海环境下的缝隙腐蚀行为。方法在距离湛江东海岛海岸50m和200 m处分别搭建楔型缝隙模型,安装大气环境Cl-收集装置和自动气象监测站。结果距离海岸越近,风速越大,大气中Cl-沉降速率也越大,X70管线钢缝隙腐蚀越严重。X70管线钢在距离海岸50 m处发生缝隙腐蚀的最大缝宽约为0.96 mm,200 m处最大缝宽约为3.75 mm,50 m处缝隙腐蚀更严重。结论缝隙腐蚀区域形成了氧浓差电池,同时随着缝隙液中Cl-向缝隙内迁移,发生闭塞区电池自催化过程,在二者共同作用下,缝隙腐蚀区域较非缝隙腐蚀区域腐蚀更严重。     

军绿有机涂层破损腐蚀行为研究

目的研究不同破损程度下军绿有机涂层的腐蚀行为,确定破损率对其防护性能变化的影响。方法通过人工制作不同的破损率,并利用电化学阻抗谱技术,研究不同破损程度下军绿有机涂层的电化学特征。结果根据不同破损程度下的军绿有机涂层的电化学特征,确定了涂层从完好到失效的四个阶段,初始完好阶段(破损率K≤0.0004%)、破损增大阶段(0.0016%K≤0.04%)、破损过大阶段(0.16%K≤1%)和失效阶段(4%K≤16%)。结论破损率K为0.04%的点是该涂层防护性能急转直下的转折点,因此破损率K大于0.04%时,应及时对车辆表面涂层进行修补和防护。     

船用钢板材料在淡水环境中初期腐蚀行为

目的研究船用钢板材料在长江淡水环境中的初期腐蚀行为。方法运用形貌分析、腐蚀质量损失、XRD、开路电位、极化曲线等方法研究Q235B和CCSA两种船用钢板材料在室外长江淡水环境中不同暴露方式(水面大气、半浸、全浸)及不同浸泡时间(0.5,1 a)腐蚀行为;室内长江淡水环境不同暴露方式(半浸、全浸)浸泡768 h内的腐蚀行为;室内长江淡水环境全浸泡下在不同时间(0~14 d)的电化学腐蚀行为。结果两种船用钢板材料在武汉长江淡水中腐蚀严重,半浸泡环境下腐蚀速率最大,达到100μm/a,水面区大气腐蚀速率最小,腐蚀速率为30μm/a左右,全浸区腐蚀速率为80μm/a左右,1 a和0.5 a的腐蚀速率相近,CCSA耐蚀性优于Q235B。室内长江淡水浸泡环境下两种船用钢板材料腐蚀电位随时间而降低,2d后趋于稳定;半浸泡环境下腐蚀速率大于全浸区;极化曲线说明浸泡2 d后,腐蚀速率降低且趋于稳定。结论 CCSA耐蚀性优于Q235B,半浸泡环境下腐蚀最严重,其次为全浸区,水面大气环境腐蚀最小。     

×飞机半封闭部位局部环境谱当量加速关系研究

目的确定局部环境谱当量加速关系。方法以×型飞机某半封闭关键部位为研究对象,依据其在机体中所处的位置及服役环境中各气候条件编制局部加速腐蚀试验环境谱,分别进行试验室周期浸润加速腐蚀和自然环境暴晒。借助涂层宏观、微观形貌检测、色差、光泽度等常规性能检测和电化学极化曲线测试,对两种不同环境下试验件进行性能测试。结果试验室周期浸润加速腐蚀196.6 h,相当于舰面停放1年,且经过实验室2个周期加速腐蚀与自然环境暴晒2年的试验件涂层形貌、失光率、色差、电化学性能一致。结论该局部环境谱当量加速关系准确可靠。     

自然型氨基酸及其钾盐的 CO2吸收和再生特性

在CO2吸收过程中,选择具有不挥发和不发生氧化降解特性的氨基酸盐吸收剂有助于降低吸收剂损失和减轻环境污染风险,故本研究以CO2吸收速率和再生速率为指标,对L-精氨酸和精氨酸钾（PA）吸收剂的CO2吸收性能和常压下热再生性能进行了实验分析,并研究了吸收剂质量分数、反应温度及吸收-再生循环次数对CO2吸收特性的影响,同时还与乙醇胺（MEA）、二乙醇胺（DEA）和三乙醇胺（TEA）进行了对比分析.结果表明,在实验的质量分数范围内,PA具有最高的CO2吸收速率和吸收能力,分别为24.5×10-3mol.（L.min）-1和1.99 mol.mol-1,比相同质量分数的MEA高2.1%和290.2%.温度影响结果表明,40℃时PA和MEA的CO2吸收速率均高于其他实验温度.相同再生条件下,PA的贫液CO2负荷要略高于MEA,但PA的再生程度可达72.8%,比MEA高19%.同时,3次＂吸收-再生＂循环之后,10%PA的CO2吸收能力仍可保持在1.03mol.mol-1,比10%MEA高255.2%.实验结果也表明,L-精氨酸具有较强的CO2吸收能力,其CO2吸收速率与同质量分数的DEA可比.     

Removal of Cd2+ from water by Friedel’s salt (FS: 3CaO.Al2O3·CaCl2·10H2O): Sorption characteristics and mechanisms

The development of low-cost and efficient new mineral adsorbents has been a hot topic in recent years. In this study, Friedel’s salt (FS:3CaO·A12O3 ·CaCl2 ·10H2O), a hexagonal layered inorganic absorbent, was synthesized to remove Cd2+ from water. The adsorption process was simulated by Langmuir and Freundlich models. The adsorption mechanism was further analyzed with TEM, XRD, FT-IR analysis and monitoring of metal cations released and solution pH variation. The results indicated the adsorbent FS had an outstanding ability for Cd(Ⅱ) adsorption. The maximum adsorption capacity of the FS for Cd(Ⅱ) removal can reach up to 671.14 mg/g. The nearly equal numbers of Cd2+ adsorbed and Ca2+ released demonstrated that ion-exchange (both surface and inner) of the FS for Cd(Ⅱ) played an important role during the adsorption process. Furthermore, the surface of the FS after adsorption was microscopically disintegrated while the inner lamellar structure was almost unchanged. The behavior of Cd(Ⅱ) adsorption by FS was significantly affected by surface reactions. The mechanisms of Cd2+ adsorption by the FS mainly included surface complexation and surface precipitation. In the present study, the adsorption process was fitted better by the Langmuir isotherm model (R2 = 0.9999) than the Freundlich isotherm model (R2 = 0.8122). Finally, due to the high capacity for ion-exchange on the FS surface, FS is a promising layered inorganic adsorbent for the removal of Cd(Ⅱ) from water.     

咸潮预警值设定的研究

为研究咸潮预警,上海某饮用水源地安装了蓝色卫士水质综合预警系统。采用实验室配制人工海水模拟减潮,通过动态实验研究蓝色卫士的成潮预警值。试验证明,成潮预警值设定范围为1．6～1．8较好。经过连续1a自动监测,蓝色卫士共准确预警预报两次成潮,成功保障了该水源地的饮水安全。     

储罐钢08MnNiVR和SPV490Q在石油沉积水中腐蚀性能对比

采用电化学试验、浸泡试验和慢应变速率拉伸试验研究储罐钢08MnNiVR和SPV490Q在石油沉积水中的腐蚀性能差异。电化学试验结果表明,08MnNiVR在石油沉积水中的自腐蚀电流比SPV490Q略大。浸泡试验结果表明,中短期试验时,08MnNiVR的腐蚀率略大;较长期试验时,SPV490Q的腐蚀率略大。慢应变速率拉伸试验结果表明,08MnNiVR和SPV490Q在石油沉积水中均具有高应力腐蚀抗力。     

LD2铝合金腐蚀行为研究

LD2铝合金广泛应用于直升机结构中。铝合金构件在服役过程中会承受环境所造成的疲劳损伤,从而大大降低其服役寿命,因此必须要研究该材料的腐蚀行为。利用SEM扫描电镜,结合能谱分析对铝合金腐蚀损伤行为进行了高精度微尺度研究,并在疲劳断口上发现腐蚀坑底部的“隧道”,该腐蚀隧道会使腐蚀损伤评定过于保守,为结构寿命预测带来较大的不确定性。     

航空高强度LY12CZ铝合金腐蚀剩余强度预测

摘要：目的研究LY12CZ铝合金在腐蚀环境下的强度退化规律。方法按ASTM标准对常温下的LY12CZ铝合金进行预腐蚀,测量腐蚀坑的深度,统计腐蚀坑数目,进行数理统计,获得其几何尺寸的分布。利用MTS880试验机进行静拉伸试验。建立腐蚀坑的物理模型,基于腐蚀坑平均特征参数和最大特征参数,利用AFGROW软件进行剩余强度预测。结果剩余强度随着腐蚀损伤加深而逐步减小。结论与实验值对比的结果证明,该方法具有应用价值。