燃煤烟气低温SCR脱硝中试研究

低温选择性催化还原(SCR)脱硝是国内外脱硝技术研发的热点,但目前主要集中在实验室小试范围,无法完全反映催化剂在实际烟气中的运行状况。在30 t/h循环流化床燃煤锅炉脱硫除尘装置后建设了2 000~5 000 m3/h的SCR脱硝中试装置,经系统研究发现,中试使用的蜂窝式催化剂对SO2和NO具有很强的吸附能力,且反应温度、喷氨速率和气体空速均会影响催化脱硝效率。为期5 d的连续运行实验结果表明,催化剂的脱硝效率一直稳定在30%~50%,并未发现明显的失活,这证明设计除雾除尘器、较大的混合器、混合器与反应器间较长的管路均有利于缓解催化剂因SO2、H2O和飞灰中的碱性金属导致的失活。     

CuO / 过硫酸氢钾体系催化氧化苯酚简

本论文通过直接沉淀法制备了CuO催化剂,结合过硫酸氢钾,在常温常压下催化氧化处理苯酚模拟废水。采用电子显微镜（SEM）、X射线粉末衍射（XRD）对催化剂进行了表征,并研究了反应过程中各影响因素对降解效率的影响。实验结果表明,在催化剂用量为0.2 g/L,氧化剂浓度为0.25 g/L,pH值为7,反应时间为60 min的条件下,浓度为50 mg/L的苯酚降解率可达100%,TOC去除率达84%。进一步实验表明,催化剂具有良好的重复使用能力。最后,通过自由基捕捉实验,考察了体系中的自由基种类,并根据实验结果,讨论了CuO/过硫酸氢钾体系的催化降解机理。     

Mn/γ-Al2O3催化剂的制备及头孢合成废水的催化臭氧氧化法深度处理

对Mn/γ-Al₂O₃催化剂的制备条件及头孢合成废水的催化臭氧氧化法深度处理工艺条件进行了优化。实验结果表明：以Mn（NO₃）₂溶液为浸渍液,Mn/γ-Al₂O₃催化剂的最优制备条件为浸渍液浓度0.10 mol/L、浸渍时间9 h、焙烧温度400 ℃、焙烧时间2 h;在反应时间为30 min、废水pH为9.0、臭氧通量为4.6 mg/min、催化剂加入量为5 g/L的条件下,当进水COD、BOD₅、ρ（氨氮）和色度分别为220~250 mg/L,8~10 mg/L,10~12 mg/L和60~70倍时,出水COD、BOD₅、ρ（氨氮）和色度的平均去除率分别为53%,30%,33%和93%,出水水质满足GB 21904—2008《化学合成类制药工业水污染物排放标准》的要求。     

新型二氧化铅电极处理染料废水

利用高压塑片法制备掺杂镧和活性炭以及聚四氟乙烯(PTFE)的新型二氧化铅电极,采用X衍射(XRD),循环伏安曲线(CV),扫描电镜(SEM)等手段对电极性能进行表征,研究了其电催化处理有机染料废水(亚甲基蓝)的降解效果,并对反应机理进行了相关研究。研究表明,该电极具有良好的抗腐蚀能力,对亚甲基蓝具有较好的降解效果。通过与普通二氧化铅电极比较,该电极在染料脱色和去除COD方面都有较明显优势,显示出较好的工业应用前景。     

铁氧化物复合氧化铝催化臭氧化过程中溴酸盐的生成控制

以市售活性炭、硅藻土和氧化铝小球为载体,考察了负载铁基活性组分对催化臭氧化过程中溴酸盐的控制情况,其中,铁基复合氧化铝小球体现出更好的溴酸盐还原特性和催化剂稳定性,证实催化剂中铁氧化物是溴酸盐得到有效控制的主要活性组分。进一步考察了铁基复合氧化铝小球催化臭氧化处理实际原水过程中对溴酸盐的生成控制,以及反应过程中溶解性有机碳（DOC）的去除情况。结果表明,与单独臭氧化相比,该催化剂既能有效去除水中的溶解性有机物,又能明显抑制溴酸盐的生成,反应50h,其活性并没有明显下降。催化剂失活主要归因于吸附位点数量的下降,可以通过负载铁氧化物来实现催化剂的再生。     

催化湿式氧化预处理造纸黑液

采用连续式固定床反应器,利用自制稀土类复合金属氧化物催化剂对草浆造纸黑液进行了催化湿式氧化(CWAO)预处理研究.通过正交实验确定了最佳工艺条件为:进水COD 40 800 mg/L,空速0.8h-1,反应温度260℃,反应压力6.5 MPa.在此最佳条件下进行实验,COD去除率达90％.经CWAO工艺处理后,草浆造纸...     

Ozone facilitated degradation of caffeine using Ce-TiO2 catalyst

The ozone initiated oxidation of 1,3,7-trimethylxanthine (caffeine), commonly found in wastewaters as model compound is reported using cerium (Ce)/titanium dioxide (TiO₂) as catalyst. The effect of pH and loading of ceria on titania were investigated. Effect of reaction conditions on degradation of caffeine based on their pseudo first-order rate constants were compared. The combination of catalyst Ce-TiO₂ and ozone aeration significantly enhanced the degradation of caffeine compared to uncatalysed ozonation. The oxidation of caffeine ensued via the free radical mechanism, through enhanced ozone decomposition into OH radicals. Ce/TiO₂(0.5?wt%) showed good activity in degradation of caffeine at pH 6, in both natural stream and river water samples showing about 60% total organic carbon removal in 2?h ozonation period. Using liquid chromatography-mass spectroscopy, degradation products were analysed. A reaction intermediate and one final product were positively identified. Nano-catalysts with different loadings of Ce on TiO₂ synthesized by sol-gel route were characterized by scanning electron microscope, transmission electron microscopy, BET and powder X-ray diffraction spectrum techniques. The results showed that the material retained a highly ordered mesoporous structure and possessed large surface area.     

CeO2/TiO2纳米管催化剂脱硝性能研究

利用废气中本身含有的CO催化还原烟气中的NO_x,可以实现以废治废。采用TiO₂纳米管负载CeO₂,制备CeO₂/TiO₂纳米管催化剂,并对其进行了SEM表征及影响因素实验。实验结果表明：在n（Ce）∶n（Ti）=3∶7、焙烧温度500 ℃、焙烧时间3 h时制备的CeO₂/TiO₂纳米管催化剂形貌较好,表面颗粒分布相对均匀;反应温度400~600 ℃时NO脱除率达98%;该催化剂具有一定的抗氧性能;当n（SO₂）∶n（NO）=（1∶2）~（2∶1）时,NO脱除率仍然在95%以上。     

CePO4-TiO2固溶体的NH3-SCR活性

采用共沉淀法合成了不同Ce与Ti摩尔比的CePO₄-TiO₂复合材料,利用XRD、TEM、NH₃-TPD和H₂-TPR技术对其物理化学性质进行了表征,并对其NH₃-SCR活性进行了评价。实验结果表明：随着CePO₄含量的增加,催化剂的活性提高;当Ce与Ti的摩尔比为8:2时催化剂的活性最高,230 ℃的NO转化率达到100%,且具有更广的温度窗口,优于纯CePO₄。表征结果显示,CePO₄与TiO₂形成固溶体后,颗粒尺寸较为均匀,强酸位的数量增多,氧化还原性能提升,从而提高了催化剂的SCR反应活性,同时改善了其抗水抗硫性能。     

预氧化聚丙烯腈/g-C3N4光催化降解罗丹明B

以聚丙烯腈(PAN)和g-C_3N_4为原料,采用超声波辅助分散的溶液浸渍法及煅烧法制备了具有共轭结构的预氧化聚丙烯腈/g-C_3N_4复合光催化剂(CPAN/g-C_3N_4),采用XRD、SEM、FTIR、UV-Vis DRS、EIS等技术对光催化剂进行了表征,考察了CPAN/g-C_3N_4对罗丹明B(Rh B)的可见光催化降解性能。结果表明:CPAN与g-C_3N_4具有良好的协同作用,使g-C_3N_4片状结构堆叠体颗粒显著减小,明显增强了光催化剂在全部光谱范围内的光吸收,有效提高了光生电子-空穴分离效率;在PAN与g-C_3N_4质量比为1∶200、煅烧温度250 ℃、煅烧时间1 h条件下所制备的CPAN/g-C_3N_4光催化活性最高,且具有良好的光催化活性稳定性。超氧自由基和光生空穴为CPAN/g-C_3N_4复合光催化剂光降解罗丹明B的主要活性物种。