瓷砖釉面TiO2薄层对甲基橙的光催化降解

采用溶胶-凝胶法，在瓷砖釉面上制备了良好光催化活性TiO2薄层材料，研究结果表明瓷砖釉面TiO2薄层材料对甲基橙的光催化反应遵循一级动力学规律，光催化降解率与液层厚度符合指数关系。在太阳光照射下，釉面瓷砖TiO2薄层材料能对甲基橙有效地降解。     

太阳能光催化降解法去除水中罗丹明染料的研究

在太阳光的紫外线辐射下，应用载有ＴｉＯ２薄层的平板式光催化反应器，进行了光催化降解法去除水中罗丹明染料的试验，结果表明，当紫外线辐射强度平均为３３Ｗ／ｍ＾２，反应时间为１８ｍｉｎ时，水中罗丹明染料浓度由１０ｍｇ／Ｌ降至０．０１ｍｇ／Ｌ，在室国家排放标准，探讨了太阳能光催化反应系统的改进方向及工业化应用的有关问题。     

Starch- polyvinyl alcohol crosslinked film— performance and biodegradation

Starch-PVOH cast films were prepared with and without crosslinking agent (hexamethoxymethylmelamine) in the absence of plasticizer. Moisture absorption in films without crosslinking agent at a low relative humidity was similar to that of PVOH and increased as the relative humidity increased. Films with crosslinking agent showed moisture absorption linearly proportional to the relative humidity. Significant improvement in resistance to water disintegration for crosslinked starch-PVOH films was observed. While the tensile strength decreased with increased relative humidity, crosslinking significantly improved the tensile strength. Increased PVOH content improved elongation of films even when the relative humidity was 80% or higher. Biodegradation studies revealed that the degradation rate was negatively correlated with the PVOH content in films and crosslinking generated more converged degradation curves. Names are necessary to report factually on available data; however, the USDA neither guarantees nor warrants the standard of the product, and the use of the name by USDA implies no approval of the product to the exclusion of others that may also be suitable.     

活性炭膜处理工业废水的试验研究

将活性炭膜与常规弹性材料同时作为生物接触氧化处理工艺的填料,分别加装在相同条件的两套接触氧化池中,采用生物接触氧化处理工艺,在同样的条件下处理工业废水,经过对试验数据的对比分析得出:以活性炭膜为填料,处理废水的能力更强,净化效果更好。     

从废感光胶片中回收银

研究了以Fe3 -乙二胺四乙酸二钠-N a2S2O3体系为浸取剂从废感光胶片中回收银的方法,考察了浸出银的最佳工艺条件。实验表明,当浸取剂中FeC l3.6H2O质量浓度为35g/L、N a2S2O3.5H2O质量浓度为150g/L、pH为7、固液质量比为3∶10时,浸取剂可重复使用6次,胶片上银的浸出率可达99%以上;浸取液中的银采用硼氢化钠还原回收,粗银粉配以熔剂高温熔炼可得到纯度达99.78%的银,银回收率达96.88%,回收银后的浸取液可循环使用。     

Mechanical Properties with the Functional Group of Additives for Starch/PVA Blend Film

This paper deals with the mechanical properties and degree of swelling (DS) of starch/PVA blend film with the functional groups i.e., hydroxyl and carboxyl group, of additives. Starch/PVA blend films were prepared by using the mixing process. Glycerol (GL) with 3 hydroxyl group, sorbitol (SO) with 6 hydroxyl group, succinic acid (SA) with 2 carboxyl group, malic acid (MA) with 1 hydroxyl and 2 carboxyl group, tartaric acid (TA) with 2 hydroxyl and 2 carboxyl group and citric acid (CA) with 1 hydroxyl and 3 carboxyl group were used as additives. The results of measured tensile strength (TS) and elongation (%E) verified that both hydroxyl and carboxyl group as a functional groups increased the flexibility and strength of the film. Values of DS for GL-added and SA-added films were low. However, DS values of the films added MA, TA or CA with both hydroxyl and carboxyl group were comparatively high. When the film was dried at low temperature, the properties of the films were evidently improved. The reason is probably because the hydrogen bonding was activated at low temperature.     

TiO2光催化氧化的研究进展

概述了TiO2光催化氧化降解水中污染物的原理及TiO2光催化剂的制备，提出了增强其活性的途径。TiO2光催化氧化可应用于印染、农药、造纸等工业废水及饮用水处理中，研制高效的负栽型纳米TiO2光催化剂、解决太阳能利用问题、开发多功能光催化反应器是今后TiO2光催化氧化的发展趋势。     

Mechanical and Barrier Properties of Biodegradable Films Made from Chitosan and Poly (Lactic Acid) Blends

Biodegradable film blends of chitosan with poly(lactic acid) (PLA) were prepared by solution mixing and film casting. The main goal of these blends is to improve the water vapor barrier of chitosan by blending it with a hydrophobic biodegradable polymer from renewable resources. Mechanical properties of obtained films were assessed by tensile test. Thermal properties, water barrier properties, and water sensitivity were studied by differential scanning calorimeter analysis, water vapor permeability measurements, and surface-angle contact tests, respectively. The incorporation of PLA to chitosan improved the water barrier properties and decreased the water sensitivity of chitosan film. However, the tensile strength and elastic modulus of chitosan decreased with the addition of PLA. Mechanical and thermal properties revealed that chitosan and PLA blends are incompatible, consistent with the results of Fourier transform infrared (FTIR) analysis that showed the absence of specific interaction between chitosan and PLA.     

炼油污水的深度处理

对炼油污水深度处理常用技术——过滤、膜分离、化学氧化技术进行了详细的论述，并结合中试试验，对动态砂滤系统、PAN膜处理系统和高级氧化系统处理炼油厂二级排放水的适用性进行了论证。     

β-In2S3的制备及其太阳光下降解土霉素

利用水热反应法制备β-In2S3纳米颗粒光催化剂,并利用SEM、TEM和XRD等对其进行分析表征;采用土霉素溶液模拟四环素类抗生素废水,探讨In2S3对土霉素的降解效果.结果表明,β-In2S3为立方相纳米颗粒结构,该纳米颗粒由纳米片组成,直径约15~30 nm.以太阳光为辐射光源,In2S3对土霉素具有良好的光催化降解效果,在4 h内对初始浓度为30 mg·L-1的土霉素降解率可达98%以上.降解土霉素后的催化剂在无水乙醇中清洗并烘干,经4次循环利用后,β-In2S3的降解能力仍能达到85%以上,表明β-In2S3光催化剂具有良好的稳定性以及光催化活性.