金属掺杂纳米TiO2薄膜的制备和抗菌性能研究

采用sol—gel法在载玻片表面制备了Ce,Cu,i．a,Ag掺杂的锐铁矿相TiO2薄膜,并通过SEM,XRD．FT—IR及UVVIS进行了表征,比较了薄膜的抗菌性能．UV—VIS研究表明,金属掺杂纳米TiO2薄膜在近紫外区吸光度有明显提高。抗菌实验表明掺Ag的TiO2薄膜抗菌效果最佳。     

高度有序的TiO2纳米管阵列光催化性能研究

采用恒压阳极氧化法在纯钛箔表面制备TiO2纳米管阵列,利用SEM和XRD对其进行了形貌和晶型的分析和表征,并通过TiO2纳米管阵列膜对甲基橙光催化降解,探讨光照时间、甲基橙溶液的初始浓度、溶液的初始pH值和H2O2加入浓度等因素对甲基橙的脱色率影响.结果表明,H2O2加入浓度为50mg·L-1,紫外光照射2h,溶液为中性时,在30 mg·L-1的甲基橙溶液(50mL)中,甲基橙溶液的脱色率达到100%.当H2O2加入浓度进一步增大到100 mg·L-1时,光催化的效率进一步提高,紫外光照射1h,甲基橙溶液的脱色率就已经达到了100%,并未出现抑制光催化的现象.同时还研究了TiO2纳米管阵列电极的稳定性.实验结果表明,随着TiO2纳米管阵列使用次数的增加,其光催化效果略有所下降.     

镧掺杂氧化锌光催化降解染料废水研究

以醋酸锌和硝酸镧为原料,丙烯酰胺为单体,N,N’-亚甲基双丙烯酰胺为网络剂,过硫酸铵为引发剂,采用高分子网络凝胶法制备得到掺镧的Zn O纳米粉体。用制备的粉体对甲基橙进行光催化降解实验,考察了掺镧量对其光催化性能的影响。用X射线衍射仪、高分辨率透射电镜、X射线能谱仪、比表面积与孔隙率分析仪等对其进行表征。结果表明,镧的掺入提高了Zn O的光催化活性,镧锌摩尔质量比为0.2%时光催化性能最好,高压汞灯下反应1 h,甲基橙的脱色率为96.5%,相比于未掺杂的Zn O提高了11.5%。     

RGO/TiO2光催化降解2,4-二氯苯氧乙酸研究

通过Hummers法及紫外光/热还原工艺制得还原氧化石墨烯(RGO),采用溶胶-凝胶-煅烧法,以RGO和钛酸酊脂为前驱体制备出RGO/TiO2光催化复合材料,并利用XRD、FT-IR等对其进行了表征.对RGO/TiO2光催化降解性能的研究发现,复合光催化剂RGO/TiO2对2,4-二氯苯氧乙酸(2,4-D)的光催化降解活性显著优于纯TiO2,并且发现负载量和pH值对光催化降解性能有较大的影响:RGO/TiO2投加量为1.2g·L~(-1)、RGO负载量2%、pH为3、初始浓度为50 mg·L~(-1)反应12 h,2,4-D去除率达到98.75%;2,4-D降解率随着RGO/TiO2投加量的增大先增大后减小;RGO/TiO2对2,4-D的降解为脱氯还原和催化氧化过程,产生氯酚、苯酚等中间产物.     

光催化氧化技术降解水中双酚A的研究进展

目前环境雌激素双酚A(bisphenol A,BPA)所带来的危害已成为学术研究的热点问题。光催化氧化技术作为新兴的高级氧化技术,可快速降解水中双酚A。介绍了几种主要的光催化氧化技术降解双酚A的机理,并综述了国内外利用新型光催化剂在降解双酚A领域所取得的研究进展,为光催化氧化技术在双酚A降解领域的研究提供参考。     

三氧化钨光催化法脱色处理化纤厂废水

以WO3粉体作为催化剂对化纤厂废水采用光催化氧化法进行脱色处理,讨论了光催化氧化法的反应机理,以及化纤厂废水的pH值、光催化剂的投入量、光照时间各因素对废水色度去除率的影响。实验结果表明：WO3粉体的投入量为1．000g／L,pH值为3．00时,利用300W高压汞灯光照7h后,废水试样的吸光度由0.596降低至0．020,色度去除率达到96．6％。     

Photocatalytic remediation of γ-HCH contaminated soil induced by α-Fe2O3 and TiO2

Heterogeneous photocatalytic degradation of γ-HCH on soil surfaces was carried out to evaluate the photocatalytic effectiveness of α-Fe2O3 and TiO2 toward degrading γ-HCH on soil surfaces. After being spiked with γ-HCH, soil samples were loaded with α-Fe2O3 or TiO2 and exposed to UV-light irradiation. Different catalyst loads(0%, 2%, 5%, 7%, and 10% (wt). α-Fe2O3; 0%, 0.5%, 1%, 2% wt. TiO2) were tested for up to 7 d irradiation. The effects of soil thickness, acidity, and humic substances were also investigated. The obtained results indicated that the γ-HCH photodegradation follows the pseudo-first-order kinetics. The addition of α-Fe2O3 or TiO2 accelerates the photodegradation of γ-HCH, while the photodegradation rate decreases when the content of α-Fe2O3 exceeds 7%(wt.). The degradation rate increases with the soil pH value. Humic substances inhibit the photocatalytic degradation of γ-HCH. Pentachlorocyclohexene, tetrachlorocyclohexene, and trichlorobenzene are detected as photodegradation intermediates, which are gradually degraded with the photodegradation evolution.     

3种染料化合物在UV-TiO2/H2O2和UV-TiO2体系中的光催化降解研究

采用自制的TiO2膜和平板式固定床型光催化氧化反应装置,对甲基橙、茜素红和罗丹明B 3种含有不同生色基团的染料化合物进行了TiO2光催化氧化降解研究,通过对照测定降解过程中吸光度、电导率、pH的变化,分析了在加入和不加入H2O22种情况下降解过程的异同,比较了3种染料化合物脱色的难易程度,揭示了降解产物中无机离子的变化规律及某些可能的产物类型.     

太阳光催化氧化工艺对藻源含氮有机物的降解研究

利用小试试验研究了太阳光/TiO2体系对铜绿微囊藻细胞内的溶解性有机氮(DON)的氧化降解过程,考察了氧化降解过程中总可溶性蛋白、多糖、UV254等指标的变化,分析了其作用机理.结果表明,7h处理后,太阳光/TiO2体系对水样中的DON降解率为29%,且降解过程中TN含量基本没有变化,而NH4+和NO3-的浓度明显增加;氧化过程中,总可溶性蛋白和多糖的含量明显减少,去除率达48.6%和54.5%.水样的浑浊度、UV254和DOC也有不同程度的去除.     

稀土Ce3+掺杂Bi2WO6光催化降解罗丹明B的研究

采用水热合成法制备稀土元素Ce3+掺杂Bi2WO6光催剂,通过X射线衍射、场发射电镜扫描、紫外-可见漫反射光谱、N2物理吸附-脱附等手段对合成材料的结构、形貌、光吸收等物理化学性能进行表征,并以染料废水中罗丹明B的降解考察其光催化活性.结果表明,Ce3+掺杂量为0.05%时,其结晶度好、颗粒较均匀、具有较强的可见光吸收性能,且比表面积比纯Bi2WO6提高近10%以上,对罗丹明B的去除效果最好;催化剂用量越高、罗丹明B的初始浓度越低、反应溶液pH值越低、H2O2的浓度越高越有利于Ce/Bi2WO6对罗丹明B的吸附和降解;而阴阳离子的影响各不相同:NO3-、SO42-没有太大的影响; Na+、K+、Ca2+、Mg2+、Cl-的加入均促使的染料的去除;HCO3-抑制了罗丹明B的吸附,但是却促进了光降解.另外,经重复使用3次,光催化降解速率常数并没有降低,表明稀土Ce3+改性Bi2WO6是一种有效稳定的光催化剂.