BiOCl/MWCNTs复合催化剂对罗丹明B光催化降解研究

以B(iNO3)3.5H2O和NaCl为原料,多壁碳纳米管(MWCNTs)为载体,水解法合成碳纳米管负载氯氧化铋复合型光催化剂(BiOCl/MWCNTs)。通过TEM、XRD、UV-Vis对催化剂的微观形貌、主要成分和光学吸收进行了表征,并以500 W氙灯为可见光光源,研究了其对罗丹明B的光催化降解能力。TEM和XRD结果表明,复合催化剂中BiOCl成块状与MWCNTs结合,粒径小,分散好;UV-Vis则显示,BiOCl/MWCNTs对420⁷80 nm波长段的光的吸收强于BiOCl,有利于可见光催化。光照2.5 h后,BiOCl和BiOCl/MWCNTs对罗丹明B的降解率分别达到78%和96%。BiOCl/MWCNTs对罗丹明B光催化反应符合一级反应动力学特征,速率常数为1.23 h-1,相比BiOCl提高了98.2%。     

负载型TiO2-xNx的制备表征及可见光催化降解亚甲基蓝

以溶胶-凝胶法制备TiO2溶胶,负载于玻璃微珠表面,在NH3气流中直接进行热处理,制备负载型掺氮纳米TiO2薄膜催化剂.选取亚甲基蓝为处理对象,结合对催化剂表面结构、晶型和紫外可见吸收的表征,对制备的催化剂进行评价.结果表明,450℃下焙烧3 h所制备的负载型催化剂为锐态矿相;可见光的范围拓展到700 nm左右;负载均...     

AgI/TiO2催化剂的焙烧处理及其可见光催化活性

常温下以TIO2为载体,使用沉积-沉淀法合成了具有不同AgI负载量的AgI/TiO2合光催化剂,并研究了焙烧处理对AgI/TiO2在可见光下(λ＞420nm)催化降解甲基橙(MO)的影响.结果表明,焙烧处理有效提高了AgI/TiO2的光催化性能,当焙烧温度高于200℃时,AgI/TiO2的光催化活性接近并达到最大值.当负载的AgI与TiO2的物质的量之比为0.15时,AgI%TiO2光催化降解MO的效率最高.XRD和UV-Vis测试表明焙烧处理提高了光敏组分AgI混晶中的γ相含量,拓宽了AgI/TiO2在可见光区的吸收范围,提高了光催化活性.     

可见光TiO2光催化降解微囊藻毒素的研究进展

蓝藻释放出的微囊藻毒素严重威胁着人类的健康,不仅对人类的肝脏造成严重的损伤,对人类的生殖生长发育也有潜在的影响。针对上述情况,文章简要评析了微囊藻毒素处理的总体研究现状,以微囊藻毒素的分子结构和理化性质为基础,重点阐明了光催化的机理与微囊藻毒素光催化过程中的中间产物,详细介绍了可见光催化降解微囊藻毒素的途径,阐述了提高二氧化钛可见光活性的方法以及常见的可见光催化处理工艺,叙述了可见光催化降解微囊藻毒素的影响因素,并指出当前探索所遇到的问题以及未来研究的发展趋势,以期为该领域的进一步研究提供参考。     

CdSe QDs/TiO2复合催化剂对氨氮废水的光降解性能研究

针对氨氮废水的有效处理,文章以水相合成法制备CdSe量子点溶液,通过巯基丙酸将CdSe量子点负载在P25载体上,制备了CdSe QDs/TiO₂复合光催化剂。通过TEM、XRD、XPS和EIS等表征测试结果,分析证实了复合催化剂的结构和可见光吸收能力。在弱碱条件下,通过考察助催化剂、CdSe QDs负载量、催化剂投加量和氨氮初始浓度等因素,评价了该体系在多因素影响下的光催化降解效率。结果表明,氨氮初始浓度为50 mg/L,pH=9,CdSe QDs负载量为1%,催化剂添加量为0.05 g,K₂S₂O₈添加量为0.054 g (2 mmol/L)时,光催化降解效果最佳,氨氮降解率达到81.79%。通过活性物质捕获实验研究了CdSe QDs/TiO₂光催化降解氨氮废水的机理,证实了体系中主要氧化活性物质为·O₂^-。     

可见光激发下模拟海水中四环素光降解的机制和路径

为了探明海水体系中多相光催化降解污染物的机制和路径,研究了在可见光激发下不同介孔TiO₂光催化降解纯水和模拟海水中四环素(TC)的过程,明确了不同盐离子对光催化降解过程的影响.结合自由基捕获实验,电子自旋共振(ESR)光谱和中间产物分析研究了光降解污染物的主要活性物种和模拟海水中TC降解途径.结果表明,模拟海水中TC光催化过程会受到显著抑制,手性介孔TiO₂催化剂对TC光降解反应速率相比其在纯水体系降低了70%左右,而非手性TiO₂光催化剂在海水体系中几乎不能降解TC.模拟海水中阴离子对光降解过程影响较小,但Mg²⁺和Ca²⁺存在会显著抑制光催化过程.无论在纯水还是模拟海水中,可见光激发后催化剂产生的活性物种都是空穴为主,因此模拟海水中降解路径与纯水体系中相同.盐离子不会抑制活性物种的产生,但Mg²⁺和Ca²⁺会富集在TC分子中电负性强的原子周边,阻碍空穴等对TC分子中电负性强原子的攻击,从而抑制了光催化降解效率.     

Effect of TiO2 calcination temperature on the photocatalytic oxidation of gaseous NH3

Carbon-modified titanium dioxide(TiO2) was prepared by a sol-gel method using tetrabutyl titanate as precursor, with calcination at various temperatures, and tested for the photocatalytic oxidation(PCO) of gaseous NH3 under visible and UV light. The test results showed that no samples had visible light activity, while the TiO2 calcined at 400℃ had the best UV light activity among the series of catalysts, and was even much better than the commercial catalyst P25. The catalysts were then characterized by X-ray diffractometry, Brunauer-Emmett-Teller adsorption analysis, Raman spectroscopy, thermogravimetry/differential scanning calorimetry coupled with mass spectrometry, ultraviolet-visible diffuse reflectance spectra, photoluminescence spectroscopy and in situ diffuse reflectance infrared Fourier transform spectroscopy. It was shown that the carbon species residuals on the catalyst surfaces induced the visible light adsorption of the samples calcined in the low temperature range( 300℃). However, the surface acid sites played a determining role in the PCO of NH3 under visible and UV light over the series of catalysts. Although the samples calcined at low temperatures had very high SSA, good crystallinity, strong visible light absorption and also low PL emission intensity, they showed very low PCO activity due to their very low number of acid sites for NH3 adsorption and activation. The TiO2 sample calcined at 400℃ contained the highest number of acid sites among the series of catalysts, therefore showing the highest performance for the PCO of NH3 under UV light.     

纳米TiN制备可见光活性TiO_2光催化剂的研究

在O2/N2混合气氛中煅烧TiN纳米粒子,制备出了一种响应可见光的氮掺杂TiO2光催化剂(TiO2-xNx)。紫外-可见吸收光谱表明,该光催化剂在可见光区具有明显的吸收。该光催化剂的XRD图谱表明,TiO2-xNx的晶型为锐钛矿相和金红石相的混合相。甲基橙溶液的降解实验结果表明,在O2/N2比例为1∶15(体积比),通氧时间为15 min,煅烧温度为650°C时,制得的催化剂活性最高。     

卟啉铁敏化二氧化钛可见光降解甲基橙

以卟啉铁为敏化剂,P25为二氧化钛载体,采用化学吸附合成了卟啉铁敏化二氧化钛复合催化剂:Fe Pp/Ti O2。利用SEM、XRD、DRS、对复合催化剂Fe Pp/Ti O2进行了表征和分析,分析结果表明,Fe Pp吸附于二氧化钛表面,未改变二氧化钛的形貌和晶型,卟啉铁使二氧化钛在可见光区(λ≥420 nm)有显著的吸收。可见光降解甲基橙结果表明,与未敏化的Ti O2相比,Fe Pp/Ti O2在可见光区(λ≥420 nm)能有效提高甲基橙溶液的降解率,3 h降解达到95.8%,并且催化性能稳定,可重复利用。     

Zn/TiO_2/泡沫镍可见光光电催化氧化水体中As(Ⅲ)

采用阴极电沉积法在泡沫镍上负载Zn掺杂TiO2,制得Zn/TiO2/泡沫镍光催化剂,利用X射线衍射仪(XRD)、扫描电镜(SEM)、X射线光电子能谱(XPS)等对其进行了晶体结构、表观形貌、表面元素状态的分析,并研究了Zn/TiO2/泡沫镍在可见光照射和负偏压作用下光电催化氧化水体中As(Ⅲ)的反应性能。试验结果表明:Zn成功以替代的形式进入TiO2晶体内,Zn/TiO2/泡沫镍在可见光照射和最佳偏压-0.4V作用下,光电催化氧化As(Ⅲ)的反应速率为TiO2/泡沫镍的1.5倍以上;当Zn2+掺杂量为0.52%,初始As(Ⅲ)浓度为1.0mg/L,pH值为7±0.05,光照3h,施加-0.4V偏压时,As(Ⅲ)的去除率高达92.6%,此时氧化As(Ⅲ)的主要物质为超氧自由基,超氧自由基在光照作用下进一步转化成羟基自由基氧化As(Ⅲ);负偏压同时起阴极保护作用,避免引起基材金属镍溶出,可应用于处理饮用水。