沿海钢结构设施的防腐研究

针对沿海钢结构设施的腐蚀情况及目前常用防腐涂料的性能,优选了3种重防腐涂料——环氧富锌底漆、环氧玻璃鳞片中间漆、聚氨酯面漆。讨论了环氧树脂、锌粉、玻璃鳞片、聚氨酯改性树脂的选择方法,并提出了适合涂料涂装的表面处理技术和施工工艺。     

复合污染中Triton X-100在膨润土/水界面上的吸附行为

研究了水溶液中膨润土对非离子表面活性剂Triton X-100(X-100)的吸附,重点探讨了阳离子表面活性剂CPC、阴离子表面活性剂SDBS、中性无机盐NaCl及温度对膨润土吸附TX-100的影响.结果表明,Na基膨润土吸附TX-100的效果好于Ca基膨润土;低浓度CPC对膨润土吸附TX-100具有增强作用,当CPC初始浓度大于l0000 mg·L-1(平衡浓度Ce约为1CMC)时具有抑制作用,当CPC浓度低于3000 mg·L-1(Ce约为0.03CMC)时,TX-100吸附量与CPC浓度成线性正相关.SDBS能显著降低膨润土对TX-100的吸附,原因是溶液中SDBS与TX-100混合胶束的形成能阻止TX-100与膨润土硅氧表面间的氢键作用及在其表面形成胶束.NaCl的存在可以大大提高膨润土对TX-100的吸附,去除率由56%提高到99%以上.膨润土对TX-100的吸附随温度升高吸附量增大,其吸附热为12.68 kJ·mol-1,标准自由能的减小和熵值的增大是TX-100在膨润土上吸附的推动力.实验结果对用膨润土处理含表面活性剂废水具有一定的理论价值.     

烷基酚及其聚氧乙烯醚的测定

本文介绍了同位素标记或多克隆抗体酶联免疫法适于测定生物体中微量APE及其降解产物,固定酶酶联免疫检测法(ELISA)可检测出～10 ng/mL的壬基酚和相关化合物.     

好氧颗粒污泥膜生物反应器污泥性状研究

采用厌氧-好氧运行方式的颗粒污泥膜生物反应器（GMBR）,连续运行近120　d表现出良好的有机物去除及同步硝化反硝化能力.对GMBR中污泥粒径分布变化研究表明,GMBR中污泥浓度的增加主要是由于粒径0.18～0.45　mm的小颗粒污泥及小于0.18　mm的絮状污泥的增加造成的,粒径大于0.45　mm的颗粒污泥能够基本稳定维持其颗粒形态,反应器运行末期,GMBR中颗粒污泥（粒径大于0.18　mm的污泥）含量稳定在污泥总量的60％～65％以上.污泥表面电荷量随着污泥组成形态的变化电负性逐渐增加,80　d后稳定在-0.42～-0.80　meq·g^-1之间.污泥表面电荷的负电性增加主要是由小于0.45　mm的污泥造成的,其中小于0.18　mm的絮状污泥对其影响最大.并且,污泥粒径越大污泥表面负电荷量越少,两者具有较好的线性关系.另外,GMBR中SVI稳定在60～90 mL/g之间,并且随着污泥表面电荷负电性的增加污泥SVI值增加,两者之间具有一定的相关性.     

超声波/零价铁协同体系作用机理探讨

在超声波/零价铁协同体系中,探讨了OH.的产生途径及其影响因素,并分析了Fe0表面形态变化。结果表明:在超声波/零价铁体系中,羟基自由基的产生途径主要有四种:声空化导致水分子热解、Fenton反应、超声波与类Fenton反应的复合效应、铁粉颗粒效应;pH值过低或过高都不利于羟基自由基产生;当铁粉投加量为2.0g/L时最有利于羟基自由基产生;超声波通过冲刷、碎裂、清洗、气蚀和熔合等多种效应,活化和增强铁粉的表面性能。     

老化的生物质炭性质变化及对菲吸持的影响

将稻壳分别在350℃和550℃热解温度下制备成生物质炭,避光条件下恒温培养300 d,通过傅里叶变换红外光谱、扫描电镜和核磁共振等技术手段及平衡吸附实验,探究生物质炭老化前后的动态结构变化及对菲吸持作用的影响.结果表明,生物质炭老化过程中氧含量增加,含氧基团增多,对菲的非线性吸附行为显著增强.热解温度的不同决定了生物质炭老化过程中性质变化的差异,350℃热解的生物质炭,老化后极性增强,芳香性减弱,而550℃热解的生物质炭,老化后脂肪族碳类物质增加,羧基减少,芳香性增强,Langmiur预测的菲在350℃热解的生物质炭上老化前后的最大吸附量分别为3.57 mg·g-1、2.35mg·g-1,主要是老化后性质变化抑制了表面吸附作用,而550℃热解的生物质炭上老化前后的最大吸附量分别为0.42mg·g-1、4.17 mg·g-1,老化后吸附量的显著增加主要是生物质炭性质变化促进了对菲的分配作用与表面吸附作用.研究生物质炭在自然环境中的老化行为对环境污染物固定的稳定性有着重要意义.     

Fe2O3 particles as superior catalysts for low temperature selective catalytic reduction of NO with NH3

Fe203 particle catalysts were experimentally studied in the low temperature selective catalytic reduction （SCR） of NO with NH3. The effects of reaction temperature, oxygen concentration, [NH3]/[NO] molar ratio and residence time on SCR activity were studied. It was found that Fe203 catalysts had high activity for the SCR of NO with NH3 in a broad temperature range of 150-270℃, and more than 95% NO conversion was obtained at 180℃ when the molar ratio [NH3]/[NO] = 1, the residence time was 0.48 seconds and 02 volume fraction was 3%. In addition, the effect of SO2 on SCR catalytic activity was also investigated at the temperature of 180℃. The results showed that deactivation of the Fe2O3 particles occurred due to the presence of SO2 and the NO conversion decreased from 99.2% to 58% in 240 min, since SO2 gradually decreased the catalytic activity of the catalysts. In addition, X-ray diffraction, Thermogravimetric analysis and Fourier transform infrared spectroscopy were used to characterize the fresh and deactivated Fe2O3 catalysts. The results showed that the deactivation caused by SO2 was due to the formation of metal sulfates and ammonium sulfates on the catalyst surface during the de-NO reaction, which could cause pore plugging and result in suppression of the catalytic activity.     

桑沟湾表层沉积物性质及对磷的吸附特征

通过研究桑沟湾表层沉积物对磷的吸附动力学曲线和吸附等温线,并结合沉积物的表面电荷性质及磷的形态分析,考察了沉积物对磷的吸附性能和吸附机制.结果表明,桑沟湾表层沉积物对磷的吸附过程包括快吸附过程和慢吸附过程,可用快慢二段一级动力学方程描述,等温线符合Langmuir交叉式模型.夏季沉积物样品的最大吸附量高于春季样品,粒级较小的沉积物吸附能力较强.沉积物样品对磷的最大吸附量Qm在0.047 1~0.123 0 mg·g-1之间,吸附/解吸平衡磷浓度(EPC0)范围在0.059 6~0.192 7 mg·L-1,沉积物充当"磷源"的作用.不同站位表层沉积物中无机磷(IP)是磷在沉积物中的主要赋存形态,吸附后的沉积物样品中弱吸附态磷(Ex-P)、铁结合态磷(Fe-P)明显增加.吸附过程包括物理吸附和化学吸附,以物理吸附为主.     

等离子体改性对活性炭纤维表面化学结构的影响

采用放电等离子体对活性炭纤维表面进行改性,通过改变活性炭纤维的化学官能团来强化活性炭纤维对SO2和NOx的吸附和催化作用。利用XPS、FTIR等方法对改性活性炭纤维的化学性质进行表征,研究了活性炭纤维表面官能团在等离子体改性过程中的转化规律和机理。实验结果表明:放电改性过程可以有效地向活性炭纤维表面引入有利于脱硫脱氮的含氧、含氮官能团;当电压为8kV,放电时间为5min时,放电改性活性炭纤维的效果最佳。     

美军C-130／A-10飞机应用PreKote表面预处理的验证试验和评价

2001年,美国奥格登空军后勤中心（OO—ALC）联合空军研究实验室（AFRL）和应用验证总司令部,开始实施PreKote验证试验和评价（QOT＆E）,同时与通常所采用的铬酸盐转化膜工艺的性能进行了对比考核试验。