Ti3C2纳米层状材料对废水中Cr（Ⅵ）的光催化去除性能

以Ti₃AlC₂为原料,采用HF刻蚀工艺制备出12种Ti₃C₂纳米层状材料,对其形貌进行了表征,并考察了以其作为光催化剂对废水中Cr（Ⅵ）的处理效果。实验结果表明：HF体积分数为80%、刻蚀时间为48 h时得到的MX-80-48的形貌较好;MX-80-48具有类似石墨烯的二维层状结构,纳米层厚度约20~50 nm,孔径2~10 nm,比表面积14.8 m²/g,在400~700 nm可见光范围内表现出强烈的吸光性;当Cr（Ⅵ）的初始质量浓度为40.00 mg/L、MX-80-48投加量为200 mg/L、pH=2、反应时间4 h（暗反应1 h+光照3 h）时,Cr（Ⅵ）去除率可达100%。     

预氧化聚丙烯腈/g-C3N4光催化降解罗丹明B

以聚丙烯腈(PAN)和g-C_3N_4为原料,采用超声波辅助分散的溶液浸渍法及煅烧法制备了具有共轭结构的预氧化聚丙烯腈/g-C_3N_4复合光催化剂(CPAN/g-C_3N_4),采用XRD、SEM、FTIR、UV-Vis DRS、EIS等技术对光催化剂进行了表征,考察了CPAN/g-C_3N_4对罗丹明B(Rh B)的可见光催化降解性能。结果表明:CPAN与g-C_3N_4具有良好的协同作用,使g-C_3N_4片状结构堆叠体颗粒显著减小,明显增强了光催化剂在全部光谱范围内的光吸收,有效提高了光生电子-空穴分离效率;在PAN与g-C_3N_4质量比为1∶200、煅烧温度250 ℃、煅烧时间1 h条件下所制备的CPAN/g-C_3N_4光催化活性最高,且具有良好的光催化活性稳定性。超氧自由基和光生空穴为CPAN/g-C_3N_4复合光催化剂光降解罗丹明B的主要活性物种。     

从6-APA和7-ADCA生产废液中回收苯乙酸

采用溶剂萃取、水法提取等方法从6-氨基青霉烷酸和7-氨基-3-去乙酰氧基头孢烷酸生产废液（简称废液）中回收苯乙酸（PAA）,考察了各种因素对回收效果的影响。实验结果表明：以甲苯为萃取剂,在萃取温度30℃、萃取时间15m in、500mL废液中萃取剂加入量130mL的最佳条件下,萃取率为96.5%;在提取温度为65℃左右、结晶温度低于10℃的条件下,PAA收率大于89%,纯度大于99%;所得PAA产品质量好,可用于青霉素G等医药产品的生产。     

黄钠铁矾渣制备透明氧化铁黄的研究

研究了以黄钠铁矾渣为原料,采用滴加法制备透明铁黄的工艺条件,讨论了亚铁浓度、温度、通气量、搅拌速度及添加剂用量等因素对铁黄制备的影响.用XRD和TEM对产品进行表征.结果表明,铁黄粒子呈针状;长轴为95～125 nm,短轴为18～25 nm;无团聚现象,单分散性好.     

活性红M-3BE脱色真菌的筛选及脱色性能研究

从自然环境中分离到2株对染料活性红M-3BE具有明显脱色效果的真菌,经形态学和26S rDNA序列分析,将其鉴定为Fusarium oxysporum和Geosmithia viridis.采用初始浓度50 mg/L M-3BE的液体培养基同步脱色培养,F.oxysporum在24 h内对M-3BE的脱色率为96%,G.viridis在36 h内的脱色率为82%.对脱色酶系的检测结果表明,脱色过程中F.oxysporum能产生LiP和MnP,G.viridis则仅产生LiP.此外,F.oxysporu和G.viridis对另外7种染料的脱色率也可分别达到16%～100%和83.3%～100%.     

用磷酸铵镁沉淀法去除沈阳老虎冲垃圾渗滤液中的氨氮

叙述了磷酸铵镁沉淀法去除垃圾渗滤液中氨氮的基本原理,分析了MAP法对氨氮的去除效果,对比了不同的镁盐及不同的反应时间对氨氮的去除效率。结果表明,MAP法对氨氮的去除效率高,产物中重金属的含量低。同时,氧化镁比氯化镁具有更好的氨氮去除综合优势。     

复合式膜生物反应器处理高浓度氨氮废水可行性试验

试验结果表明,以甲壳素为载体的复合式膜生物反应器,在进水氨氮浓度为2100mg/L,氨氮容积负荷为2.19kg/(m3.d)时,氨氮去除率接近100%,系统运行稳定。载体投加量为2.778g/L时,膜通量可维持在87%左右。     

Antioxidant responses to benzo[a]pyrene, tributyltin and their mixture in the spleen of Sebasticus marmoratus

It has been reported that there is an interaction between Benzo[a]pyrene （BaP）, a widespread carcinogenic polycyclic aromatic hydrocarbon, and tributyltin （TBT）, an organometal used as an antifouling biocide. This study was therefore designed to examine the potential in vivo influence of BaP, TBT and their mixture on splenic antioxidant defense systems of Sebastiscus marmoratus. The fish were exposed to water containing environmentally relevant concentrations of BaP, TBT and their mixture. Spleens were collected for biochemical analysis after exposure for 7, 25, 50 d and after recovery for 7, 20 d. Cotreatment with BaP and TBT for 7 d potentiated the induction of glutathione peroxidase （GPx） activity by BaP or TBT alone. The cotreatment for 25 and 50 d resulted in inhibition of GPx activity, which was similar to the effect of TBT. Splenic glutathione S-transferase （GST） activities were significantly elevated in S. marmoratus exposed to BaP starting from 7 d and remained high up to 25 d. However, no further activity change was found with prolonged exposure. Cotreatment of BaP and TBT primarily inhibited the GST activity, which was similar to the effect of TBT. Cotreatment with BaP and TBT for 25 or 50 d potentiated the depletion of GSH （glutathione） by BaP or TBT alone. MDA （malondialdehyde） contents in spleen of S. marmoratus were not significantly altered compared with the control during the test period. Spleen, as an immune organ, is sensitive to exposure of BaP or TBT. It should have an effective mechanism to counteract oxidative damage. Antioxidative defense systems in spleen of S. marmoratus should be considered as potential biomarkers. Short-term exposure of BaP or TBT could result in induction of antioxidant defense system. A significant decrease of these indices, such as GSH, GST, GPx might indicate more severe contamination.     

A study on oxidative degradation of polyacrylamide in wastewater with UV/FENTON/C4H4O62−

The degradation of polyacrylamide (PAM) in simulate wastewater was studied in UV/Fenton/C₄H₄O₆^2? system. The factors such as molecular ratio of H₂O₂/Fe²⁺/C₄H₄O₆^2?, pH, and the dosage of Fenton reagent that could affect the PAM degradation in the UV/Fenton/C₄H₄O₆^2? system were investigated. The experimental results showed that adding C₄H₄O₆^2? to UV/Fenton system could form photosensitive ferrous complexes, which led to higher degradation efficiency of PAM. The degradation rate of PAM could be up to 95.2% under the following conditions: the concentration of H₂O₂, Fe²⁺, and C₄H₄O₆^2? were 22.5, 2.25, and 2.25 mmol/L, respectively (i.e., molecular ratio of H₂O₂/Fe²⁺/C₄H₄O₆^2? was 10:1:1), the pH value was 3.0.     

不同类型填料的三维电极/Fenton试剂法处理苯酚废水

采用不同类型填料对三维电极/Fenton试剂法处理苯酚模拟废水进行研究.结果表明.不同类型活性炭填料对苯酚去除率有很大影响,粒炭不适合做粒子电极,采用5.0 mm柱炭处理效果较好;采用石英砂与活性炭混合填料的处理效果比单一活性炭填料好,但苯酚去除率提高不明显;电解槽反应器中按比例投加涂膜活性炭和活性炭混合填料能明显提高苯酚去除率;当涂膜活性炭与活性炭体积比为1,2时,苯酚去除率最高,达96.8%.