信号分子强化改性挂膜沸石持续抑制沉积物中氨氮释放

为寻找一种长期有效的底泥修复方式,对沸石进行了改性并挂膜的实验.考察了 4种铝盐[AlCl3、Al(NO3)3、Al2(SO4)3和KAl(SO4)2]改性挂膜沸石对上覆水中氨氮的去除情况.结果表明,AlCl3改性挂膜沸石效果最佳,且最佳改性浓度为0.8 mol·L-1.进一步分析添加信号分子OHHL后,AlCl3改性...     

Promoting effect of vanadium on catalytic activity of Pt/Ce–Zr–O diesel oxidation catalysts

A series of Pt–V/Ce–Zr–O diesel oxidation catalysts was prepared using the impregnation method. The catalytic activity and sulfur resistance of Pt–V/Ce–Zr–O were investigated in the presence of simulated diesel exhaust. The effect of vanadium on the structure and redox properties of the catalysts was also investigated using the Brunauer–Emmett–Teller method,X-ray diffraction, H2temperature-programmed reduction, CO temperature-programmed desorption, X-ray photoelectron spectroscopy, and Energy Dispersive Spectroscopy. Results showed that the Pt particles were well dispersed on the Ce–Zr–O carrier through the vanadium isolation effect, which significantly improved the oxidation activity toward CO and hydrocarbons. An electron-withdrawing phenomenon occurred from V to Pt, resulting in an increase in the metallic nature of platinum, which was beneficial to hydrocarbon molecular activation.     

官厅水库入库水生物接触A/O工艺低温试验研究

试验表明,生物接触A/O工艺可以在低温下稳定运行,对官厅水库入库水中NH₄⁺-N有较好的去除效果,对COD、TN均有一定的去除效果.当温度大幅下降时,在温度下降初期NH₄⁺-N去除率明显下降,但经过一段时间后,NH₄⁺-N去除率逐渐回升,并稳定在较高的去除率水平.在本试验条件下,0～5℃时,进水N₄⁺-N为10mg/L左右,NH₄⁺-N去除率最终稳定在95%以上,出水NH₄⁺-N稳定＜0.5mg/L.另外,温度变化对COD去除效果的影响不明显.镜检结果表明,在0～5℃条件下生物膜中的微生物仍具有较好的活性.     

沸石床多级生物膜焦化废水处理系统的NH_~4+-N去除稳定性研究

焦化废水处理中预处理蒸氨工艺不稳定容易引起生物处理出水NH+4-N的波动,为了在有机物去除的同时提高生物系统对NH+4-N的去除效果和稳定性,采用对NH+4-N有良好吸附性能的天然斜发沸石为生物填料构建沸石床多级生物膜系统,考察了进水负荷对系统运行稳定性的影响、抗冲击负荷能力以及系统的功能分区和污染物迁移转化规律.结果表明,当系统进水NH+4-N负荷≤0.21 kg/(m3·d)、COD负荷≤1.35 kg/(m3·d)时,出水NH+4-N和COD的平均浓度分别为(2.2±1.2)mg/L和(228±60)mg/L,平均去除率分别达(99.1±0.5)%和(86.0±2.6)%.在低、高两次NH+4-N冲击负荷[0.03 kg/(m3·d)和0.06 kg/(m3·d)]条件下,系统对NH+4-N的平均去除率仍然分别高达99.0%和92.9%,高于对比系统的96.8%和89.3%,表现出良好的抗NH+4-N冲击负荷性能与处理稳定性.系统好氧单元反应器沿程出现脱碳/硝化功能区(C/N区)和硝化功能区(N区),其中N区的NH+4-N 降解速率为C/N区的2～8倍.系统进水中相对分子质量＜1×103、 1×103～1×104、＞1×104的TOC浓度分别为227.6、104.8和35.0 mg/L,处理出水中的TOC浓度分别为31.2、 22.9和31.5 mg/L,其中相对分子质量＜1×103和1×103～1×104这2个范围的有机物降解良好,出水残余物质主要为相对分子质量＞1×103的有机物.     

低溶解氧污泥微膨胀节能方法在A/O中的试验验证

采用实际的生活污水,在A/O系统中验证了低溶解氧污泥微膨胀节能理论与方法.结果表明,A/O系统在微膨胀运行期间SVI值能稳定维持在150～230 mL/g之间,单纯低溶解氧不会造成污泥沉降性能的严重恶化.相对于高溶解氧、污泥沉降性能良好时的运行情况,微膨胀期间COD和总氮去除率略有升高,分别为86%和63%,氨氮去除率略有下降,平均为70%,且约有10%～25%的氮可通过同步硝化反硝化去除.丝状菌的网捕作用使出水的SS浓度明显减低,出水浊度低于3 NTU.维持DO=0.5 mg/L所需的理论供气量相对DO=2.0 mg/L时可节约17%,对实际的小试结果比较发现可节约57%的曝气量.     

催化湿式氧化处理造纸废水的研究

以过渡金属氧化物CuO为活性组分,采用催化湿式氧化法处理造纸废水,考察Cu负载量、催化剂用量、反应温度对废水COD去除率的影响。结果表明:固定氧气分压在2.5MPa和反应时间3h,催化剂用量为3g,Cu负载量为4%,反应温度为220℃,500mL浓度为3250mg/L造纸废水的COD去除率为90%,色度去除率为89%,pH值由9.6变为7.8。另外,对催化剂进行再生处理和稳定性测试。结果表明:450℃下活化3h,在上述相同反应条件下,对原废水的COD去除率降低为88%,重复使用9次后对废水的COD去除率仍能保持在85%左右。     

MnO2/Al2O3催化剂-微气泡臭氧体系催化降解喹啉及其机理

制备了纳米MnO₂,并以Al₂O₃为载体制备了掺杂型MnO₂/Al₂O₃颗粒催化剂.催化剂焙烧温度和时间分别为500℃和4 h、MnO₂质量分数为8%时,催化剂具有最高的臭氧催化氧化活性.SEM分析表明,纳米MnO₂均匀分布于Al₂O₃载体表面.MnO₂/Al₂O₃催化剂的比表面积（BET）为183.22 m²·g^-1,平均孔容为0.27 cm³·g^-1,平均孔径为4.87 nm.建立了MnO₂/Al₂O₃催化剂-微气泡臭氧催化反应体系,研究了该体系对喹啉的降解去除效果及其机理.臭氧微气泡的平均粒径为61.7 μm.微气泡臭氧投量为30 mg·L^-1时,反应60 min后喹啉去除率能达到95%以上;反应20 min后,MnO₂/Al₂O₃催化剂-微气泡臭氧体系对实际煤化工废水二级出水的TOC去除率可达到55%以上.以叔丁醇作为分子探针,证明了羟基自由基（·OH）氧化作用在臭氧微气泡催化氧化体系中对喹啉的降解起到主导作用.     

缙云山土地利用方式对土壤轻组及颗粒态有机碳氮的影响

选取缙云山阳坡同一海拔处亚热带常绿阔叶林(以下简称林地)、果园、坡耕地和撂荒地这4种不同土地利用类型,在0~60 cm深度内每隔10 cm采集一个土样,测定土壤轻组有机碳氮(LFOC、LFON)和颗粒态有机碳氮(POC、PON)含量,并计算其分配比例和碳氮比.结果表明,在0~60 cm土壤深度范围内,林地转变为坡耕地后,LFOC及LFON含量分别降低了71.42%和38.46%(P0.05),转变为果园后变化不明显,坡耕地撂荒后其含量分别升高了3.77倍和1.38倍(P0.05);林地转变为坡耕地或果园后,POC及PON含量均无明显变化,而坡耕地撂荒后其含量分别增加了4.12和1.25倍(P0.05).林地转变为坡耕地后土壤LFOC及LFON分配比例显著降低,转变为果园后则明显升高,而POC及PON分配比例变化均不明显;坡耕地撂荒后,LFOC、LFON、POC、PON分配比例均显著增加.土壤SOC/TN为撂荒地(12.93)林地(8.53)果园(7.52)坡耕地(4.40),LFOC/LFON为撂荒地(16.32)林地(14.29)果园(11.32)坡耕地(7.60),POC/PON为撂荒地(23.41)坡耕地(13.85)林地(10.30)果园(9.64).以上研究结果表明林地开垦为果园或坡耕地后容易导致土壤轻组有机碳氮的损失,而坡耕地撂荒则有利于土壤活性有机碳氮的积累;林地转变为坡耕地减弱了土壤有机碳氮的活性,而林地转变为果园以及坡耕地撂荒均使土壤有机碳氮活性增强;林地转变为坡耕地和果园加剧了土壤有机质的矿化,相对而言,坡耕地撂荒后有利于土壤有机质的固定.     

TiO2–PANI/Cork composite: A new floating photocatalyst for the treatment of organic pollutants under sunlight irradiation

A novel photocatalyst based on TiO_2–PANI composite supported on small pieces of cork has been reported. It was prepared by simple impregnation method of the polyaniline(PANI)–modified TiO_2 on cork. The TiO_2–PANI/Cork catalyst shows the unique feature of floating on the water surface. The as-synthesized catalyst was characterized by X-ray diffraction(XRD),scanning electron micrograph(SEM), transmission electron microscopy(TEM), thermogravimetric analysis(TGA), Fourier transform infrared spectroscopy(FT-IR), UV–vis diffuse reflectance spectra(UV–vis DRS) and the Brunauer–Emmett–Teller(BET) surface area analysis. Characterization suggested the formation of anatase highly dispersed on the cork surface. The prepared floating photocatalyst showed high efficiency for the degradation of methyl orange dye and other organic pollutants under solar irradiation and constrained conditions, i.e., no-stirring and no-oxygenation. The TiO_2–PANI/Cork floating photocatalyst can be reused for at least four consecutive times without significant decrease of the degradation efficiency.     

改性人造沸石处理含黄玉铬洁(Ⅵ张焕)祯地下水的实验研究

为了提高人造沸石对地下水中铬(Ⅵ)的去除能力,采用氯化铝对人造沸石进行改性。确定最佳改性条件:20%氯化铝溶液,液固比12 mL/g,室温下以180 r/min振荡改性8 h;最佳除Cr(Ⅵ)条件:pH值为4～8,液固比为33.3 mL/g,室温下水浴恒温振荡2 h。改性沸石对铬(Ⅵ)的吸附符合Langmuir及Freundlich等温线方程,由Langmuir吸附等温线可得其吸附容量为5.624 mg/g。在最佳反应条件下,水样中铬(Ⅵ)浓度可由5 mg/L下降到0.026 mg/L,低于0.05 mg/L,满足GB/T 14848—93《地下水环境质量标准》Ⅲ类标准。