焚烧飞灰熔融过程重金属迁移特性中试研究

通过中试试验研究垃圾焚烧飞灰熔融过程重金属Cd、Pb、Zn、Cu、Cr和Ni的迁移特性,着重研究重金属在熔渣中的固化效果,考察了温度（1 290℃、1 320℃、1 360 ℃）、助熔剂（10 %的玻璃粉）、冷却方式（水冷、空冷）对重金属固定率的影响.结果表明,温度的提高使Pb、Zn、Cu、Cr和Ni的固定率都有一定的提高;加入10%的玻璃粉使各种重金属的固定率都有显著提高,只有Zn例外;对Zn、Cu、Cr和Ni,空气冷却方式下的重金属固定率比水冷方式下的高.     

利用粉煤灰研制高效无机混凝剂聚硅酸铝

研究了以粉煤灰为原料制取高效无机混凝剂聚硅酸铝的工艺及生产条件。产品用于处理工业废水水样 ,并与传统混凝剂处理废水的效果进行了比较。结果表明 ,聚硅酸铝混凝剂用药量少 ,处理效果较好     

Effects of metal cations on sorption-desorption of p-nitrophenol onto wheat ash

The mutual e ects of metal cations (Cu2+, Pb2+, Zn2+, and Cd2+) and p-nitrophenol (NP) on their adsorption desorption behavior onto wheat ash were studied. Results suggested that Cu2+, Pb2+, and Zn2+ diminished the adsorption and increased the desorption of NP remarkably, while Cd2+ had no such e ect. In contrast, NP diminished the adsorption of Cu2+, Pb2+, and Zn2+ onto ash, however, this suppression e ect depended on the initial concentrations of metal cations. NP had no e ect on Cd2+ adsorption on ash. Fourier transform infrared (FT-IR) and X-ray absorption spectroscopic (XAS) studies suggested the following mechanisms responsible for the metal suppression e ect on NP adsorption: (1) large hydrated Cu2+, Pb2+, and Zn2+ shells occupied the surface of ash and prevent nonspecific adsorption of NP onto ash surface; (2) Cu2+, Pb2+, and Zn2+ may block the micropores of ash, resulting in decreased adsorption of NP; (3) complexation of Cu2+, Pb2+, and Zn2+ was likely via carboxyl, hydroxylic and phenolic groups of wheat ash and these same groups may also react with NP during adsorption. As a “soft acid”, Cd2+ is less e cient in the complexation of oxygencontaining acid groups than Cu2+, Pb2+, and Zn2+. Thus, Cd2+ had no e ect on the adsorption of NP on wheat ash.     

垃圾焚烧炉飞灰的低温玻璃固化初步研究

在研究我国城市生活垃圾焚烧炉飞灰的毒性特征和高温灼烧特性的基础上，试验了几种常用玻璃熔制助溶剂、烟气净化产物中的成分对飞灰的溶融温度和熔融减量的影响，以实现低温玻璃固化。实验发现受热温度越高、时间越长，飞灰减量越大；B2O3、硼砂、CaF2对飞灰助溶效果明显，而废玻璃、CaO、CaCl2能使悄灰溶融后形成的玻璃态物质地均匀、少孔。按一定比例同时加入硼砂、CaF2、废玻璃、CaO、CaCl2于飞灰中，混合物的熔融温度降到1000℃以下，大大低于飞灰自身的熔融温度（1200℃）。对该熔融物在空气中淬火形成的玻璃态物质按标准方法浸沥，选择测量了浸出液中铅、汞、镉、砷的浓度，初步发现低温玻璃态物质对重金属铅和镉具有较好的固化效果，而对汞有砷的固化效果尚不确定。     

粉煤灰多孔陶粒在水处理中的应用研究

研究采用电厂的粉煤灰为主要原料制备多孔陶粒,分别将其用作水处理中的微生物载体和吸附剂。挂膜结果表明:COD、氨氮这两项指标的出水基本稳定,去除率高。用多孔陶粒作吸附剂处理含铬废水时,等温吸附实验表明,多孔陶粒吸附水中的铬的等温方程基本符合Langmiur等温方程式,在pH值为酸性时对铬的去除率较高。用HCl和NaOH溶液再生多孔陶粒,酸的效果更好。     

垃圾焚烧飞灰熔融过程中重金属迁移分布规律的研究

垃圾焚烧飞灰处理中重金属污染一直是倍受关注的问题。采用高温熔融法处理飞,该工艺具有二恶英去除率高、高效减容、有效固化重金属、熔渣可资源化利用等优点。目前学术界针对重金属在熔融过程中的迁移分布规律,研究了温度、碱度、添加剂、气氛、熔融时间等因素对重金属分布的影响。但关于影响程度的量化及影响机制的阐述,仍需要进一步探讨。     

城市垃圾焚烧飞灰特性及水泥固化试验研究

试验分析了重庆市某城市垃圾焚烧发电厂飞灰的化学成分,研究了原飞灰的浸出毒性,考察了水泥对原飞灰和酸洗预处理飞灰中重金属的固化效果. 结果表明:飞灰中重金属Pb和Zn的浸出质量浓度均超过《危险废物浸出毒性鉴别标准》(GB5085.3-2007),因而被认为是危险废物,必须对之进行稳定化处理;酸洗预处理飞灰固化试块的抗压强度得到了一定程度的提高,其重金属Pb和Zn的浸出毒性均较相同配比、相同养护时间的原飞灰固化试块有明显降低;酸洗预处理飞灰固化试块抗压强度随掺入飞灰比例的降低和养护时间的延长而加大,在养护28 d时其抗压强度最高,达4.25 MPa;酸洗预处理飞灰固化试块在养护28 d时,其重金属Pb和Zn的浸出质量浓度分别比原飞灰所制固化试块降低了10.6%～59.0%和7.4%～73.7%.      

Solubility of ion and trace metals from stabilized sewage sludge by fly ash and alkaline mine tailing

Stabilized sewage sludge （SS） by fly ash （FA） and alkaline mine tailing as artificial soil, to be applied on the ecological rehabilitation at mining junkyards, offers a potentially viable utilization of the industrial by-product, as well as solves the shortage of soil resource in the mine area. An incubation experiment with different ratios of SS and FA was conducted to evaluate the solubility of ions and trace elements from stabilized sewage sludge. Results showed that fly ash offset a decrease in pH value of sewage sludge. The pH of （C） treatment （FA：SS = 1：1） was stable and tended to neutrality. The SO4^2- and Cl^- concentrations of the solution in the mixture were significantly decreased in the stabilized sewage sludge by alkaline fly ash and mine tailing, compared to the single SS treatment. Stabilized sewage sludge by FA weakened the nitrification of total nitrogen from SS when the proportion of FA in the mixture was more than 50%. The Cr, Ni, and Cu concentrations in the solution were gradually decreased and achieved a stable level after 22 days, for all treatments over the duration of the incubation. Moreover stabilized sewage sludge by fly ash and/or mine tailing notably decreased the trace metal solubility. The final Cr, Cu, and Ni concentrations in the solution for all mixtures of treatments were lower than 2.5, 15, and 50 μg/L, respectively.     

粉煤灰微珠负载碘氧化铋复合催化剂的光催化性能

在固体废弃物粉煤灰微珠(FACs)上负载BiOI,通过水热法制备了BiOI/FACs复合催化剂。运用XRD、SEM、EDS、UV-VisDRS等技术对复合催化剂进行了分析表征。表征结果显示:FACs为壁薄中空的球形,粒径约100μm,壁厚约为3μm;BiOI为片状,直径约2μm,颗粒团聚成球花状;球花状的BiOI负载在FACs表面;BiOI/FACs复合催化剂主要含Fe、Si、Al、Bi、I、O等元素。BiOI/FACs复合光催化剂具有较高的可见光催化活性,禁带宽度为1.74 eV。采用4 g/L的BiOI/FACs复合催化剂处理10 mg/L的亚甲基蓝溶液,在300 W氙灯照射240 min后,亚甲基蓝去除率达91%。重复使用4次亚甲基蓝去除率仍达80%。     

Possible Use of Ash Residues for the Construction of Artificial Reefs at Sea

Utilization of ash residues, including coal ash, oil ash, and municipal solid waste combustion ash, for the construction of artificial reefs at sea has been investigated by many researchers throughout the world for nearly 20 years. Both laboratory and field studies have shown that an artificial reef made of stabillized ash-concrete (SAC) has had no adverse effect on the marine environment. Indeed, published studies have shown that fish counts increase around SAC reefs owing to an abundance of colonizing organisms and to protection provided by cavities within the reef structures. However, public and regulatory resistance to the use of SAC for artificial reef construction at sea is still very strong in certain countries due to concern for possible negative environmental impacts, primarily in the area of bioaccumulation of elements or compounds originating from the ash component of SAC.

In this paper, technological feasibility of using ash residues for artificial reef construction is presented, based on the available 20 years of scientific data, including engineering workability, physical integrity, chemical leaching potential and biological effects. More important, we also identify conceptual barriers for the acceptance of using SAC for the construction of ocean reefs and suggest approaches to overcome these barriers.