石墨气体扩散电极的制备与性能优化

电极的制备工艺及参数直接影响电极材料的活性。主要考察了C/PTFE质量比、碾压压力、煅烧温度、造孔剂NH4HCO3及稀土掺杂等因素对电极产出H2O2的影响规律。研究结果表明,电极最佳制备条件为:石墨和PTFE质量比为2∶1、石墨、造孔剂和稀土元素质量比为6∶1∶1、碾压压力10 MPa、煅烧温度330℃。在pH=3、电解质Na2SO4浓度为0.05mol/L条件下,电解2 h后,改性电极产生的H2O2从95 mg/L提高到350 mg/L,提高了268.4%。     

标准石英粉尘及青石棉直接诱导8-羟基脱氧鸟苷加合物形成的研究

应用液相色谱结合电化学检测技术，研究了标准石英粉尘和青石棉体外诱导DNA分子氧化损伤产生加合物8－羟基脱氧鸟苷的形成与机制。结果表明，石英粉尘和青石棉均可致DNA分子氧化损伤并形成8－羧基脱氧鸟苷，但青石棉作用强于石英粉尘；石英粉尘的青石棉对H2O2氧化DNA的催化能力有较大差异。标准石英粉尘和青石棉，具有直接的遗传毒性；两者诱导DNA分子形成强致突变的8－羧基鸟苷可能是其潜在致癌机制之一。     

位阻胺混合甘氨酸盐溶液吸收CO2的研究

在双搅拌反应釜中研究了位阻胺2-氨基-2-甲基-1-丙醇(AMP)与甘氨酸钠(SG)混合溶液吸收CO2的性能.实验温度293~313K,混合溶液的浓度为AMP(1.5kmol/m3)+SG (0.2,0.4,0.6,0.8kmol/m3),SG浓度每增加0.2kmol/m3,200min内的平均吸收速率分别提高11.47%,10.07%,9.18%和5.33%.与AMP单一溶液相比,混合溶液在200 min时的吸收容量增加了11.5%~41.1%.在293~313K,吸收速率随温度上升而提高.使用加热的方法进行再生实验,得到1.5 kmol/m3 AMP + 0.6 kmol/m3 SG混合液的最适再生温度为378K.AMP + SG混合溶液的再生效率高于单一SG溶液及AMP + MEA/DEA混合溶液.     

活性炭纤维电极电还原产H2O2的实验研究

利用活性炭纤维作为阴极,比较了活性炭纤维电极和石墨板电极产H2O2的浓度,并对影响活性炭纤维电极产H2O2的因素(pH、电流密度和电解质浓度)进行了研究.研究发现,活性炭纤维电极电还原产生H2O2的浓度远大于石墨板电极.当实验在pH=3.00、电流密度8.89 mA/cm2和电解质(Na2SO4)浓度0.05 moL/...     

基于卫星遥感的广东地区对流层二氧化碳时空变化特征

利用瓦里关全球本底站和番禺气象局地面观测的CO2浓度资料对SCIAMACHY反演得到的对流层CO2产品进行验证.结果显示:SCIAMACHY产品能较好地反映对流层CO2的分布状况,在珠三角地区反演和观测的残差为1.29×10-6,相关系数为0.69,可用于分析区域对流层CO2的时空分布特征.利用2003~2009年SCIAMACHY观测资料分析研究显示:广东地区对流层CO2柱浓度最高值出现在春季,最低值出现在夏季,浓度年均值和年增长率分别为384.84′10-6和1.53′10-6/a,大于全球和我国同期的观测结果;粤东、粤西、粤北和珠三角地区的浓度均在春、冬季显著高于夏季、秋季 ,相同季节内各区域之间的差异不显著;粤西地区CO2柱浓度的年增长率最高,为1.82′10-6/a,珠三角和粤东地区的年增长率相当,分别为1.65,1.64′10-6/a,粤北地区的年增长率最低,为1.61′10-6/a.     

H_2O_2致大鼠RTE细胞系氧化应激作用及GSH保护作用的体外研究

许多具有氧化作用的空气污染物,均能使细胞产生氧化损伤,使胸腺基质淋巴生成素(thymic stromal lymphopoietin,TSLP)含量上升。而TSLP是一种启动过敏性炎症的重要因子,会导致哮喘等疾病发生率的上升。在本研究中用过氧化氢(H_2O_2)模拟具有氧化作用的空气污染物进行染毒,研究细胞氧化应激水平的变化,并讨论还原型谷胱甘肽(GSH)对细胞受氧化损伤的保护作用。将大鼠支气管上皮细胞(RTE)分组培养,每组设置6个平行实验,分别用低、中、高剂量H_2O_2染毒3 h;高剂量设置1个重复,作为保护组,在染毒前用GSH保护2 h。结果显示,高剂量组H_2O_2(3.2 mmol·L~(~(-1)))染毒的细胞,其细胞活力下降(P0.01),丙二醛(MDA)水平上升(P0.01),TSLP水平上升(P0.05),与之相比,用GSH保护后的同剂量染毒组,上述指标得到全面缓解(P0.01)。这表明高浓度的H_2O_2会损伤细胞活力,并使MDA及TSLP水平上升,而GSH对TSLP及MDA的升高有极显著的抑制作用,即对细胞有一定的保护作用。     

Effect of transition metal doping under reducing calcination atmosphere on photocatalytic property of TiO2 immobilized on SiO2 beads

TiO₂ immobilized on SiO₂ (TiO₂/SiO₂) have been prepared by sol-gel method and various ions of transition metals (Cr³⁺, Co²⁺, Ni²⁺, Cu²⁺, and Zn²⁺) were doped on the photocatalyst using wet impregnation method under reducing calcination atmosphere. The photocatalytic activity of metal doped TiO₂/SiO₂ towards phenol degradation under black light irradiation were investigated and compared with undoped TiO₂/SiO₂. The results showed that the photoresponse of Cu²⁺ and Zn²⁺ doped TiO₂/SiO₂ were larger than undoped TiO₂/SiO₂, indicating that the photogenerated carriers were separated more efficiently in Cu²⁺ and Zn²⁺ doped TiO₂/SiO₂. The reactivity was in the order of Cu²⁺ > Zn²⁺ > Ni²⁺ > Cr³⁺ > Co²⁺. The different photoreactivity was ascribed to combine effect of the different ionic radii and photocorrison tendency of the dopants. The sample was also characterized by surface analytical methods such as X-ray diffraction, scanning electron micrograph/electron dispersive X-ray analyzer and UV-Vis absorption spectrum.     

半干法脱除球团烟气中的SO2及Hg0

采用钙基吸收剂及复合氧化剂半干法脱除模拟球团烟气中的SO_2及Hg~0,考察了多因素条件对吸收效果的影响。实验结果表明,在以NaClO和NaClO_2为复合氧化剂、 NaClO与NaClO_2体积比1∶0.5、复合氧化剂质量分数3%、反应温度110℃、钙基吸收剂质量3.0 g、模拟烟气进气流量1.2 L/min的条件下,SO_2和Hg~0的脱除率分别为98%和93%,证明钙基吸收剂与复合氧化剂对污染物球团烟气中的SO_2和Hg~0有良好的脱除作用。     

Pd/g-C3N4对水中2,4-二氯酚的催化加氢脱氯研究

分别采用光沉积法和浸渍法制备了载钯石墨相氮化碳催化剂(Pd/g-C3N4-PD和Pd/g-C3N4-IMP),并对其进行了电感耦合等离子体发射光谱(ICP-AES)、X射线衍射(XRD)、透射电镜(TEM)和Zeta电位的表征.结果表明,不同载钯量Pd/g-C3N4-PD的等电点均在pH 2.3左右;Pd/g-C3N4-PD表面Pd粒子分散均匀,且Pd粒径小于Pd/g-C3N4-IMP.分别将Pd/g-C3N4-PD和Pd/g-C3N4-IMP用于2,4-二氯酚的催化加氢脱氯研究,Pd/g-C3N4-PD的催化脱氯效果明显优于Pd/g-C3N4-IMP.低pH值利于2,4-二氯酚的催化加氢脱氯过程,但不利于保持催化剂的稳定性.     

BiOCl/TiO_2复合材料的可见光活性及机理研究

采用水热法和溶胶凝胶法制备新型BiOCl/TiO2复合材料并明确了最优的掺杂比例(2%).随后利用X射线衍射(XRD)、紫外可见漫反射(DRS)、透射电镜(TEM)和X射线光电子能谱(XPS)对该材料进行表征.由于禁带宽度较大,纯BiOCl和TiO2的可见光催化性能极差,然而二者复合后,同条件下的苯降解率却大幅提升,可以达到40%以上.经证实,催化剂制备过程中,Bi的状态发生变化,在TiO2导、价带之间插入新的能级,使其禁带宽度变窄,电子可以实现可见光跃迁.