Application of magnetic particles modified with amino groups to adsorb copper ions in aqueous solution

A magnetic adsorbent can be easily recovered from treated water by magnetic force,without requiring further downstream treatment.In this research,amine-functionalized silica magnetite has been synthesized using N-[3-(trimethoxysilyl)propyl]-ethylenediamine(TPED) as a surface modification agent.The synthesized magnetic amine adsorbents were used to adsorb copper ions in an aqueous solution in a batch system,and the maximum adsorption was found to occur at pH 5.5 ± 0.1.The adsorption equilibrium data fitted t...     

吸附树脂负载铁酞菁催化降解硝基苯的研究

在可见光照射下,采用吸附树脂负载铁酞菁催化过氧化氢降解硝基苯.考察了光照、催化剂投加量、双氧水投加量、温度及pH值等因素对催化效果的影响.结果表明,在功率为50W卤钨灯照射下,硝基苯溶液初始质量浓度为200 mg/L,初始pH值为3,催化剂投加量为1.5 g/L,双氧水投加量为1.0 mL/L,温度为35℃下反应10h,硝基苯去除率可达到79.9％.     

Debromination of decabromodiphenyl ether by organo-montmorillonite-supported nanoscale zero-valent iron：Preparation, characterization and influence factors

An organo-montmorillonite-supported nanoscale zero-valent iron material(M-NZVI) was synthesized to degrade decabromodiphenyl ether(BDE-209). The results showed that nanoscale zero-valent iron had good dispersion on organo-montmorillonite and was present as a core-shell structure with a particle size range of nanoscale iron between 30–90 nm, characterized by XRD, SEM, TEM, XRF, ICP-AES, and XPS. The results of the degradation of BDE-209 by M-NZVI showed that the efficiency of M-NZVI in removing BDE-209 was much higher than that of NZVI. The efficiency of M-NZVI in removing BDE-209 decreased as the pH and the initial dissolved oxygen content of the reaction solution increased, but increased as the proportion of water in the reaction solution increased.     

Photocatalytic activity of Fe-doped CaTiO3 under UV-visible light

The photocatalytic degradation of methylene blue（MB） over Fe-doped CaTiO3 under UV-visible light was investigated. The as-prepared samples were characterized using X-ray diffraction（XRD）, scanning electron microscope（SEM） equipped with an energy dispersive spectrometer（EDS） system, Fourier transform infrared spectra（FT-IR）, and UV-visible diffuse reflectance spectroscopy（DRS）. The results show that the doping with Fe significantly promoted the light absorption ability of CaTiO3 in the visible light region. The Fe-doped CaTiO3 exhibited higher photocatalytic activity than CaTiO3 for the degradation of MB.However, the photocatalytic activity of the Fe-doped CaTiO3 was greatly influenced by the calcination temperature during the preparation process. The Fe-doped CaTiO3 prepared at500°C exhibited the best photocatalytic activity, with degradation of almost 100% MB（10 ppm）under UV-visible light for 180 min.     

注入式低温等离子体技术用于卷烟厂异味处理的效果研究

将注入式低温等离子体技术应用于烟厂制丝排潮和制丝除尘排放气体异味处理中,研究了注入式低温等离子体发生器参数对臭味浓度、非甲烷总烃和可检出典型有机物去除率的影响规律。结果表明:注入式低温等离子体发生器工作电压越高,注入处理烟道的氧化活性物种浓度越高,注入量越大,臭味浓度、非甲烷总烃和可检出典型有机物去除率也越高。选取合理的工作电压,臭味浓度去除率可达90%以上,非甲烷总烃去除率分别达到了83.8%(制丝排潮)和78.1%(制丝除尘)。     

聚硅酸铝铁/羧基壳聚糖复合絮凝剂处理硫化黑染料废水的研究

用聚硅酸铝铁/羧基壳聚糖复合絮凝剂对硫化黑染料废水进行了处理,研究了影响絮凝剂处理硫化黑染料废水的影响因素。结果表明,较佳的条件为转速50 r/min、聚硅酸铝铁和羧基壳聚糖的质量配比为3、废水pH值为9.0、絮凝剂用量为60 mg/L。在该条件下,复合絮凝剂对硫化黑染料废水的COD、色度、浊度去除率分别为92.1%,88.6%,96.3%。     

钒钛磁铁矿尾矿锰、铁元素浸出规律研究

以攀西地区钒钛磁铁矿尾矿为研究对象,通过设置浸出实验,从酸类、p H、温度、反应时间4个方面探讨尾矿中Mn、Fe元素的迁出规律。结果表明,Mn在草酸中的浸出浓度远大于在醋酸和盐酸中的浸出浓度。随着p H的增大,Mn的浸出浓度整体呈减小趋势,有机酸做浸提剂时,Mn的浸出浓度在p H=2或3时达到最大值;无机酸做浸提剂时,Mn的浸出浓度在p H=1时达到最大值。Fe在草酸中的浸出浓度大于在醋酸和盐酸中的浸出浓度,随着p H增大,Fe的浸出浓度逐渐减小并趋于稳定。另外,温度升高、反应时间延长都有利于Mn、Fe从尾矿中浸出。各变量对Mn、Fe浸出的影响效果为p H酸类温度反应时间。本研究可以对尾矿浸出液的安全使用提供初步指导。     

构筑安全科学的光荣与梦想——访中国安全生产科学研究院院长刘铁民

人们依然记得4年多前的那一天：2005年1月18日,在国务院领导的关心支持和国家安监总局的不懈努力下。经中央机构编制委员会办公室批准,中国安全生产科学研究院（以下简称安科院）正式挂牌成立。 时代的列车隆隆驶过,人们普遍认为,安科院的成立,像是一次不失时机的搭乘。时光飞逝,4年多的时间里,在科技兴安战略的指引下,安科院的发展取得了长足进步,当然,也依然面临着前所未有的机遇与挑战。为此,我们走访了安科院院长刘铁民。     

聚合氯化铝铁絮凝剂的制备及其在焦化废水深度处理中的应用

以铝酸钙粉和硫酸亚铁为主要原料,通过酸溶、氧化、聚合和熟化过程制备了无机高分子絮凝剂聚合氯化铝铁,采用正交试验优选出制备聚合氯化铝铁的最佳条件,联合使用聚合氯化铝铁与氧化剂深度处理焦化废水.结果表明,聚合氯化铝铁的最佳制备条件为:硫酸亚铁投加量10 g(以每100 g铝酸钙粉计,下同)、盐酸投加量400 mL、反应温度80℃、反应时间2.5 h;在此条件下制得的絮凝剂氧化铝质量分数为30.5%,全铁质量分数为1.2%.当聚合氯化铝铁投加量为200 mg/L、氧化剂投加量为10 mg/L时,焦化废水中COD去除率可达70%,色度去除率可达63%,出水水质达到<污水综合排放标准>(GB 8978-1996)中的一级排放标准.     

铁改性海泡石除锑的影响因素研究

选择廉价海泡石, 用氯化铁对其改性。研究铁改性海泡石对锑的吸附特性。结果表明,氯化铁浓度、吸附时间、初始锑浓度以及温度等因素对锑的吸附影响较大,溶液初始pH影响不明显。在初始锑浓度50 mg/L,pH 6.8,5%氯化铁改性海泡石投加量为2 g/L,吸附90 min, 温度35℃下,吸附量可达21.6 mg/g。海泡石对吸附锑具有缓冲特性,溶液的初始pH值在3.1～10.1范围时,吸附后溶液的最终pH值为8～8.5。IMS吸附锑是放热过程。改性后海泡石比表面积增大,表面羟基数量增加,导致其吸附能力增强。通过XRD谱图并未发现铁晶体的存在。