海绵城市用多孔泡沫玻璃的制备与性能研究

以多孔材料作为基材的分散式小规模海绵设施应用广泛。为了在保证不产生二次污染的前提下不断提高材料自身的孔隙率、强度和吸水释水能力,以适应更多的应用场景,对多孔泡沫玻璃进行了改性研究。以废玻璃粉为主要原材料,加入一定量的发泡剂、改性剂等,在500～950℃的烧制温度下,制备了可用于海绵城市蓄排水的开孔泡沫玻璃,并对其微观结构和物理性能进行表征。结果表明：开孔泡沫玻璃呈现大量致密的不规则开孔结构,孔道彼此连通,孔径在0.1～5 mm,孔隙率达93%;抗压强度可达2.3 MPa,可应用于对抗压强度要求较高的场景;通过控制原材料可保证重金属污染物含量极低,对水体不造成污染;具有很强的吸水能力和良好的缓释效果,饱和吸水率可达95%,释水8 h后,质量吸水率减小至30%;用于地下封闭环境时,需要考虑排气设计和抗浮设计。该研究为海绵城市雨水蓄排提供了一种新型环保基材,有利于泡沫玻璃在海绵设施中推广应用。     

某铀尾矿库区周围稻田土壤不同组分对U(Ⅵ)的吸附性能分析

通过斯笃克定律提取土壤胶体,连续提取法吸附土壤中的有机质,得到土壤矿质胶体,采用比表面积(BET)法和Zeta电位对原土、土壤胶体和矿质胶体进行了表征分析,考察了溶液p H、接触时间、U(Ⅵ)初始浓度以及温度等因素对3种样品吸附溶液中U(Ⅵ)的影响性能。结果表明:原土、土壤胶体和矿质胶体的比表面积和平均孔径分别为11. 5,31. 1,28. 8 m2/g和18. 76,35. 55,17. 5 nm。在p H为5. 5,固液比在1. 0 g/L,温度为20℃,U(Ⅵ)初始浓度为10. 0 mg/L,土壤、土壤胶体反应时间为50 min,矿质胶体反应时间为40 min时,原土、土壤胶体、矿质胶体的对U(Ⅵ)吸附率分别达到76. 67%、83. 03%、48. 87%,吸附容量分别达到8. 53,9. 24,5. 43 mg/g。对比研究结果可以看出,土壤中的胶体对溶液中U(Ⅵ)有着明显的吸附能力,该研究结果对进一步研究含U(Ⅵ)废水的处理及U(Ⅵ)在土壤和地下水中的迁移过程有一定的参考意义。     

H-ZSM-5分子筛吸附-氧化NOx的研究

针对湿法脱硫后船舶尾气特点,考察了3种不同硅铝比的H-ZSM-5分子筛对船舶脱硫后尾气中NO_x的吸附-氧化过程及其影响因素,并采用TPD研究了干气下不同硅铝比的分子筛吸附饱和后的脱附情况.结果表明:干气条件下,硅铝比低的分子筛具有较好的吸附效果;硅铝比高的分子筛具有较好的抗水性,但从干气到饱和湿度下,硅铝比为300的分子筛的NO氧化率从36%降至18%;干气下,低温有利于分子筛的吸附-氧化;分子筛用量增加能够增加其对NO_x的吸附效果和氧化效果.TPD结果表明:NO和NO2共吸附在分子筛上,3种分子筛中脱附出的NO_x中NO2均占脱附总量的80%以上,但在600℃时,NO_x在分子筛上脱附仍不完全.     

Ti-MCM-41的微波水热法合成、表征及其催化氧化性质研究

本研究利用微波水热法合成Ti-MCM-41,并采用XRD、FTIR、BET、XPS及TEM等技术对材料进行表征.同时,使用甲基橙溶液作为光催化氧化的对象,对光催化剂的氧化性能进行考察.实验结果表明:利用微波水热法合成Ti-MCM-41,可将合成时间缩短至3 h,能够大大缩减反应时间并节省能源.通过在MCM-41多孔结构中掺杂钛,可明显提高其光催化活性.在酸性溶液中,Ti-MCM-41的催化氧化效率较高.XRD、FTIR、BET、XPS及TEM等表征结果表明,钛成功地掺入到了MCM-41中,并未破坏其多孔有序的结构,Ti-MCM-41同时兼具介孔材料的高比表面积和二氧化钛的光催化性能,有利于在环境污染修复上的应用.     

从节能角度探讨填料型A~2O工艺的参数优化

文章对碳纤维填料型A2O工艺在不同内回流比和溶解氧(DO)条件下对生活污水的处理效果进行了研究,考察了不同条件下生活污水中常规指标的去除效果。研究结果表明,在水力停留时间(HRT)为18 h,其中厌氧4.5 h,缺氧4.5 h及好氧9 h的条件下,在不同内回流比的对比实验中,内回流比为200%时去除效果最好,不同DO浓度对比实验中,DO浓度为2.5 mg/L时去除效果最好。从节能角度考虑,DO浓度为2 mg/L时,A2O工艺出水有小幅度升高,但仍满足《城镇污水处理厂污染物排放标准》(GB18918-2002)中的一级A排放标准。实验表明碳纤维填料型A2O工艺内回流比为200%,DO浓度为2 mg/L时既满足出水水质要求,又达到节能降耗的目的。     

Heterogeneous Fenton-like degradation of 4-chlorophenol using iron/ordered mesoporous carbon catalyst

Ordered mesoporous carbon supported iron catalysts(Fe/OMC) were prepared by the incipient wetness impregnation method and investigated in Fenton-like degradation of 4-chlorophenol(4CP) in this work. XRD and TEM characterization showed that the iron oxides were well dispersed on the OMC support and grew bigger with the increasing calcination temperature. The catalyst prepared with a lower calcination temperature showed higher decomposition efficiency towards 4CP and H2O2, but more metals were leached. The effect of different operational parameters such as initial pH, H2O2 dosage, and reaction temperature on the catalytic activity was evaluated. The results showed that 96.1% of 4CP and 47.4% of TOC was removed after 270 min at 30°C, initial pH of 3 and 6.6 mmol/L H2O2. 88% of 4CP removal efficiency was retained after three successive runs, indicating Fe/OMC a stable catalyst for Fenton reaction. 4CP was degraded predominately by the attack of hydroxyl radical formed on the catalyst surface and in the bulk solution due to iron leaching. Based on the degradation intermediates detected by high performance liquid chromatography, possible oxidation pathways were proposed during the 4CP degradation.     

透析对施氏矿物微观结构及其砷吸附能力的影响

探讨透析对施氏矿物微观结构和砷吸附能力的调控,对高效合成施氏矿物,进而将其应用于含砷地下水处理具有重要意义.本研究在利用FeCl_3·6H_2O与Na_2SO_4合成施氏矿物的基础上,用截留分子量100000 Da和20000 Da透析袋分别对施氏矿物透析10 d与20 d,探究了透析过程对施氏矿物产生量、比表面积、孔体积、平均孔径等矿物特征的影响,并考察了透析前后施氏矿物对废水中砷的吸附去除效果.研究结果表明,透析过程可显著提高矿物的合成量,增加矿物比表面积及孔体积,增加矿物的平均孔径.施氏矿物在截留分子量100000 Da与20000 Da透析袋中透析20 d,矿物产生量分别增加70.70%与79.84%;比表面积分别增加68.75%与45.85%;其中微孔(2 nm)比表面积增加439.90%与395.11%,中孔(2～50 nm)比表面积增加30.63%与9.96%;孔体积分别增加332.79%与287.25%,其中微孔体积增加491.61%与419.92%,中孔体积增加了220.36%与211.95%,透析后矿物平均孔径增长了214.77%与244.31%;矿物对污水中砷的吸附去除能力提高65.60%与64.74%.本研究结果可为化学合成施氏矿物改性并将其应用于地下水除砷领域提供必要的参数支撑.     

应用多导流筒气升式环流生物反应器处理化肥工业含氨废水

在天津××化工厂建立了一套反应器有效体积为80m3的低高径比、多导流筒气升式环流生物反应器处理化肥工业含氨废水的装置。针对影响生物硝化效果的影响因素气液比、水力停留时间进行了考察,得到了操作的优化条件气液比为50∶1,水力停留时间为5h。在此条件下,该装置对废水中的COD_(Cr)和NH4+-N的去除率分别在75%和98%以上,出水中COD_(Cr)<50mg/L,NH4+-N<10mg/L。     

大孔树脂对邻苯二甲酸的吸附研究

研究了XDA-200大孔树脂对水溶液中邻苯二甲酸的吸附。结果表明XDA-200树脂对水溶液中的邻苯二甲酸吸附速度很快，30min内基本达到平衡，其后达到完全平衡的吸附进程非常缓慢。树脂对邻苯二甲酸的吸附量随质量浓度增加而增加。pH值降低，有利于邻苯二甲酸在溶液中以分子态存在，易于树脂吸附。邻苯二甲酸的吸附均满足Freundlich和Langmiur等温吸附方程。泄漏点与进水浓度和流速均有很大关系。