预处理垃圾焚烧飞灰作为碱胶凝材料混合材的研究

试验分析了垃圾焚烧飞灰的主要化学成分及矿物组成,探讨了预处理垃圾焚烧飞灰作为碱胶凝材料混合材的可能性.研究表明,垃圾焚烧飞灰主要由黏土类矿物组成,飞灰直接作为混合材参与水化过程会产生明显膨胀现象,加入30%(质量分数)飞灰制成的矿渣/飞灰试块在成型1 d脱膜时膨胀率达到15.7%,标准养护28 d后无侧压抗压强度只有12.4 MPa.对飞灰进行热活化预处理,900℃条件下活化效果最佳,同样的飞灰掺量下,试块在标准养护28 d后无侧压抗压强度达到46.0 MPa,膨胀现象消失,且碱胶凝材料中重金属稳定性良好.     

城市垃圾焚烧飞灰中重金属的形态及酸浸出性研究

研究了城市垃圾焚烧飞灰中重金属形态在不同粒径上的分布,以及HNO3对飞灰中重金属的浸出性.结果表明:飞灰中重金属主要以残渣态存在,可交换离子态含量很少;易挥发性的重金属在较大粒径上有较高分布,亲石性重金属Cr和Ni的分布与粒径的相关性不大,在各粒径上的分布较均匀;飞灰中以碳酸盐结合态存在的重金属对酸不稳定,易被HNO3浸出,而残渣态部分对酸较稳定,不易被HNO3浸出.     

Management of mine spoil for crop productivity with lignite fly ash and biological amendments

Long-term field trials using lignite fly ash (LFA) were carried out in rice crops during the period 1996-2000 at Mine I, Neyveli Lignite Corporation, Tamil Nadu. LFA, being alkaline and endowed with an excellent pozzolanic nature, silt loam texture, and plant nutrients, has the potential to improve the texture, fertility, and crop productivity of mine spoil. The rice crops were the first, third, fifth, and sixth crops in rotation. The other crops, such as green gram (second) and sun hemp (fourth), were grown as green manure. For experimental trials, LFA was applied at various dosages (0, 5, 10, 20, 50, 100, and 200 t/ha), with and without press mud (10 t/ha), before cultivation of the first crop. Repeat applications of LFA were made at the same dosages in treatments of up to 50 t/ha (with and without press mud) before cultivation of the third and fifth crops. Press mud, a lightweight organic waste product from the sugar industry, was used as an organic amendment and source of plant nutrients. Also, a recommended dosage of chemical fertilizer, along with gypsum, humic acid, and biofertilizer as supplementing agents, was applied in all the treatments, including control. With one-time and repeat applications of LFA, from 5 to 20 t/ha (with and without press mud), the crop yield (grain and straw) increased significantly (p < 0.05), in the range from 3.0 to 42.0% over the corresponding control. The maximum yield was obtained with repeat applications of 20 t/ha of LFA with press mud in the third crop. The press mud enhanced the yield in the range of 1.5-10.2% with various dosages of LFA. The optimum dosage of LFA was 20 t/ha for both one-time and repeat applications. Repeat applications of LFA at lower dosages of up to 20 t/ha were more effective in increasing the yield than the corresponding one-time applications of up to 20 t/ha and repeat applications at 50 t/ha. One-time and repeat applications of LFA of up to 20 t/ha (with and without press mud), apart from increasing the yield, evinced improvement in the texture and fertility of mine spoil and the nutrient content of crop produce. Furthermore, some increase in the content of trace and heavy metals and the level of gamma-emitters in the mine spoil and crop produce was observed, but well within the permissible limits. The residual effect of LFA on succeeding crops was also encouraging in terms of eco-friendliness. Beyond 20 t/ha of LFA, the crop yield decreased significantly (p < 0.05), as a result of the formation of hardpan in the mine spoil and possibly the higher concentration of soluble salts in the LFA. However, the adverse effects of soluble salts were annulled progressively during the cultivation of succeeding crops. A plausible mechanism for the improved fertility of mine spoil and the carryover or uptake of toxic trace and heavy metals and gamma-emitters in mine spoil and crop produce is also discussed.     

生活垃圾焚烧飞灰在饰面砖中资源化应用技术

分析了飞灰的性质,利用飞灰、红泥及缸砂研制饰面砖,研究了飞灰对饰面砖性能及微观结构的影响,并对其安全性进行了评价。结果表明:飞灰主要化学成分是CaO、SiO2、Al2O3,构成SiO2-Al22O3-金属氧化物体系,可用作饰面砖的原材料;当飞灰掺加量为20%时,饰面砖表现出良好的性能:抗压强度19·2MPa,吸水率7·2%,表观质量达到一等品要求;与飞灰相比,饰面砖中重金属浸出能力大大降低:As、Pb、Ni、Cr、Cu、Hg、Cd水平振荡浸出毒性未检测出,Zn的水平振荡浸出值下降到飞灰中的0·014倍,Hg、Cd有效浸出毒性未检测出,As、Pb、Ni、Cr、Cu、Zn的有效浸出毒性分别下降到飞灰中的0·056、0·001、0·067、0·058、0·056、0·029倍。     

粉煤灰沸石分子筛负载氧化铈催化剂的制备及其催化燃烧二氯甲烷性能

以发电厂粉煤灰为原料,采用碱融水热法合成了HZSM-5分子筛(FHZSM-5),用浸渍法负载10％(w)CeO2制备了CeO2/FHZSM-5催化剂,用于二氯甲烷的催化燃烧.盐酸浓度为2 mol/L及粉煤灰和NaOH的质量比为1:1.2时制备的FHZSM-5纯度最高,结晶度最好,用其制备的CeO2/FHZSM-5催化剂...     

Utilization of MSWI fly ash as partial cement or sand substitute with focus on cementing efficiency and health risk assessment

• Washed MSWI fly ash was used as partial cement or sand substitute. • Sand replacing is beneficial for strength, while cement replacement reduces strength. • Cementing efficiency factor and mortar pore structure explain the strength results. • Health risk assessment was conducted for MSWI fly ash blended cement mortar. • CR and HI contributed by different exposures and heavy metals were analyzed. The strength of cement substituted mortar decreases with the increase in fly ash amount, whereas the strength increases when the fly ash is blended as sand substitute. A mortar with highest strength (compressive strength= 30.2 Mpa; flexural strength= 7.0 Mpa) was obtained when the sand replacement ratio was 0.75%. The k value (cementing efficiency) of fly ash varied between 0.36 and 0.15 for the fly ash fraction in binder between 5% and 25%. The k values of fly ash used for sand replacement were all significantly above that used for cement substitution. The macropores assigned to the gaps between particles decreased when the fly ash was used as sand replacement, providing an explanation for the strength enhancement. The waste-extraction procedure (toxicity-sulphuric acid and nitric acid method (HJ/T 299-2007)) was used to evaluate metal leaching, indicating the reuse possibility of fly ash blended mortar. For the mortar with the mass ratio of fly ash to binder of 0.5%, the carcinogenic risks (CR) and non-carcinogenic hazard quotient (HQ) in sensitive scenario for blended mortar utilization were 9.66 × 10^-7 and 0.06, respectively; these results were both lower than the threshold values, showing an acceptable health risk. The CR (9.89 × 10^-5) and HQ (3.89) of the non-sensitive scenario for fly ash treatment exceeded the acceptable threshold values, indicating health risks to onsite workers. The main contributor to the carcinogenic and non-carcinogenic risk is Cr and Cd, respectively. The CR and HQ from inhalation was the main route of heavy metal exposure.     

基于响应曲面法优化烧结烟气脱硫灰改性工艺

采用BOX-Behnken的中心组合实验设计及响应面分析方法对半干法烧结烟气脱硫灰进行改性研究,得到脱硫灰转化率的预测模型。结果表明:通过该预测模型可以很好地描述脱硫灰的转化率与反应温度、反应时间和气固比等重要操作参数之间的关系,R2=0.9903。因素分析表明,反应温度对脱硫灰的转化率影响最大,同时反应温度和气固比的交互作用与反应温度和时间的交互作用对脱硫灰的转化率的影响作用相同。利用得到的改进预测模型可以计算脱硫灰的转化率。     

浅析XLDM型脉冲袋式除尘器在CFB锅炉上的应用

介绍了兖矿国宏化工公司2台160 t/h CFB锅炉配套XLDM-5700型袋式除尘器的实际运行情况,从除尘效率、喷吹方式、运行能耗等方面分析了袋式除尘器的性能,并总结出XLDM型袋式除尘器最佳运行方式。     

循环流化床锅炉燃煤技术热电厂生命周期评价

运用生命周期评价方法,应用Gabi5.0软件对采用循环流化床锅炉燃煤技术的热电企业进行资源耗竭和环境影响分析,计算各生产单元生命周期清单的全球变暖潜值、酸化效应潜值、富营养化潜值、非生物资源耗竭潜值、人体毒性潜值以及光化学烟雾和臭氧生成潜值等主要环境影响类型,对燃煤发电过程进行生命周期评价。结果表明,全球变暖和非生物资源耗竭为发电运行过程中主要的环境影响因素,分别占53%和15.05%;锅炉燃烧阶段的环境影响最重,占整个生命周期影响值的77.12%,并且除生物耗竭潜值外的其他5项指标均为发电运行阶段各个单元中最高。采用SNCR脱硝技术减少燃烧过程中NOx的排放量,并对该技术方案进行生命周期评价,比较方案实施前后的环境影响。     

1000 MW燃煤机组电除尘深度节能技术研究及应用

电除尘设备在减少工业粉尘排放量、降低大气环境污染、保护生态环境等方面有着重要的作用,随着我国对节能减排工作的重视及环保要求的提高,保证其安全、稳定、经济、节能运行成为火电厂环保工作重点。对北仓电厂三期2×1000 MW机组电除尘电场供电方式优化、电除尘振打方式优化、电除尘闭环控制技术、电除尘高频电源技术、电除尘灰斗、瓷套蒸汽加热技术组合集成应用进行了研究,在确保除尘效率达到要求的情况下,降低运行电耗。相关的电除尘深度节能技术成果在国内同类型设备中具有一定的借鉴意义。