Behaviour of Dioxins,Furans and Metals Associated with Stabilized Msw Combustor Ash in Sea Water

This report presents the results of a research programme designed to examine the engineering and environmental acceptability of stabilizing municipal solid waste (MSW) combustor ash for artificial reef construction. Municipal solid waste combustor ash was combined with Portland cement to form solid blocks using conventional construction block making technology. the resultant stabilized combustor ash (SCA) blocks were used to construct an artificial habitat in Conscience Bay, Long Island Sound, New York and compared to identical concrete blocks, fabricated using natural aggregates. Over a 4.5 year period divers periodically returned to the site to monitor the interaction of SCA blocks with the marine environment and compare the performance of these blocks with the concrete control blocks. Results show that the SCA blocks retain their strength after prolonged sea water exposure. Contaminants of environmental concern, including metals, dioxins and furans, were retained within the cementitious matrix of the SCA blocks after prolonged sea water submersion. in addition, organisms growing on the surfaces of the SCA blocks did not accumulate contaminants from the blocks.     

含砷废物资源化产品中砷的浸出特性与环境风险分析

分别以我国某地2种含砷废物(污泥和废渣)为研究对象,用EA NEN 7371实验方法分析其不同资源化产品(烧制砖、免烧砖和含砷水泥等)中As的有效量浸出特性,从环境风险的角度探讨了含砷废物资源化利用的可行性. 结果显示:含砷污泥进行烧砖处置后,其产品中As的有效量浸出率从15%左右升至60%～70%;含砷废渣与水泥进行混合粉磨共处置后,含砷水泥产品中As的有效量浸出率从60%～70%降至4%以下;含砷废渣制成免烧砖后,As的有效量浸出率从60%～70%降至10%左右. 表明含砷污泥不宜进行烧砖处置;而含砷废渣可根据含砷量,在控制掺加比例的条件下与水泥熟料共处置生产混合水泥或作为原材料生产免烧砖.      

浸取方式对废物水泥窑共处置产品中Pb,Cd和Ni浸出的影响

模拟煅烧试验制取含Pb,Cd和Ni的水泥熟料,并将其制成混凝土样品,通过水槽浸出试验研究间歇浸取方式对混凝土中Pb,Cd和Ni释放的影响. 结果表明:间歇碳化保存处理浸出液的pH为9.5～10.4,低于连续浸取处理浸出液的pH(10.3～11.0),而间歇自然保存处理的浸出液pH则与连续浸取处理浸出液的pH相近;间歇浸取过程的碳酸化作用增加了混凝土中Pb和Cd的释放,表现为间歇浸取碳化保存处理的累积浸出量最大(Pb和Cd分别为686和332 mg/m2),连续浸取处理的累积浸出量最低(Pb和Cd分别为480和203 mg/m2);间歇处理对Ni的释放影响与Pb和Cd的不同,连续浸取处理的累积浸出量最大,为155 mg/m2,而间歇碳化保存处理的累积浸出量(85 mg/m2)最小.      

钒钛磁铁矿制备絮凝剂用于有机污水处理的研究

以钒钛磁铁矿为原料,利用盐酸浸出工艺制备铁、钛、钒三元絮凝剂,对工艺条件进行优化后用于处理模拟有机污水,并与聚合氯化铁(PFC)的絮凝效果进行对比.结果表明:在浸出时间为4 h、浸出温度为80℃、液固质量比为5、盐酸初始质量分数为20％时,浸出效果最佳,钒、铁、钛的浸出率分别为99.98％、97.77％、10.41％;...     

高效絮凝剂制备的前期浸取研究

我国油田多采用絮凝剂处理含油污水。为得到高效、廉价的絮凝剂,使用赤泥最优化制备聚合氯化铝铁。通过化学分析法和X射线衍射分析,得出赤泥中铝﹑铁元素含量。正交实验结果表明:影响Fe溶出的因素由强到弱依次为盐酸用量系数﹑反应温度﹑目数和反应时间,最佳浸出条件为目数80～120、液固比5.5、反应温度95℃、反应时间3.5h。     

废旧阴极射线管(CRT)显示器玻壳中铅浸出特性研究

CRT显示器玻壳中含有大量的铅,废旧CRT显示器玻壳被列为危险废物。采用4种浸提方法(水平振荡法(GB5086.2-1997)、翻转法(GB5086.1-1997)、硫酸硝酸法(HJ/T299-2007)、醋酸缓冲溶液法(HJ/T300-2007))研究CRT显示器玻壳中铅的浸出特性。同时探讨浸提液pH和pH缓冲能力、振荡方式、CRT玻壳颗粒粒径、液固比、浸提时间对CRT玻壳颗粒中的Pb浸出的影响。结果表明:上述4种方法浸提液中Pb的平均浓度分别为0.07、0.69、1.64、11.33 mg/L。随着醋酸缓冲液初始pH值从4.0升高到7.0,其浸提的Pb的含量呈现出逐渐下降的趋势。而去离子水的pH值低于5时,其浸提的Pb的含量才明显升高。Visual MINTEQ模型计算结果表明:在去离子水和硫酸硝酸混合液浸提过程中,主要以酸碱反应为主;而在醋酸缓冲液浸提过程中,以酸碱反应和络合反应为主。前3种浸提方法使用的浸提液类似于天然水环境或降水,其浸提的Pb浓度高于地下水环境质量III标准。第4种浸提方法模拟垃圾填埋场环境,其浸提的Pb的浓度高于工业固废最高容许浸出浓度。因此,废旧CRT玻壳无论填埋处置或直接进入土...     

锌冶炼废渣重金属在地块土壤中的垂向迁移特征及归趋

为探讨冶炼废渣中重金属对土壤及地下水的影响,开展了90 d持续和间歇淋溶下锌挥发窑渣浸出液中重金属在场地剖面土柱的迁移模拟实验,分析淋出液Cd、 Cu、 Pb和Zn浓度及其在土壤剖面的累积、赋存形态和粒径分布特征,并探讨重金属在土壤剖面滞留机制.结果表明,土柱淋出液重金属浓度在淋溶初期达到峰值后迅速降低,Cd浓度超过《地下水环境质量标准》(GB/T 14848-2017)Ⅳ类水质限值(0.1 mg·L^-1),地下水存在Cd污染风险.剖面土壤对废渣中重金属固持量大,Cd、 Cu、 Pb和Zn主要累积在浅层土壤(0～10 cm),分别为淋溶前土壤的237～429、 1.25～16.2、 1.38～2.31和1.79～3.17倍;持续淋溶下废渣重金属较间歇淋溶的迁移距离较长,Cd在土柱深层有明显累积.土壤粗颗粒(0.5～2.0 mm)对Cd、 Cu和Zn累积总量的贡献率较大,而Pb更易累积在<0.25 mm粒径.BCR顺序提取结果显示,浅层土壤累积的Cd、 Cu和Zn主要以弱酸提取态为主,占比分别高达62.4%～76.7%、 72.0%～95.8%和67.6%～8...     

Combination of ion exchange system and biological reactors for simultaneous removal of ammonia and organics

A novel process for a simultaneous removal of ammonia and organics was developed on the basis of ion exchange and biological reactions. From batch experiments, it was found out that NH₄⁺ could be removed effectively by combining cation exchange and biological nitrification showing 0.98 mg N/m²?s of a maximum flux. On the other hand, the removal of NO₃⁻ was 3.5 times faster than NH₄⁺ and the maximum flux was calculated to be 3.4 mg N/m²?s. The systems for NH₄⁺ and NO₃⁻ removal were combined for establishing the IEBR process. When the process was operated in a continuous mode, approximately 95.8% of NH₄⁺ was removed showing an average flux of 0.22 mg N/m²·s. The removal efficiency of total nitrogen was calculated as 94.5% whereas that of organics was 99.5%. It was concluded that the IEBR process would be effectively used for a simultaneous removal of NH₄⁺ and organics.     

不同农作物秸秆原料制备生物炭特性及重金属浸出行为

采用水稻秆、大豆秆、小麦秆和玉米秆为原料在550℃缺氧条件下制备生物炭,考察不同原料生物炭理化性质及热解后重金属(Cr﹑Ni、 Cu﹑As﹑Cd和Pb)迁移转化特征,及其在不同浸出液中的浸出行为.结果表明,4种原料制备的生物炭的理化特性和元素组成基本一致,其中玉米秆生物炭微孔体积(0.006 cm³·g^-1)和比表面积(110.120 m²·g^-1)低于其他原料生物炭.秸秆热解后重金属(除Cd外)含量增加了14.04%～410.81%,且大部分重金属(除Cd和Pb外)化学形态由不稳定态(弱酸提取态和可还原态)向稳定态(可氧化态和残渣态)转化.制备的生物炭中的重金属在超纯水和缓冲盐溶液中无浸出或浸出量较少,在乙酸溶液和腐殖酸溶液中浸出量较高.其中Cu在乙酸溶液中浸出量较高,为2.601～4.224 mg·kg^-1,As在腐殖酸溶液中浸出量较高,介于0.074～0.166 mg·kg^-1.热解后,各种重金属的环境质量指数(PI_i)和内梅罗...     

废物水泥窑共处置产品中重金属的释放特性

选用欧盟固体中无机组分有效量测试方法(EA NEN7371)和块状材料中无机组分的扩散实验方法(EA NEN7375),研究了模拟混凝土样品中重金属(Cr、Ni、As、Cd和Pb)的释放特性.结果表明,混凝土中重金属的有效释放量低于总量;不同重金属的有效释放量与总量比值差异较大.扩散控制是混凝土中Cr、Ni和Cd释放的主要机理,释放曲线与斜率为0.5的直线拟合较佳,且不同区间浸出量曲线的斜率均在0.35~0.65范围内;As在释放前期有延滞现象,但中后期仍以扩散控制为主;Pb的释放为溶解控制,受浸取液的pH值影响较大.重金属扩散系数负对数值按Pb相似文献