以湖北省某化工企业含砷废水处理过程中产生的含硫化砷废渣为研究对象,采用氧化碱浸—沉淀工艺制备砷酸铜。考察了沉淀反应液pH、沉淀反应温度、搅拌转速对砷沉淀效果的影响。采用XRD和SEM技术对砷酸铜的物相及形貌进行了表征。实验结果表明：废渣在氧化碱浸过程的砷浸出率为96.53%;沉淀反应时间为30 min时,沉淀步骤的最佳工艺条件为沉淀反应液pH 5.0、搅拌转速500 r/min、沉淀反应温度50 ℃。验证实验结果表明,在该工艺条件下,砷沉淀率均达93.96%以上。SEM表征结果显示,砷酸铜产品为颗粒状,粒径约为500 nm。XRD表征结果显示,砷酸铜产品中主要含有Cu₃As₂O₈,Cu₄O（AsO₄）₂,Cu₄（As₂O₇）O₂。该方法工艺简单、无二次污染,为废渣的综合利用提供了一种新的技术路线。     

锰矿浸渣中水溶性锰的回收

采用水洗—生石灰沉淀法回收锰矿浸渣中的水溶性锰,考察了液固比、水洗时间对锰矿浸渣中水溶性锰洗出率（洗出液与锰矿浸渣中水溶性锰的质量比）的影响,并探讨了n（生石灰）∶n（水溶性锰）、聚丙烯酰胺絮凝剂加入量、反应温度和反应时间对洗出液中水溶性锰回收率（沉淀与洗出液中锰的质量比）的影响。实验结果表明：水洗工段,在去离子水体积（mL）与锰矿浸渣质量（g）比为5∶1、水洗时间5 min的条件下,水溶性锰洗出率达到92%;生石灰沉淀工段,n（生石灰）∶n（水溶性锰）对水溶性锰回收率的影响最大,其次为反应温度、絮凝剂加入量和反应时间,在n（生石灰）∶n（水溶性锰）=1.8、絮凝剂加入量0.2 mg/L、常温、反应时间10 min的条件下,水溶性锰回收率达90%以上;锰矿浸渣中水溶性锰的总回收率达83%以上。     

铅冶炼烟尘的物性分析及浸出性研究

采用XRF、XRD、激光粒度分析、DTA-TG、FTIR以及SEM-EDS等技术,对某铅冶炼厂烟尘（简称烟尘）进行了物性分析,并采用稀硫酸对烟尘进行了浸出性研究。分析结果表明：烟尘所含主要元素为Pb,Zn,Cd,Cl,S,As;烟尘是氧化物、硫酸盐、硅酸盐、硫化物和砷化物等物质的混合物,主要物相为ZnO,PbO,PbSO₄,CdO,CdS;烟尘颗粒大小不一,形状各异,多呈相互黏结或包裹状。实验结果表明：在ρ（硫酸）=120 g/L、浸出时间30 min、液固比（稀硫酸体积（mL）与烟尘质量（g）之比）20∶1、浸出温度60 ℃的条件下,Pb,Zn,Cd,As,Cl的浸出率分别达到0.16%,98.95%,49.36%,89.12%,99.31%。     

机械活化对CRT锥玻璃浸出动力学的影响

通过研究CRT锥玻璃经机械活化后在硝酸溶液体系中浸出反应动力学规律,考察了机械球磨转速、浸出温度以及硝酸初始浓度对锥玻璃中铅的浸出效果影响。研究结果表明,锥玻璃经机械活化预处理后,反应活性显著增强,锥玻璃中铅浸出率大幅度提高。浸出反应的表观活化能和反应级数由109.4 kJ/mol和0.79降至54.3 kJ/mol和0.51。     

重金属污染土壤的草酸和EDTA混合淋洗研究

采用不同浓度的草酸(oxalic acid,OX)和乙二胺四乙酸(EDTA)混合的淋洗方法研究重金属污染土壤的最佳混合淋洗方式,探讨了液固比、淋洗时间及pH对淋洗效果的影响,并分析了0.2 mol/L OX+0.2 mol/L EDTA处理前后土壤中重金属形态的变化。结果表明,采用0.2 mol/L OX+0.2 mol/L EDTA混合的淋洗法可同时去除多种重金属,且对Cu、Zn、Ni和Cr的去除率明显高于单用OX和EDTA,去除率分别为Cu 41.29%、Zn 84.73%、Ni 54.2%和Cr 66.01%。0.2mol/L OX+0.2 mol/L EDTA在液固比为5∶1、淋洗时间为4 h、pH为6时可分别达到最佳淋洗效果,且分别为Cu 62.59%、Zn 93.48%、Ni 55.95%和Cr 71.57%;Cu 50.47%、Zn 86.67%、Ni 61.53%和Cr 72.68%;Cu 44.40%、Zn 81.82%、Ni68.76%和Cr 74.93%。形态分析结果表明,0.2 mol/L OX+0.2 mol/L EDTA能较好地改变土壤中重金属形态的分布。     

铁镁质尾矿中的钙镁浸取效果优化

铁镁质尾矿含有丰富的钙镁,利用浸取剂可以促进铁镁质尾矿中钙镁的释放,使这些尾矿成为固定CO2的材料。尾矿中钙镁的浸出率大小跟多个因素相关,如何寻求浸取钙镁的最优化条件,是有效利用铁镁质尾矿的重要内容。考虑环境友好的方案,采用EDTA、柠檬酸和柠檬酸钠浸取尾矿中的钙镁,并对比了不同条件下的浸取效果。通过比较,显示柠檬酸钠的浸取效果较好,在此基础上利用响应面法对粒度、pH值、固液比等主要影响因子进行优化处理。当反应液的pH=1,尾矿粒度<75μm,固液比为2.6∶100时,模型预测实验尾矿淋滤的Mg2+浓度为143.4 mg/L,Mg达到最佳溶出率2.03%。实验模型的预测精度良好,表明响应面法适用于尾矿的浸取实验优化。     

Sugarcane straw management and soil attributes on alachlor and diuron sorption in highly weathered tropical soils

This research evaluated the effects of the new sugarcane harvesting system (without straw burning) and soil attributes on the organic carbon (OC) accumulation and sorption of alachlor (2-chloro-N-(2,6-diethylphenyl)-N-(methoxymethyl)acetamide) and diuron (3-(3,4-dichlorophenyl)-1,1-dimethylurea) in highly weathered Brazilian soils. Alachlor was more likely to leach (K _d,app = 1.0–7.0 L kg^?1 and mean K _oc,app = 174 L kg^?1) than diuron (K _d,app = 6.2–116.3 L kg^?1 and mean K _oc,app = 1789 L kg^?1). The sorption coefficient (K _d,app) values correlated better with soil OC contents, but the Fe-oxides also played an important role in these highly weathered soils. Sorption was enhanced in the areas without straw burning mostly due to OC accumulation that was higher in the clayey soils, but it was not enough to change their mobility classification.     

Distribution of organophosphate insecticides in a Thai biomass-water system

Sorption and leaching of the organophosphate (OP) pesticides chlorpyrifos, profenofos, methyl parathion and malathion were investigated with four different types of biomass: coconut husk, rice husk, peat moss and peanut shell. Organic carbon contents of the biomass were in the range of 35.4–45.4%. Sorption studies were carried out by the batch (equilibrium) method at 4 different OP spike concentrations and at pH 3–7. Sorption isotherms conformed to a linear Freundlich equation and the Freundlich constant or sorption coefficient (K_D) confirmed that biomass organic carbon content was the principal sorbent factor affecting OP sorption. For a given sorbent, correlation of the extent of sorption with sorbate chemical properties was examined. Column leaching experiments involving different masses of coconut husk and peanut shell pre-spiked with OPs at the level equivalent to actual spraying concentrations in some Thai tangerine orchards were conducted. These experiments included repeated spikings and leaching. A water flow rate of 20 mL min^?1 was employed corresponding to the current average watering regime. Retardation and biodegradation with these sorbents were also examined.     

Differential sorption of herbicides as related to soil topography and organic matter 1

Abstract

The sorption of bromacil and simazine by the surface soil (0–15 cm) sampled at various positions along an 8% slope citrus grove (Candler fine sand; Typic Quartzipsamment) and at various depths (0–200 cm) at upper, middle, and lower positions along the slope were investigated. The sorption of both herbicides by the top 15 cm soil decreased considerably from the upper to mid position along the slope and increased at the lower position. The organic matter content and concentrations of Ca, Mg, K, P, and Cu in the soil showed evidence of transport of organic matter and mineral nutrients from the mid position on the slope and accumulation in the lower position. The differential sorption of herbicides by the soil samples taken at various positions along the slope was closely related to changes in organic matter content. Although sorption of bromacil and simazine varied considerably at various positions along the slope, the sorption of bromacil was very similar at depths below 30 cm regardless of positions along the slope. In the case of simazine, however, the sorption was much greater at all depths in the lower than in the upper and mid position of the slope. The sorption of both herbicides decreased considerably at depths below 30 cm at all positions along the slope, thus, indicating the potential for rapid leaching of the herbicides down the soil profile.     

电镀污泥回收重金属的新工艺

合理、经济地处理混合电镀污泥,回收其中有价值的金属具有重要意义。以不同的酸作为浸出剂对电镀污泥中的金属进行了浸出效果实验。结果表明,在相同条件下,各酸的浸出效果顺序为:硫酸>盐酸>王水>硝酸;液体水与固体电镀污泥比为3,干污泥为5 g,硫酸加入量为15 mL,时间1 h条件下,混合电镀污泥中金属铜锌的浸出率最大,达到97.38%。分别采用铁和铁锰合金还原剂常温还原低熔点重金属离子铜、锌,浸出液中99%以上含量的铜、锌沉淀,使低熔点重金属与黑色金属铁、锰、铬有效分离。低熔点混合重金属可以用来做铜合金添加剂使用,最后沉淀的混合黑色金属氢氧化物处理后可以用来做炼钢合金添加剂使用。