聚硅酸氯化铝铁絮凝剂制备及絮凝效果的研究

以粉煤灰和硫铁矿烧渣两种工业固体废弃物为主要原料,制取聚硅酸氯化铝铁(PSAFC)无机高分子絮凝剂。粉煤灰、硫铁矿烧渣和纯碱按1：1：0．8混合．在800～900(焙烧15～30min,用定量1：1盐酸浸取,固体溶出率高达94％,陈化后即为PSAFC絮凝剂。通过模拟和真实印染废水絮凝试验．表明PSAFC絮凝效果与聚合氯化铝(PAC)相当,在沉降速度、污泥体积等方面要优于PAC,且成本比PAC低．具有较大的市场前景。     

Al3+对序批式生物膜反应器(SBBR)中污泥脱氢酶活性(DHA)和胞外聚合物(EPS)的影响

通过向序批式生物膜反应器(SBBR)中投加氯化铝,研究了化学协同生物除磷过程中Al~(3+)对污泥脱氢酶活性(DHA)、胞外聚合物(EPS)及系统处理效果的影响.结果表明,氯化铝投加量少于0.1 mmol·L~(-1)时,Al~(3+)对微生物的活性有促进作用,多于0.1 mmol·L~(-1)的Al~(3+)对其活性有明显的抑制作用.氯化铝投加量少于0.1 mmol·L~(-1)时,Al~(3+)能够促进EPS中多糖(PS)和蛋白质(PN)的分泌,多于0.1 mmol·L~(-1)的Al~(3+)则只促进多糖的分泌,但对EPS的分泌总量没有影响.Al~(3+)会使污泥的SVI值显著降低,大大改善其沉降性能.MLSS、MLVSS基本上是随着Al~(3+)投加量的增加而增大,MLVSS/MLSS随着投药量的增加先减小后增大再减小.Al~(3+)对COD和TN的去除具有轻微抑制作用,但对TP的去除具有显著的改善作用.当Al~(3+)的投加为0.5 mmol·L~(-1)时,TP的去除效果最好,出水浓度仅为0.44 mg·L~(-1),满足一级A排放标准.此时,TP的去除率为92.7%,比不加药时提升了10.2%.     

钛盐混凝剂调理对活性污泥絮体理化性质的影响作用机制

研究了预制的不同形态钛盐混凝剂对污泥的调理效果,结果表明不同碱化度[B值,即n(OH)/n(Ti)]聚合氯化钛(PTC)单一调理污泥时,在相同投加量时,PTC_(0.5)调理后污泥比阻、可压缩性以及EPS中有机物含量均低于其他形态钛盐,其最佳投加量以TSS计,为0.005 g·g~(-1),该投加量远低于传统的铁盐和铝盐混凝剂.不同B值PTC调理污泥脱水能力的强弱顺序为:PTC_(0.5)PTC_(1.5)Ti Cl_4PTC_(2.5).同时分析了调理过程中污泥絮体粒径(d_(0.5))和分形维数(D_F)的变化特征.采用三维荧光光谱和高效体积排阻色谱,解析了钛盐混凝剂对污泥胞外聚合物(EPS)分布和组成的影响,EPS蛋白峰的荧光强度和有机物相对分子质量峰分布变化规律与污泥比阻、可压缩性和脱水能力变化规律有一定相关性.     

城市生活垃圾焚烧飞灰中钾盐浸出研究

通过物理化学表征手段和多因素水浸试验对城市生活垃圾焚烧飞灰的性质和飞灰中钾盐浸出规律进行研究.结果表明,飞灰的主要成分为CaO、KCl和NaCl,平均粒径为12.599μm,水洗后的飞灰颗粒粒径会变大,而比表面积变小.粒径范围0.037~0.075 mm飞灰中的金属元素含量对飞灰金属总量贡献率全部在60%左右.浸出过程中,在pH=12的条件下,搅拌强度为400 r·min~(-1),浸出温度为90℃,采用液固质量比为5∶1能使氯化钾的浸出率达到90%以上.浸出液中含有大量的可溶性氯化钾表明飞灰中的钾盐可以通过水洗、过滤、纯化、分布结晶的方式收,氯化钾晶体纯度可达到90%.     

CTAC改性活性炭去除水中砷(V)的柱实验吸附和再生研究

为了开发一种能有效去除水中砷的吸附材料, 研究了十六烷基三甲基氯化铵(CTAC)改性活性炭后, 活性炭对水中五价砷As(V)的去除效果.研究中利用动态小柱实验(Rapid small-scale column test, RSSCT)探讨了CTAC改性后活性炭对砷的吸附能力、影响吸附能力的因素和活性炭再生方法.结果表明, CTAC改性能有效提高活性炭对As(V)的吸附.活性炭对As(V)的吸附受溶液pH、空床接触时间、进水中砷浓度及水中其他离子存在的影响.另外, 1 mol·L^-1的盐酸能有效对吸附穿透后的活性炭进行再生,再生后的活性炭可以重复使用.同时,柱实验中对出水CTAC的检测结果表明, CTAC和活性炭的结合非常稳定.     

Preparation of high concentration polyaluminum chloride by chemical synthesis-membrane distillation method with self-made hollow fiber membrane

A method of direct contact membrane distillation (DCMD) with a self-made hollow polyvinylidene fluoride membrane was applied to prepare high concentration polyaluminum chloride (PACl) with high Al_b content based on chemical synthesis. The permeate flux and Al species distribution were investigated. The experimental results showed that the permeate flux decreased from 14 to 6 kg/(m²·hr) at the end of the DCMD process, which can be mainly attributed to the formation of NaCl deposits on the membrane surface. The Al_b content decreased slightly, only from 86.3% to 84.4%, when the DCMD experiment finished, correspondingly the Al_c content increased slightly from 7.2% to 8.5%, and the Al_a content remained at 7% during the whole DCMD process. A PACl with Al_b content of 84% at total aluminum concentration 2.2 mol/L was successfully prepared by the chemical synthesis-DCMD method.     

PSAF-DMDAAC复合絮凝剂的制备及含铊废水的处理

将自制聚硅酸铝铁（PSAF）与二甲基二烯丙基氯化铵（DMDAAC）复配,制备了复合高分子絮凝剂PSAF-DMDAAC,并将其用于含铊废水的处理。表征结果显示：PSAF与DMDAAC先利用氢键形成聚合体后脱水,然后DMDAAC链上的烯基双键与PSAF中的聚铁、聚铝基团发生桥联反应,以配位键形式将基团引入DMDAAC链,形成一种新型复合絮凝剂。实验结果表明：复合絮凝剂制备的最优条件为（Al+Fe）与Si的摩尔比2∶1、Al与Fe的摩尔比1∶2、60%（w）DMDAAC溶液加入量0.8%（w）;废水处理的最优条件为絮凝剂投加量0.8 g/L、废水pH 9.5、沉降时间10 min;在上述优化条件下,废水的色度、浊度、铊的去除率分别达到95.0%,96.4%,95.6%,处理后废水的色度、浊度、铊质量浓度分别为10度、6 NTU、13 μg/L。     

间接原子吸收法测定水中氯化物研究

本工作以Ｃｌ＾－与过量Ａｇ＾＋生成ＡｇＣｌ沉淀反应为基础，较详细地探讨了各种强电解质作为絮凝剂对ＡｇＣｌ沉淀的影响，确定了反应的条件，从而提出了一个测定水中Ｃｌ＾－的是接原子吸收法，Ｃｌ＾－浓度在０－５０μｇ／１０ｍｌ范围呈线性，用建立的方法测定自来水中Ｃｌ＾－，再现性与准确度俱佳，用本法测定废水中Ｃｌ＾－的结果与经典的比浊法，和离子色谱法的结果相符。     

采集方法对氯化物沉积速率测试结果的影响

空气中氯化物的沉降速率是环境因素法评估大气腐蚀严酷度的一个重要因素,ISO9223标准规定的测试方法是使用湿烛法采集空气中的氯化物,而我国目前采用的方法是挂片法。文中同时使用湿烛法和挂片法采集万宁试验站近海暴露场大气中的氯化物并计算其沉积速率,每月采集一次,每次采集时间为1个月,连续采集11次,对这两种方法的测试结果是否一致进行了研究。研究表明：当显著水平为0．01时,湿烛法和挂片法具有明显的差异,挂片法确定的氯离子沉积速率等级可能要比湿烛法所确定的高一级。     

利用废旧电子元件粉末/PVC制备复合材料

利用电子废弃物中非金属材料/聚氯乙烯(PVC)制备复合材料,考察了流变仪温度、转速.液压机压力、温度、废旧电子元件目数等对复合材料力学性能的影响.结果表明,废旧电子元件粉末添加量为70%时,目数为120目,流变仪加工温度为205 ℃,转速为45 r/min,液压机液压温度为185 ℃,压力为15 MPa时,制得复合材料...