Cadmium removal mechanistic comparison of three Fe-based nanomaterials: Water-chemistry and roles of Fe dissolution

● nZVI, S-nZVI, and nFeS were systematically compared for Cd(II) removal. ● Cd(II) removal by nZVI involved coprecipitation, complexation, and reduction. ● The predominant reaction for Cd(II) removal by S-nZVI and nFeS was replacement. ● A simple pseudo-second-order kinetic can adequately fit Fe(II) dissolution. Cadmium (Cd) is a common toxic heavy metal in the environment. Taking Cd(II) as a target contaminant, we systematically compared the performances of three Fe-based nanomaterials (nano zero valent iron, nZVI; sulfidated nZVI, S-nZVI; and nano FeS, nFeS) for Cd immobilization under anaerobic conditions. Effects of nanomaterials doses, initial pH, co-existing ions, and humic acid (HA) were examined. Under identical conditions, at varied doses or initial pH, Cd(II) removal by three materials followed the order of S-nZVI > nFeS > nZVI. At pH 6, the Cd(II) removal within 24 hours for S-nZVI, nFeS, and nZVI (dose of 20 mg/L) were 93.50%, 89.12% and 4.10%, respectively. The fast initial reaction rate of nZVI did not lead to a high removal capacity. The Cd removal was slightly impacted or even improved with co-existing ions (at 50 mg/L or 200 mg/L) or HA (at 2 mg/L or 20 mg/L). Characterization results revealed that nZVI immobilized Cd through coprecipitation, surface complexation, and reduction, whereas the mechanisms for sulfidated materials involved replacement, coprecipitation, and surface complexation, with replacement as the predominant reaction. A strong linear correlation between Cd(II) removal and Fe(II) dissolution was observed, and we proposed a novel pseudo-second-order kinetic model to simulate Fe(II) dissolution.     

Simplified creation of polyester fabric supported Fe-based MOFs by an industrialized dyeing process: Conditions optimization, photocatalytics activity and polyvinyl alcohol removal

MIL-53(Fe) was successfully prepared and deposited on the surface carboxylated polyester (PET) fiber by an optimized conventional solvothermal or industrialized high temperature pressure exhaustion (HTPE) process to develop a PET fiber supported MIL-53(Fe) photocatalyst ([email protected]) for the degradation of polyvinyl alcohol (PVA) in water under light emitting diode (LED) visible irradiation. On the basis of several characterizations, [email protected] was tested for the photocalytic ability and degradation mechanism. It was found that temperature elevation significantly enhanced the formation and deposition of MIL-53(Fe) with better photocatalytic activity. However, higher temperature than 130°C was not in favor of its photocatalytic activity. Increasing the number of surface carboxyl groups of the modified PET fiber could cause a liner improvement in MIL-53(Fe) loading content and photocatalytic ability. High visible irradiation intensity also dramatically increased photocatalytic ability and PVA degradation efficiency of [email protected] Na₂S₂O₈ was used to replace H₂O₂ as electron acceptor for further promoting PVA degradation in this system. [email protected] prepared by HTPE process showed higher MIL-53(Fe) loading content and slightly lower PVA degradation efficiency than that prepared by solvothermal process at the same conditions. These findings provided a practical strategy for the large-scale production of the supported MIL-53(Fe) as a photocatalyst in the future.