铁改性海泡石除锑的影响因素研究

选择廉价海泡石, 用氯化铁对其改性。研究铁改性海泡石对锑的吸附特性。结果表明,氯化铁浓度、吸附时间、初始锑浓度以及温度等因素对锑的吸附影响较大,溶液初始pH影响不明显。在初始锑浓度50 mg/L,pH 6.8,5%氯化铁改性海泡石投加量为2 g/L,吸附90 min, 温度35℃下,吸附量可达21.6 mg/g。海泡石对吸附锑具有缓冲特性,溶液的初始pH值在3.1～10.1范围时,吸附后溶液的最终pH值为8～8.5。IMS吸附锑是放热过程。改性后海泡石比表面积增大,表面羟基数量增加,导致其吸附能力增强。通过XRD谱图并未发现铁晶体的存在。     

土壤中零价铁还原3-氯硝基苯的作用

利用零价铁在常温常压下对土壤中的3-氯硝基苯的还原,对反应物和产物随时间的变化及反应的各个影响因素进行了研究。实验结果表明,零价铁能够有效地将3-氯硝基苯还原为3-氯苯胺,反应过程中没有检测到脱氯产物。其反应速率随铁粉用量、反应体系含水量的增加以及反应温度的升高而升高,随土壤初始pH值的升高而降低。在土壤中3-氯硝基苯含量约为2.5×10^-6 mol/g,铁粉使用量为25 mg/g,反应体系中含水量为0.75 mL/g,pH值为6.8时,在恒温生化培养箱(25±1)℃反应5 h后,3-氯硝基苯的还原率达到92.75％。     

废钢铁切割加工烟尘的治理

介绍了氧-乙炔火焰切割加工废钢铁产生的烟尘治理系统的设计和系统设备选型,重点介绍了烟尘捕集罩的设计和除尘器、电磁脉冲阀、风机的选型和PLC自动控制以及系统实际运行效果,为废钢铁加工企业治理污染提供一套简单、经济、实用的除尘系统作参考.     

A comparison of the low frequency electrical signatures of iron oxide versus calcite precipitation in granular zero valent iron columns

Geophysical methods have been proposed as technologies for non-invasively monitoring geochemical alteration in permeable reactive barriers (PRBs). We conducted column experiments to investigate the effect of mineralogy on the electrical signatures resulting from iron corrosion and mineral precipitation in Fe0 columns using (a) Na2SO4, and (b) NaHCO3 plus CaCl2 mixture, solutions. At the influent interface where the reactions were most severe, a contrasting time-lapse electrical response was observed between the two columns. Solid phase analysis confirmed the formation of corrosion halos and increased mineralogical complexity in the corroded sections of the columns compared to the minimal/non-corroded sections. We attribute the contrasting time-lapse signatures to the differences in the electrical properties of the mineral phases formed within the two columns. While newly precipitated/transformed polarizable and semi-conductive iron oxides (mostly magnetite and green rust) increase the polarization and conductivity of the sulfate column, the decrease of both parameters in the bicarbonate column is attributed to the precipitation of non-polarizable and non-conductive calcite. Our results show that precipitate mineralogy is an important factor influencing the electrical properties of the corroded iron cores and must be considered if electrical geophysical methods are to be developed to monitor PRB barrier corrosion processes in situ.     

EDTA-2Na/Fe(Ⅱ)对自养生物体系下硝酸盐还原过程的影响

采用厌氧序批式生物膜反应器(ASBBR),以固定浓度的硝酸盐和硫酸亚铁为基质,按不同梯度条件添加EDTA-2Na,进行长时间的培养驯化,研究铁盐脱氮的启动过程,同时探究不同EDTA-2Na/Fe(Ⅱ)对铁自养反硝化过程以及硝酸盐异化还原为铵(DNRA)的影响.结果表明:经过65d的培养驯化,反应器成功稳定运行.当EDTA-2Na/Fe(Ⅱ)<1.50时,反应器只进行铁自养反硝化过程,NO₃^--N去除率最高仅为71.70%;当EDTA-2Na/Fe(Ⅱ)≥1.50时,反应器同时进行铁自养反硝化与DNRA过程,NO₃^--N去除率最高为99.70%.值得注意的是,在EDTA-2Na/Fe(Ⅱ)=1.50时,铁自养反硝化速率达到最大值1.63mg/(L·h)的同时,DNRA的产氨量也达到最大值9.75mg/L.Visual MINTEQ模拟结果表明:EDTA-2Na与Fe(Ⅱ)的摩尔比会影响进水中EDTA-2Na与Fe(Ⅱ)的存在形态,物质的量比越大,FeEDTA^2-度越高,Fe...     

钢铁企业大型低位料仓汽车卸料的粉尘控制

某钢企大型低位料仓为汽车卸料,料仓厂房内空高,跨度大,料仓上部贯通,物料落差大,卸料中产生大量粉尘,环境污染问题典型突出。通过对低位料仓汽车卸料产尘特性分析,采取加强生产管理、组织汽车有序卸料、料仓厂房有效密闭、合理设计捕尘方式和布袋除尘系统等措施,能够有效地控制粉尘污染。除尘系统具有投资及运行费用少,除尘效果明显的优点。     

不同粒径零价铁（ZVI）对污水污泥H_2S和CH_4释放速率的影响

考察了不同粒径零价铁（ZVI）,包括200目普通铁粉（200m-ZVI）、800目超细铁粉（800m-ZVI）和纳米铁粉（nZVI,粒径=20 nm）,对污水污泥的硫化氢和甲烷释放速率的影响。研究发现：（1）在22 d内,添加0.1%的200m-ZVI使污泥的硫化氢释放速率提高48.0%,而添加0.1%的800-ZVI和nZVI,则使污泥的硫化氢释放速率分别降低33.1%和77.1%;（2）不同粒径ZVI均可以提高污泥沼气中的甲烷浓度,且依次为nZVI〉800m-ZVI〉200m-ZVI;（3）在23 d内,添加0.1%的200m-ZVI和nZVI使污泥的甲烷累计产生量分别提高了15.5%和40.6%,而添加0.1%800m-ZVI则使甲烷产生量降低了12.5%。nZVI可以有效控制污泥的硫化氢释放,并显著提升污泥在厌氧发酵过程的产甲烷速率。     

Immobilization of non-point phosphorus using stabilized magnetite nanoparticles with enhanced transportability and reactivity in soils

Laboratory batch and column experiments were conducted to investigate the immobilization of phosphorus (P) in soils using synthetic magnetite nanoparticles stabilized with sodium carboxymethyl cellulose (CMC-NP). Although CMC-stabilized magnetite particles were at the nanoscale, phosphorus removal by the nanoparticles was less than that of microparticles (MP) without the stabilizer due to the reduced P reactivity caused by the coating. The P reactivity of CMC-NP was effectively recovered when cellulase was added to degrade the coating. For subsurface non-point P pollution control for a water pond, it is possible to inject CMC-NP to form an enclosed protection wall in the surrounding soils. Non-stabilized “nanomagnetite” could not pass through the soil column under gravity because it quickly agglomerated into microparticles. The immobilized P was 30% in the control soil column, 33% when treated by non-stabilized MP, 45% when treated by CMC-NP, and 73% when treated by both CMC-NP and cellulase.     

铁炭复配修复地下水中NO_3~--N的条件研究

采用了铁炭复配修复地下水中NO3--N,探讨了实验条件对修复效果的影响。结果表明,在pH值近中性条件(初始pH 6.42)下,反应时间为1 h时NO3--N修复率达到60.85%;Fe/C=1∶1时介质最佳用量分别为4~5 g;Fe/C=1/1.5时修复率为72.80%;反应速率在高振荡强度下大于低振荡强度;氧化铜的催化效果最好,可使修复率提高7.5个百分点。铁炭复配介质修复地下水中NO3--N是有效可行的,修复率随反应时间的增加而提高,在Fe/C=1∶1时修复率与介质用量呈正相关,无限减小Fe/C比并不能无限提高修复率,振荡强度对修复具有显著影响,低振荡强度下的修复过程较高强度存在滞后现象,并非所有金属氧化物催化剂对铁炭修复NO3--N均有促进作用。     

Impact of nano-CuO stress on rice (Oryza sativa L.) seedlings

Indiscriminate release of metal oxide nanoparticles (NPs) into the environment due to anthropogenic activities has become a serious threat to the ecological system including plants. The present study assesses the toxicity of nano-CuO on rice (Oryza sativa cv. Swarna) seedlings. Three different levels of stress (0.5 mM, 1.0 mM and 1.5 mM suspensions of copper II oxide, <50 nm particle size) were imposed and seedling growth performance was studied along control at 7 and 14 d of experiment. Modulation of ascorbate–glutathione cycle, membrane damage, in vivo ROS detection, foliar H₂O₂ and proline accumulation under nano-CuO stress were investigated in detail to get an overview of nano-stress response of rice. Seed germination percentage was significantly reduced under stress. Higher uptake of Evans blue by nano-CuO stressed roots over control indicates loss of root cells viability. Presence of dark blue and deep brown spots on leaves evident after histochemical staining with NBT and DAB respectively indicate severe oxidative burst under nano-copper stress. APX activity was found to be significantly increased in 1.0 and 1.5 mM CuO treatments. Nevertheless, elevated APX activity might be insufficient to scavenge all H₂O₂ produced in excess under nano-CuO stress. That may be the reason why stressed leaves accumulated significantly higher H₂O₂ instead of having enhanced APX activity. In addition, increased GR activity coupled with isolated increase in GSH/GSSG ratio does not seem to prevent cells from oxidative damages, as evident from higher MDA level in leaves of nano-CuO stressed seedlings over control. Enhanced proline accumulation also does not give much protection against nano-CuO stress. Decline in carotenoids level might be another determining factor of meager performance of rice seedlings in combating nano-CuO stress induced oxidative damages.