燃煤锅炉烟气汞污染控制技术浅析

燃煤锅炉烟气是最大的人为汞排放源。通过对燃煤锅炉烟气汞分布及脱汞技术的分析,提出利用现有的烟气污染控制设备以提高汞的脱除效率,走复合式污染控制之路是目前我国经济技术上可行的选择。     

碳纳米管负载TiO2对1,2,4-三氯苯的光降解研究

碳纳米管负载TiO2复合光催化剂与纳米TiO2光催化剂对1,2,4-三氯苯的光催化降解效果,及降解动力学的研究结果表明,复合光催化剂比纳米TiO2有更好的光催化降解效果,经254 nm紫外光辐照60 min后,使用复合光催化剂的1,2,4-三氯苯降解了70%,而使用纳米TiO2为催化剂的1,2,4-三氯苯仅降解了51%...     

Effects of different mixing ratios on emissions from passenger cars fueled with methanol/gasoline blends

The effects of different mixing ratios of methanol/gasoline blends and new three-way catalytic converter on regulated and unregulated emissions, especially VOC and carbonyl compound emissions were investigated.     

O3/TiO2催化氧化工艺对饮用水中AOC的影响

以陶粒、硅胶和沸石为载体,分别负载二氧化钛（TiO₂）进行臭氧催化氧化去除硝基苯的实验,并对饮用水中生物可同化有机碳（AOC）所代表的小分子有机物(酮、醛、醇和羧酸类物质)的生成情况进行了研究.发现臭氧催化氧化比单纯的臭氧氧化能更彻底地将部分大分子有机物氧化成小分子中间产物,陶粒、硅胶和沸石负载TiO₂ 3种催化剂分别将AOC从大约300　μg·L^-1增加到 674.1　μg·L^-1、847.2　μg·L^-1和882.1　μg·L^-1,并且分别使AOC/TOC从原水的4.68%升高到30.5%、33.21%和46.04%,大大地提高了水中有机物的可生物降解性.如果增加臭氧投量,催化氧化可使小分子有机物部分被氧化,致使水样AOC又略有回降.在这一过程中,AOC-NOX所代表的羧酸类物质急剧增加,达到总AOC的90％以上,取代AOC-P17成为了AOC的主体组成部分.     

低温条件下Nano-MnOx上NH3选择性催化还原NO

采用流变相法制备了无载体Nano-MnO_x催化剂,在低温条件下(50～150℃)以NH₃为还原剂系统考察了氮氧化物的选择催化还原特性.结果表明,流变相法制备的Nano-MnO_x催化剂具有良好的低温催化活性.实验条件下,80℃即可获得98.25%的NO转化率,100～150℃内NO几乎完全转化;SO₂和H₂Ｏ会与NO和NH₃在催化剂表面产生竞争吸附,导致催化活性下降,但该影响是可逆的.经分析,较大的比表面积和较低的晶化度是Nano-MnO_x具有良好低温活性的2个主要原因.     

凹凸棒土复合催化剂的制备及对零价汞催化氧化性能的影响

以天然的凹凸棒土(ATP)为原料,通过溶胶凝胶法(Sol-gel)、水热法、离子液体熔盐法与不同金属化合物(Fe2O3,Ce O2,Fe VO4,Ce VO4)复合制备催化剂。结果表明,Sol-gel、离子液体熔盐法制得的催化剂对Hg0的催化氧化效果较好,尤以Ce化合物改性ATP催化效果更佳。     

负载型膨胀石墨催化剂低温催化氧化NO研究

膨胀石墨(EG)具有四级孔结构,是一种优良的吸附剂和催化剂载体.采用超声浸渍法制备了Mn/EG催化剂,用于低温催化氧化NO,考察了金属负载量、进口NO质量浓度及O2体积分数对NO氧化效率的影响.结果表明,利用超声浸渍法制备得到的Mn/EG催化剂低温催化氧化活性较好,且催化剂表面的3价Mn对反应活性有重要影响.进口气体中O2体积分数对反应活性有明显的影响,低温时高体积分数的氧能促进NO的转化.150℃时,在NO体积分数为0.05％、O2体积分数为3％、空速为47 770 h-1的条件下,该催化剂的NO催化氧化效率可达42％.     

石墨烯改性Al-MCM-41介孔分子筛负载铁芬顿催化剂降解苯酚

采用高温回流法将石墨烯(gh)掺杂于Al-MCM-41介孔分子筛中,通过浸渍法制备了石墨烯改性Al-MCM-41介孔分子筛负载铁芬顿催化剂(gh-Al-MCM-41-Fe),利用比表面仪、扫描电子显微镜-X射线能谱(SEM-EDX)对催化剂进行了表征,考察了不同p H条件下该催化剂对苯酚的催化降解效能.结果表明,gh-Al-MCM-41-Fe催化剂具有介孔结构,表明颗粒分布均匀,石墨烯的掺杂减小了颗粒粒径,与多种催化剂(非介孔Al2O3-Cu Al2O4、介孔Al2O3-Cu、介孔Al2O3-Fe、介孔Al-MCM-41-Fe)相比,gh-Al-MCM-41-Fe具有最高的苯酚催化降解效能,反应符合一级反应特征,石墨烯的掺杂能明显提高苯酚降解率和COD去除率,减少铁的溶出,拓宽p H范围,当p H值为3—5,反应90 min,COD去除率达到60%以上.     

Oxidation of diesel soot on binary oxide CuCr(Co)-based monoliths

Binary oxide systems (CuCr₂O₄, CuCo₂O₄), deposited onto cordierite monoliths of honeycomb structure with a second support (finely dispersed Al₂O₃), were prepared as filters for catalytic combustion of diesel soot using internal combustion engine's gas exhausts (O₂, NO_x, H₂O, CO₂) and O³ as oxidizing agents. It is shown that the second support increases soot capacity of aforementioned filters, and causes dispersion of the particles of spinel phases as active components enhancing thereby catalyst activity and selectivity of soot combustion to CO₂. Oxidants used can be arranged with reference to decreasing their activity in a following series: O₃ >> NO₂ > H₂O > NO > O₂ > CO₂. Ozone proved to be the most efficient oxidizing agent: the diesel soot combustion by O₃ occurs intensively (in the presence of copper chromite based catalyst) even at closing to ambient temperatures. Results obtained give a basis for the conclusion that using a catalytic coating on soot filters in the form of aforementioned binary oxide systems and ozone as the initiator of the oxidation processes is a promising approach in solving the problem of comprehensive purification of automotive exhaust gases at relatively low temperatures, known as the "cold start" problem.     

Immobilization of self-assembled pre-dispersed nano-TiO2 onto montmorillonite and its photocatalytic activity

The immobilization of pre-dispersed TiO₂ colloids onto the external surface of the clay mineral montmorillonite (Mt) was accomplished and regulated via a self-assembly method employing the cationic surfactant cetyltrimethylammonium bromide (CTAB). The role of CTAB in the synthesis process was investigated by preparing a series of TiO₂-CTAB-Mt composites (TCM) with various CTAB doses. The results indicated that a uniform and continuous TiO₂ film was deposited on the external surface of montmorillonite in the composite synthesized with 0.1 wt.% of CTAB, and the TCM nano-composites showed much higher values for specific surface area, average pore size and pore volume than the raw montmorillonite clay. Then, the formed TCM materials were applied in photocatalytic degradation of 2,4-dichlorophenol (2,4-DCP) in aqueous solution. The degradation efficiency reached as high as 94.7%. Based on the degradation intermediates benezoquinone, fumaric acid and oxalic acid identified by LC–MS analysis, a mechanism for the photocatalytic oxidation of 2,4-DCP on TiO₂/Mt nano-composites is proposed.