为了提高染料废水中COD和色度的去除效果,采用响应曲面法对聚硅酸类新型复合絮凝剂的制备工艺进行了优化实验研究。在单因素实验基础上采用Box-Behnken Design(BBD)实验设计方法,设计出了影响染料废水处理效果的3因素3水平共15组实验,其中n(Fe+Al):n(Si)的摩尔比为4～6,n(B+Mg):n(Si)的摩尔比为0.3～0.7,熟化时间为1～3 d。根据15组实验结果,以COD去除率和色度去除率为响应值分别建立了二次多项式响应曲面模型。模型优化结果显示,在n(Fe+Al):n(Si)摩尔比为5∶1,n(B+Mg):n(Si)为0.5∶1,熟化时间为2 d的条件下,制备得到的新型复合絮凝剂聚硅酸铝铁硼镁具有最佳的絮凝处理性能和脱色效果,能有效去除染料废水中的COD和色度,其中出水色度接近于0,COD的去除率达到87.65%,模型验证实验进一步验证了本文所建立的响应曲面法在复合絮凝剂制备工艺优化中的有效性。     

海水环境下玻璃纤维增强复合材料力学性能演化规律研究

目的 研究海水环境下海流能发电机组叶片用玻璃纤维复合材料力学性能的变化规律.方法 在实验室内通过海水浸泡试验、拉伸试验、弯曲试验以及剪切试验,测定叶片用玻璃纤维树脂基复合材料的吸水特性,以及在人工海水介质中各项力学性能参数的演变规律.结果 随着浸泡时间的增加,玻璃纤维树脂基复合材料吸水率先逐步增大、后趋于稳定,总吸水率约0.075％.抗拉强度呈先降低、后提高、又降低的趋势,抗拉强度最高可超过1100 MPa,最小值约为940 MPa.弹性模量和弯曲强度呈逐渐降低的趋势,弹性模量降幅约9.5％,弯曲强度降幅约为30％.弯曲模量变化起伏不定,变化幅度在15％以内.材料剪切强度呈先增大、后降低的趋势,最小值为189 MPa,较初始值高10 MPa.剪切模量呈先降低、后提高的现象,在浸泡28 d时,剪切模量最小,为16.4 GPa.结论 玻璃纤维增强树脂基复合材料经过长期海水浸泡后,拉伸及抗剪切性能略有降低,但降幅不大,抗弯性能下降明显,需要在叶片结构设计和强度计算时,充分考虑抗弯性能衰减的负面影响.     

湖泊、水库水的强化混凝除藻的试验研究

就高锰酸钾复合药剂强化混凝对湖泊、水库水中藻类的去除进行了研究，试验表明：投加一定量的高锰酸钾复合药剂可显著提高水中藻类的去除率。将经与预氯化、预投加高锰酸钾除藻工艺进行比较，表明高锰 酸钾复合药剂强化混凝除藻效率明显优于传统预氯化、预投加高锰酸钾除藻工艺。     

多层阻尼复合板常温贮存5年性能研究

目的分析多层阻尼复合板常温贮存5年的性能变化。方法对多层阻尼复合板进行常温下贮存5年的减振性能研究,通过贮存前后的正弦扫描试验和随机振动试验,获得贮存前后多层阻尼复合板的减振性能和模态变化,进行对比分析。结果阻尼复合板常温贮存5年后,径向模态有较大的下降,法向模态变化较少,组件上的加速度响应基本无变化。结论该多层阻尼复合板常温贮存5年后仍然满足要求。     

石墨-活性炭纤维复合电极电吸附处理含盐废水的研究

高盐废水是目前水处理领域的难点,作为一种新型的除盐技术,电吸附技术具有众多优点.本文研究了一种新型碳基复合材料,石墨-活性炭纤维复合电极,并考察了其应用于电吸附的影响因素和除盐效果.在电压为1.6 V,停留时间为60min,极板间距为1 cm时电吸附装置的除盐效果最优.用其分别对精制棉黑液和叶绿素铜钠废水进行了处理.电极对数为8对时对经酸析处理后的精制棉黑液的电导率和COD的去除率分别达到58.8%和75.6%;电极对数为6~8时对叶绿素铜钠生产废水的电导率的去除率能超过50.0%,COD的去除率约为13.5%.     

Revisiting the national corporate social responsibility index

This paper relies on Gjølberg’s national corporate social responsibility (CSR) index while its purpose is twofold. First, it seeks to extend the methodological instrument for assessing national CSR and, second, it applies the new approach to a much larger pool of countries (n = 86) in an attempt to provide a global CSR outlook. The emergent picture from the study is one of deficient CSR penetration and wide variation among countries where most of the assessed countries are still lagging in the endorsement of international CSR initiatives and schemes. Findings offer fertile ground to theorists and researchers for a deeper investigation of the national specificity of CSR and to further identify institutional determinants that shape the social responsiveness and self-regulation of business entities. The study has also implications for managers and top executives to consider as it infers that the national background can be influential in the development of a CSR agenda and can condition the level of CSR penetration.     

Identifying the largest individual sample value from a two-way composite sampling design

Composite sampling techniques for identifying the largest individual sample value seem to be cost effective when the composite samples are internally homogeneous. However, since it is not always possible to form homogeneous composite samples, these methods can lead to higher costs than expected. In this paper we propose a two-way composite sampling design as a way to improve on the cost effectiveness of the methods available to identify the largest individual sample value.     

高铁铝矾土制备聚合氯化铝铁及其在污水处理中的应用研究

利用含铁的低品位铝矾土为主要原料,添加适量铝酸钙粉,制备出絮凝剂聚合氯化铝铁.制备方法为酸溶两步法.对影响聚合铝铁制备的因素,如盐酸浓度、盐酸用量、温度和铝酸钙粉用量等进行了系统研究,得到了制备聚合铝铁的优化条件,同时将该絮凝剂用于实际工业污水的处理.研究结果表明：制备的絮凝剂絮凝效果明显优于一些传统的絮凝剂;不仅具有去浊性能好、沉降快的优点,而且具有原料易得,制备成本低的优势.     

青霉菌HHE-P7利用酱油废水产生微生物絮凝剂的研究

研究了微生物絮凝剂产生菌HHE-P7在酱油废水中产生微生物絮凝剂的絮凝特性。实验表明，酱油废水由于碳源丰富，是一种良好的培养基。HHE-P7菌最佳培养条件为：COD20000mg／L，K2HP041．0g／L，培养3d。最佳絮凝条件为在1L高岭土水中投加10～15mL微生物絮凝剂（MBF7），pH调至9，则絮凝率为90％以上；微生物絮凝荆在水系中主要起吸附架桥的作用。     

超细无碱玻纤复合滤料的过滤性能

袋式除尘是一种高效的除尘技术,对PM2.5具有较高的过滤效率,但是其运行阻力较大,因此,研发高效、低阻过滤材料是解决大气污染问题的关键所在。以耐高温的PPS纤维针刺布为上下层,超细无碱玻纤为中间层,经过超声波粘合或线缝合技术制备了多层复合过滤材料,研究了滤料在容尘状态下的过滤效率、过滤阻力,以及孔径变化。结果表明,该复合滤料的初始阻力低于150 Pa,容尘后对0.2~2 μm的颗粒物的过滤效率达80%以上;随着粉尘的沉积,滤料的过滤效率有了较大提高,对1 μm以上颗粒物的过滤效率可达99.99%以上,对最易透过粒径（MPPS）的过滤效率达95%以上;过滤前后,滤料的孔径分布发生了变化,过滤后滤料出现了1~5 μm的孔径分布。该复合滤料在工业高温粉尘过滤中将会有较好的应用前景。