瓷砖釉面TiO2薄层对甲基橙的光催化降解

采用溶胶-凝胶法，在瓷砖釉面上制备了良好光催化活性TiO2薄层材料，研究结果表明瓷砖釉面TiO2薄层材料对甲基橙的光催化反应遵循一级动力学规律，光催化降解率与液层厚度符合指数关系。在太阳光照射下，釉面瓷砖TiO2薄层材料能对甲基橙有效地降解。     

硅藻土负载型非均相芬顿催化剂制备及其降解苯酚的实验研究

以硅藻土为载体,采用直接蒸发法负载铁的氧化物,制备了一种新型负载型非均相芬顿催化剂,通过SEM、EDS和XRD等对催化剂进行了表征,并以苯酚去除率考察了催化剂性能。结果表明:铁氧化物可成功负载于硅藻土上;催化剂制备时最优铁离子浓度和固液质量比分别为0.5 mol/L和1∶10;催化剂重复使用性高,耐酸碱性良好,对苯酚的去除率可达99%以上。催化剂利用了硅藻土优异的物化性质,对难降解有机废水具有良好的应用前景。     

等离子体催化降解甲苯途径的原位红外研究

考察了在常温常压条件下,等离子体分别协同SiO₂、Al₂O₃、NiO/Al₂O₃降解甲苯的性能,并从材料的介电常数、对甲苯的吸附性及臭氧分解能力等角度分析了不同活性表现的原因,同时,采用原位红外技术研究了甲苯降解过程中催化剂表面吸附物种的变化.结果表明,当甲苯浓度为100 ppm,气体流量为100 mL·min^-1时,一定范围内,甲苯降解率随着能量密度、介电常数、吸附性及臭氧分解能力的提高而提高.甲苯在催化剂表面的吸附对其降解途径有十分重要的影响:在放电区域中加入SiO₂,甲苯仍然在气相中完成降解;而存在Al₂O₃ 及NiO/Al₂O₃时,甲苯氧化成苯甲酸的过程主要发生在催化剂表面,是甲苯催化降解的关键步骤,苯甲酸在活性位点的积累将降低催化剂的反应活性.     

Effect of transition metal doping under reducing calcination atmosphere on photocatalytic property of TiO2 immobilized on SiO2 beads

TiO₂ immobilized on SiO₂ (TiO₂/SiO₂) have been prepared by sol-gel method and various ions of transition metals (Cr³⁺, Co²⁺, Ni²⁺, Cu²⁺, and Zn²⁺) were doped on the photocatalyst using wet impregnation method under reducing calcination atmosphere. The photocatalytic activity of metal doped TiO₂/SiO₂ towards phenol degradation under black light irradiation were investigated and compared with undoped TiO₂/SiO₂. The results showed that the photoresponse of Cu²⁺ and Zn²⁺ doped TiO₂/SiO₂ were larger than undoped TiO₂/SiO₂, indicating that the photogenerated carriers were separated more efficiently in Cu²⁺ and Zn²⁺ doped TiO₂/SiO₂. The reactivity was in the order of Cu²⁺ > Zn²⁺ > Ni²⁺ > Cr³⁺ > Co²⁺. The different photoreactivity was ascribed to combine effect of the different ionic radii and photocorrison tendency of the dopants. The sample was also characterized by surface analytical methods such as X-ray diffraction, scanning electron micrograph/electron dispersive X-ray analyzer and UV-Vis absorption spectrum.     

Supercritical water oxidation of polyvinyl alcohol and desizing wastewater：Influence of NaOH on the organic decomposition

Polyvinyl alcohol is a refractory compound widely used in industry. Here we report supercritical water oxidation of polyvinyl alcohol solution and desizing wastewater with and without sodium hydroxide addition. However, it is difficult to implement complete degradation of organics even though polyvinyl alcohol can readily crack under supercritical water treatment. Sodium hydroxide had a significant catalytic effect during the supercritical water oxidation of polyvinyl alcohol. It appears that the OH ion participated in the C-C bond cleavage of polyvinyl alcohol molecules, the CO2-capture reaction and the neutralization of intermediate organic acids, promoting the overall reactions moving in the forward direction. Acetaldehyde was a typical intermediate product during reaction. For supercritical water oxidation of desizing wastewater, a high destruction rate (98.25%) based on total organic carbon was achieved. In addition, cases where initial wastewater was alkaline were favorable for supercritical water oxidation treatment, but salt precipitation and blockage issues arising during the process need to be taken into account seriously.     

Homogeneous and heterogeneous reactions of anthracene with selected atmospheric oxidants

The reactions of gas-phase anthracene and suspended anthracene particles with O3 and O3-NO were conducted in a 200-L reaction chamber, respectively. The secondary organic aerosol (SOA) formations from gas-phase reactions of anthracene with O3 and O3-NO were observed. Meanwhile, the size distributions and mass concentrations of SOA were monitored with a scanning mobility particle sizer (SMPS) during the formation processes. The rapid exponential growths of SOA reveal that the atmospheric lifetimes of gas-phase anthracene towards O3 and O3-NO are less than 20.5 and 4.34 hr, respectively. The particulate oxidation products from homogeneous and heterogeneous reactions were analyzed with a vacuum ultraviolet photoionization aerosol time-of-flight mass spectrometer (VUV-ATOFMS). Gas chromatograph/mass spectrometer (GC/MS) analyses of oxidation products of anthracene were carried out for assigning the time-of-flight (TOF) mass spectra of products from homogeneous and heterogeneous reactions. Anthrone, anthraquinone, 9,10- dihydroxyanthracene, and 1,9,10-trihydroxyanthracene were the ozonation products of anthracene, while anthrone, anthraquinone, 9-nitroanthracene, and 1,8-dihydroxyanthraquinone were the main products of anthracene with O3-NO.     

LNAPLs污染物在层状非均质多孔介质中的运移试验研究

文章通过室内试验研究层状非均质多孔介质中轻非水相液体(Light Non-Aqueous Phase Liquid,LNAPL)的运移机制与分布特性。首先,在二维砂槽上进行LNAPL的入渗试验,试验过程中用数码相机进行拍照,把LANPL的扩散过程以图像的形式记录下来;然后,用AutoCAD对图片进行分析处理,得出不同时刻LNAPL的入渗锋面变化图。结果发现,介质结构突变面改变了LNAPL的迁移模式。在LNAPL由中砂进入细砂层后,由于受到毛细作用的增强,其运移速度加快;而由中砂进入粗砂,受粗砂介质阻滞作用增强的影响,LNAPL运移速度变小。当LNAPL由干砂进入湿润砂体时,由于孔隙水浮托力增大,LNAPL先产生纵向运移,随后以横向迁移的形式在地下水位上部聚积。当达到一定厚度后,LNAPL的压头足以克服浮托力,驱替孔隙水进入砂土孔隙。另外,LNAPL的厚度足够大时,方可克服饱水层受到的浮托力,在地下水位上形成LNAPL池,并因孔隙水向周围砂体排泄,LNAPL池周围的水位上升。     

非均相类Fenton试剂的制备及其在焦化废水处理中的应用研究

利用浸渍法,将Fe3＋负载在经酸碱改性后的粉状活性炭上,当浸渍液浓度为2．5％,固化温度为270℃时,制成的催化剂催化活性较高。用自制的非均相类benton试剂降解焦化废水,通过正交试验和极差分析得出,影响因素的主次顺序为催化剂用量〉初始pH值〉反应时间〉H：0：投加量。结果表明,在100ml水样中。室温条件下,初始pH值为4．0,催化剂使用量为1．5g,H20：投加量为5ml（分两次投加）,反应时间为90min时,COD去除率可达99％。采用混凝＋化学沉淀＋非均相类Fenton试剂法处理焦化废水,各主要出水水质指标为：色度lO倍;COD浓度38．5mg／L;氨氮浓度8．4mg／L,达到国家一级排放标准。     

催化技术对绿色化学的影响研究

绿色化学又称环境友好化学,它是在化学产品的设计、制造和应用过程中运用一套原理和理论来减少或者消除对有害物质的生产和利用的一门学科。绿色化学工艺的目标是用化学的技术和手段去减少或消除那些对人类健康有害的原料、产物、副产物、溶剂和试剂等的产生或应用。催化技术是绿色化学工艺研究及应用的重要手段,简要介绍了绿色化学与催化的关系、催化剂的研究进展及典型实例,并列举了几种新型绿色催化剂,详细分析了其环境友好特性。