A study was conducted to determine the effect of the chironomid larval tube on heavy metal toxicity. Silica gel was provided as a substrate with which the chironomid larvae could construct larval tubes. A series of 96 h LC₅₀ bioassays were conducted with and without the presence of the silica gel substrate, to allow comparison between the two test conditions. From the study it was observed that a 10–15% variation in LC₅₀ value occurred. The 96 h LC₅₀ for copper at the temperatures 35, 28, 20, 15, and 10°C was observed to be 7.5, 9.5, 7.5, 4.5, 3.6, and 2.8 mg L^?1, respectively. The same test when conducted in the presence of silica gel produced LC₅₀ values of 26.50, 33.50, 15.82, 12.77, and 9.94 mg L^?1 for the same temperatures. This would demonstrate that the larval tube did, to some extent, protect the larvae from the effects of the heavy metal.     

电站锅炉管件失效泄漏原因分析

火力发电厂管件失效泄漏是频发事故,严重影响机组的安全、经济运行。以某发电厂后墙省煤器和低温再热器管子失效泄漏事故为例,通过对失效泄漏的管件进行宏观形貌分析、金相分析和强度分析,论证了泄漏事故的原因是由于腐蚀和钢管固有缺陷导致低温再热器高温段弯管外侧发生泄漏,泄漏的高速流体冲刷、气蚀导致后隔墙省煤器发生泄漏,进而对低温再热器反冲刷,加剧泄漏事故的恶化。最后提出更换失效管件,加强金属监督,尽量扩大防磨防爆检查范围,对易被气流磨损、冲刷部位进行防磨喷涂或加装防磨罩。     

氮化油管工艺危害识别及液氨槽事故树分析

对氮化油管工艺和设备存在的问题进行了危险分析,用事故树分析了液氨槽的爆炸危险性,并提出安全对策。     

玻璃纤维编织管动态膜生物反应器处理沼渣废液

一种新型的玻璃纤维编织管动态膜生物反应器应用于高黏度、高氨氮和高COD的沼渣废液的处理。该玻璃纤维编织管经过了固化和覆膜的组合改性,膜组件采用平板化的栅式构型。研究表明:组合改性方式分别为1∶4+1∶50和1∶2+1∶50时的膜组件的稳定通量分别为5.45 L/(m2.h)和6.50 L/(m2.h);同时膜组件的清洗效果良好,再次运行仍能够稳定,通量为5.35 L/(m2.h)。而且出水比较澄清,没有臭味,养分也得到了有效保留。此外,改性后的玻纤编织管估算价格约为93.2元/m2,低于传统有机膜。     

双层管用于发光细菌检测水样毒性时的色度修正

阐述了应用发光细菌检测有色水样毒性时,水样色度会引起附加发光抑制的原因,提出应用同心双层检测玻管,可以对有色水样色度引起的附加发光抑制加以修正.通过比较单层管和双层管测定标准曲线间的差异、设置阴性对照和阳性对照评价该方法的可靠性,以及用该方法检测有色水样活性黑KN-B溶液的急性毒性实验,结果表明,用同心双层检测玻管可以有效修正由水样色度引起的附加发光抑制.     

蒸汽发生器管束外表面的应力腐蚀破裂规律(续一)

报道了某核动力系统蒸汽发生器,因管束的应力腐蚀破裂而发生严重泄漏事故的原因和规律.采用肉眼宏观检查、着色探伤、超声波探伤和单管泵压试验等方法探明了蒸汽发生器的应力腐蚀破裂特点和在管束表面上的立体分布规律;采用电子探针、电子显微镜、X射线衍射仪和扫描电镜等微观分析技术查明了产生应力腐蚀破裂的原因和文中所述分布规律的原因,并提出了一些改进办法.不仅为后来的蒸汽发生器的设计、制造和运行提供了依据,而且也为应力腐蚀破裂的研究,提供了大量的实际资料.展示了众多在蒸汽发生器的实际运行过程中所产生的应力腐蚀破裂形貌的照片,并列出了形成各种规律的统计数据.     

玻璃纤维-砂浆管试件动态拉伸破坏特性试验研究

为了探究动载作用下GFRP（玻璃纤维）-砂浆管的动态拉伸破坏特性,采用分离式SHPB试验装置对2种空心率的水泥砂浆管和GFRP-砂浆管进行动态拉伸试验。结果表明:空心率越小、冲击气压和壁厚越大,试件峰值抗拉强度越大;GFRP-砂浆管的峰值抗拉强度随GFRP管壁厚的增大而不断增大,在空心率为0.292时,峰值抗拉强度随GFRP管壁厚增大呈对数函数递增,而在空心率0.187时,峰值抗拉强度随GFRP管壁厚增大呈指数函数递增;无GFRP管时水泥砂浆管呈对称四块破碎,GFRP-砂浆管在0.5~0.7 MPa冲击气压下仅有细小裂纹产生,在0.8 MPa冲击气压下,与入射杆接触部分产生“楔形”破坏,但总体保持为管状、破坏程度仍低于水泥砂浆管,表明GFRP管对水泥砂浆管具有较好的保护作用,可有效提高其动态抗拉强度。     

大容积无缝气瓶瓶口外螺纹修复方法及安全分析

为确定不同瓶口壁厚气瓶的外螺纹修复方式,采用数值和理论方法,通过分析外螺纹修复后气瓶的瓶体应力分布、周向转动和轴向窜动情况,对直接加工和采用热套工艺加装衬环2种瓶口外螺纹修复方式的安全性进行评价。结果表明:针对内螺纹规格为3-1/4″-8UN的气瓶,当采用直接加工方式将外螺纹修复至4-1/2″-8UN时,气瓶最大应力位于气瓶筒体上,此时气瓶可安全使用;当已修复至4-1/2″-8UN的瓶口外螺纹再次出现磨损时,直接加工的修复方式会对气瓶的安全使用造成影响,应采用热套工艺加装衬环方式修复瓶口螺纹。     

取芯管取芯过程管壁温度变化特性试验*

为给冷冻取芯过程中瓦斯解吸模拟试验提供依据,依托自主研制的取芯管管壁温度自动采集装置,研究不同取芯深度及煤体破坏类型下取芯过程管壁温度变化特性。结果表明:在原生结构煤中取芯时,取芯过程管壁温度变化主要分为3个阶段,即稳定不变阶段、快速上升阶段与缓慢下降阶段,分别对应进钻、取芯与退钻过程;在构造煤中取芯时,管壁温度变化可分为缓慢上升阶段、快速上升阶段与缓慢下降阶段,分别对应进钻、取芯与退钻过程。在构造煤中,取芯深度越大,取芯管管壁升温幅度越大,取样过程中管壁温度峰值越大,且在取芯过程中,取芯管管壁温度传感器B1,B2,B3存在温升滞后现象;同一取芯深度,煤体破碎程度越大,取芯管管壁升温幅度越小,取芯结束时取芯管管壁温度越低。     

换热器不锈钢换热管束开裂原因分析

一台换热器换热管束发生了开裂泄漏.采取全面检验的方式,通过宏观检查、化学成分分析、断口微观形貌和能谱分析、金相分析等方法,对换热管开裂原因进行了分析.结果表明:该换热管开裂为氯化物应力腐蚀开裂.壳程介质循环冷却水中CI元素含量是应力腐蚀开裂的主要因素,结构缺陷、敏感的工作温度区间、水中溶解氧和含S杂质导致了应力腐蚀的快速发展.