改性粉煤灰处理低浓度含磷废水的研究

以酸改性粉煤灰为吸附剂,处理低质量浓度(1 mg/L左右)磷酸盐溶液,探讨了改性剂的种类、改性剂用量、吸附剂用量、反应时间、pH以及温度对除磷效果的影响.结果表明:(1)经过酸改性后粉煤灰的磷去除率显著提高,而且硫酸改性粉煤灰的除磷效果更好,磷去除率最高可达97.68％.(2)最佳条件:选择硫酸用量为5 mL/g进行改性,硫酸改性粉煤灰投加量为2.0g,反应时间为60 min,pH为7.2～10.8,温度为25℃(即室温).(3)改性粉煤灰对磷的吸附更符合Freundlich吸附等温模型,既有物理吸附,也有化学吸附,并以Ca、Mg氧化物与磷形成磷的沉淀物为主.     

粉煤灰微波改性及其对Cr~（6＋）的吸附特性

将粉煤灰（fly ash,FA）微波辐照制得微波改性粉煤灰（MFA）,选择用H2SO4、NaOH和Ca（OH）2对MFA进行化学改性制得微波化学改性粉煤灰（MMFA）,结果表明,用2 mol/L NaOH并按与MFA的质量体积比为1∶4制得的MMFA对Cr6＋的吸附去除效果最好,与原灰相比,去除率显著增强。研究了NaOH改性MMFA对废水中Cr6＋的吸附性能。动力学研究结果表明,MMFA对Cr6＋的吸附动力学符合二级吸附动力学速率方程,吸附受颗粒内扩散过程控制。热力学研究结果表明,在25、35和45℃下MMFA对Cr6＋的等温吸附行为均可用Langmuir方程、Freundlich方程和线性方程描述,所得热力学参数吸附自由能（ΔG）、吸附焓（ΔH）和吸附熵（ΔS）均为负值,说明MMFA对Cr6＋的吸附过程为自发进行的放热吸附过程。     

垃圾焚烧飞灰对染料（亚甲基蓝）的吸附性能

以垃圾焚烧飞灰为吸附剂对亚甲基蓝进行了吸附脱色实验。主要探讨了飞灰粒径、用量、温度、pH值和初始浓度等因素对亚甲基蓝吸附的影响,同时分析了吸附上清液中重金属Pb和Cr的浸出毒性。研究结果表明,在25—45℃、pH值2～12、飞灰用量1～5g范围内,经过180min吸附,亚甲基蓝的脱色率都达75％以上,最高可达99．46％。实验还得出,除重金属Pb外,吸附上清液中重金属的浸出量远远低于《危险废物鉴别标准浸出毒性鉴别》的限定值。因此,若能降低重金属Pb的浸出,飞灰将具有应用于处理染料废水的巨大潜力。     

碱熔预处理对粉煤灰溶解规律的影响及其动力学

在用粉煤灰合成沸石分子筛的过程中,粉煤灰在碱液中的溶解影响到合成反应的速率以及合成分子筛的性能。采用碱熔的方法处理粉煤灰,研究了粉煤灰在碱液中的溶解机理以及碱熔预处理对粉煤灰溶解规律的影响,并采用Noyes-Whitney方程分析其溶解动力学。结果表明,经过碱熔预处理的粉煤灰有36．11％的SiO2和16．33％的Al2O3转化为水溶性成分,剩余的非水溶性部分在碱液中的溶解速率也有大幅提高,硅铝离子达到平衡浓度的时间缩短,铝离子的平衡浓度有较大提升。Noyes-Whitney方程对粉煤灰在碱液中的溶解规律适用,相关系数都达到0．979以上。     

垃圾焚烧飞灰中不同粒径的毒性特性

对广州市某垃圾焚烧发电厂的焚烧飞灰进行粒径分级毒性分析研究。主要研究了粒径在35～1 000μm范围内的飞灰的腐蚀性和短期浸出毒性,包括Cr、Cd、Mg、Pb、Mn、Fe、Cu、Zn、Ni、Co等重金属,SO24-,Cl-,NO3--N和NO2--N,同时也研究了飞灰的物质组成和矿物特性。研究结果表明,所有粒径飞灰的浸出液pH值在12.3～12.5之间,属于有腐蚀性的危险废物,重金属Mg、Pb、Zn的浸出浓度最高,分别为168.78、53.94和86.40 mg/L。飞灰浸出液和含量最高分别达到8.87g/L和1.38 g/L,同时浸出液中测出一定量的硝态氮和亚硝态氮,证明飞灰吸附了垃圾焚烧过程中产生的氮氧化物气体。另外,研究得出飞灰的基本组成元素为Ca、Si、Cl、K、Na、S、Al、Mg和Fe,而重金属则以Zn、Pb、Mn、Cu、Cr等为主。矿物相主要为含硅和钙的化合物及NaCl和KCl等氯化物。     

Effect of fly ash on sorption behavior of metribuzin in agricultural soils

This investigation was undertaken to determine the effect of two different fly ashes [Kota and Inderprastha (IP)] amendment on the sorption behavior of metribuzin in three Indian soil types. The IP fly ash was very effective in increasing the metribuzin sorption in the soils. The sorption with IP amendment was increased by 15–92%, whereas with the Kota fly ash an increase in sorption by 13–38% was noted. The adsorption isotherms fitted very well to the Freundlich adsorption equation and, in general, slope (1/n) values less then unity were observed. Although both the fly ashes significantly decreased metribuzin desorption, the IP fly ash was comparatively more effective in retaining metribuzin in the soils. Metribuzin sorption in the IP fly ash-amended soils showed strong correlation with the fly ash content and compared to K_f/K_d values, K_FA values (sorption normalized to fly ash content) showed less variation. Metribuzin sorption-desorption did not correlate to the organic carbon content of the soil-fly ash mixture. The study demonstrates that all coal fly ashes may not be effective in enhancing the sorption of metribuzin in soils to the same extent. However, among the fly ashes used in this study, the IP fly ash was observed to be significantly effective in enhancing the sorption of metribuzin in soils. This may play an important role in reducing the run off and leaching losses of the herbicide by retaining it in the soil.     

CaCl2高温热处理垃圾焚烧飞灰中重金属的挥发特性

以深圳市某垃圾焚烧厂飞灰为原料,采用高温管式电阻炉,研究了在0．6L／minN,气氛下,CaCl2在不同添加量、处理温度及处理时间下对飞灰中重金属Pb、Cd、Zn和Cu挥发特性的影响,并对收集到的二次飞灰进行成分及物相分析。结果显示,X射线衍射仪和EDS分析表明,二次飞灰主要是由NaCl、KCl和部分SiCl4组成,zn主要以K2ZnCl4形式挥发,而Pb则主要以氧化物PbO和Pb3SiO5的形式挥发。最终得到CaCl2热处理飞灰的最佳二次气化条件：以0．6L／minN,为载气,添加14wt％的CaCl2,在1100℃高温下处理2．5h。经CaCl2热处理后的剩余飞灰,其浸出毒性达到了《生活垃圾填埋场污染控制标准》要求。     

粉煤灰沸石负载Ce^3＋／TiO2光催化降解水中的菲和荧蒽

以钛酸四丁酯为前驱体,粉煤灰合成沸石为载体,采用溶胶-凝胶方法,在低温条件下制备了稀土铈掺杂的TiO2光催化剂。利用SEM—EDS、XRD、FTIR对催化剂进行了分析和表征。以高压汞灯为灯源,对多环芳烃菲、荧蒽的降解进行了研究。实验考查了稀土铈掺杂质量分数、催化剂用量、溶液pH、目标物初始质量浓度等因素对光催化降解的影响,研究了其光降解动力学。结果表明,当稀土铈含量为0．5％,催化剂用量为3g／L,pH偏碱性时,催化效果最佳。光催化反应符合Langmuir—Hinshelwood动力学规律,菲、荧蒽的降解过程符合一级反应动力学,反应速率常数分别为0．0126min^-1,0．0099min^-1。     

CaCl2高温热处理垃圾焚烧飞灰中重金属的挥发特性

以深圳市某垃圾焚烧厂飞灰为原料,采用高温管式电阻炉,研究了在0.6 L/min N₂气氛下,CaCl₂在不同添加量、处理温度及处理时间下对飞灰中重金属Pb、Cd、Zn和Cu挥发特性的影响,并对收集到的二次飞灰进行成分及物相分析。结果显示,X射线衍射仪和EDS分析表明,二次飞灰主要是由NaCl、KCl和部分SiCl₄组成,Zn主要以K₂ZnCl₄形式挥发,而Pb则主要以氧化物PbO和Pb₃SiO₅的形式挥发。最终得到CaCl₂热处理飞灰的最佳二次气化条件:以0.6 L/min N₂为载气,添加14 wt%的CaCl₂,在1 100℃高温下处理2.5 h。经CaCl₂热处理后的剩余飞灰,其浸出毒性达到了《生活垃圾填埋场污染控制标准》要求。     

改性油页岩灰渣对水中DNBP吸附去除效果

采用PDMDAAC改性方法对油页岩灰渣进行改性,确定最佳改性方案,并研究了环境因素对改性油页岩灰渣吸附DNBP的影响。实验研究结果表明,油页岩灰渣经20 g/L 的PDMDAAC处理时,对DNBP的吸附能力最强。在吸附温度为30℃,初始溶液pH值为4的条件下,0.3 g 的改性油页岩灰渣对30.0 mg/L DNBP溶液50 mL,吸附120 min时,其吸附率达到94.48%以上。在实验条件下,改性油页岩灰渣对DNBP的吸附符合Langmuir和Freundlich等温吸附方程,相关系数分别为0.9985和0.9776,其对DNBP的理论饱和吸附量达到6.196 mg/g。改性油页岩灰渣对DNBP的吸附主要归因于离子交换和表面吸附作用。