海水环境下玻璃纤维增强复合材料力学性能演化规律研究

目的 研究海水环境下海流能发电机组叶片用玻璃纤维复合材料力学性能的变化规律.方法 在实验室内通过海水浸泡试验、拉伸试验、弯曲试验以及剪切试验,测定叶片用玻璃纤维树脂基复合材料的吸水特性,以及在人工海水介质中各项力学性能参数的演变规律.结果 随着浸泡时间的增加,玻璃纤维树脂基复合材料吸水率先逐步增大、后趋于稳定,总吸水率约0.075％.抗拉强度呈先降低、后提高、又降低的趋势,抗拉强度最高可超过1100 MPa,最小值约为940 MPa.弹性模量和弯曲强度呈逐渐降低的趋势,弹性模量降幅约9.5％,弯曲强度降幅约为30％.弯曲模量变化起伏不定,变化幅度在15％以内.材料剪切强度呈先增大、后降低的趋势,最小值为189 MPa,较初始值高10 MPa.剪切模量呈先降低、后提高的现象,在浸泡28 d时,剪切模量最小,为16.4 GPa.结论 玻璃纤维增强树脂基复合材料经过长期海水浸泡后,拉伸及抗剪切性能略有降低,但降幅不大,抗弯性能下降明显,需要在叶片结构设计和强度计算时,充分考虑抗弯性能衰减的负面影响.     

Starch, Poly(lactic acid), and Poly(vinyl alcohol) Blends

Research on biodegradable materials has been stimulated due to concern regarding the persistence of plastic wastes. Blending starch with poly(lactic acid) (PLA) is one of the most promising efforts because starch is an abundant and cheap biopolymer and PLA is biodegradable with good mechanical properties. Poly(vinyl alcohol) (PVOH) contains unhydrolytic residual groups of poly(vinyl acetate) and also has good compatibility with starch. It was added to a starch and PLA blend (50:50, w/w) to enhance compatibility and improve mechanical properties. PVOH (M_W 6,000) at 10%, 20%, 30%, 40%, 50% (by weight) based on the total weight of starch and PLA, and 30% PVOH at various molecular weights (M_W 6,000, 25,000, 78,000, and 125,000 dalton) were added to starch/PLA blends. PVOH interacted with starch. At proportions greater than 30%, PVOH form a continuous phase with starch. Tensile strength of the starch/PLA blends increased as PVOH concentration increased up to 40% and decreased as PVOH molecular weight increased. The increasing molecular weight of PVOH slightly affected water absorption, but increasing PVOH concentration to 40% or 50% increased water absorption. Effects of moisture content on the starch/PLA/PVOH blend also were explored. The blend containing gelatinized starch had higher tensile strength. However, gelatinized starch also resulted in increased water absorption.     

Mechanical Properties with the Functional Group of Additives for Starch/PVA Blend Film

This paper deals with the mechanical properties and degree of swelling (DS) of starch/PVA blend film with the functional groups i.e., hydroxyl and carboxyl group, of additives. Starch/PVA blend films were prepared by using the mixing process. Glycerol (GL) with 3 hydroxyl group, sorbitol (SO) with 6 hydroxyl group, succinic acid (SA) with 2 carboxyl group, malic acid (MA) with 1 hydroxyl and 2 carboxyl group, tartaric acid (TA) with 2 hydroxyl and 2 carboxyl group and citric acid (CA) with 1 hydroxyl and 3 carboxyl group were used as additives. The results of measured tensile strength (TS) and elongation (%E) verified that both hydroxyl and carboxyl group as a functional groups increased the flexibility and strength of the film. Values of DS for GL-added and SA-added films were low. However, DS values of the films added MA, TA or CA with both hydroxyl and carboxyl group were comparatively high. When the film was dried at low temperature, the properties of the films were evidently improved. The reason is probably because the hydrogen bonding was activated at low temperature.     

含疏松缺陷的ZL205A合金力学性能研究

目的获取含疏松缺陷ZL205A材料主要力学性能参数的变化规律及力学行为。方法通过单轴拉伸实验测试,采用割线法估算含不同等级疏松ZL205A试样的力学性能参数;基于试样断面及载荷-位移曲线分析,归纳ZL205A材料的力学行为,并通过有限元模拟对假设的力学模型进行验证。结果发现ZL205A材料的抗拉强度、伸长率、弹性模量及屈服强度指标呈现随疏松等级增加而降低的趋势,材料变形塑性屈服阶段不明显且具有脆性断裂特征。结论 Ramberg-Osgood方程适合于描述ZL205A材料的弹塑性本构关系。     

丁腈橡胶密封圈高温老化行为——自由状态和承压状态

目的研究丁腈橡胶密封圈自由状态和承压状态下的高温老化行为。方法以拉伸强度和拉断伸长率为参数,对各温度下的老化行为进行表征和分析。结果 70℃条件下机械应力大大加快了橡胶密封件拉伸强度的下降速率,以致试验64 d时拉伸强度甚至比110℃时还低,拉断伸长率的下降速率也明显加快了;90℃加速条件下机械应力对拉伸强度的下降有一定的促进作用,但对拉断伸长率的变化基本无影响;110℃加速条件下机械应力对拉伸强度和拉断伸长率均没有明显的影响。结论机械应力在较低温度下可以显著促进丁腈橡胶密封圈热氧老化,高温条件下促进作用不明显。     

火灾下钢框架结构热-力耦合模拟与性能分析

基于"自然火灾安全概念"(NFSC)的基本思想,提出了火灾下钢结构热-力耦合模拟方法。利用ANSYS的参数化设计语言,建立了ANSYS软件与OZone火灾分析软件的数据接口,实现了火灾分析软件与大型有限元软件的耦合运用。基于火灾模拟软件OZone的分析结果,利用APDL语言,对钢框架结构进行了真实火灾场景下的热-力耦合模拟。研究表明:钢框架结构在真实火灾场景下,受非均匀变热流影响,结构内部将产生热应力梯度和应力牵移现象;同时钢框架中钢梁固接时,火灾初期变形较小,当达到某个关键时间点后将开始大的变形破坏,其主要原因是钢框架内部产生塑性铰,即钢梁由固接变为铰接,释放了对钢梁的约束。     

某推进剂低温加速老化试验研究

目的考查某推进剂在-10℃和-28℃这两个温度下性能随老化时间的变化趋势。方法采用低温加速老化试验。结果在低温下老化推进剂最大抗拉强度先下降然后逐渐升高,伸长率变化趋势较为复杂。常温正常拉伸速度条件下伸长率基本在初始值附近波动,低温快速拉伸条件下伸长率直线下降。结论低温下推进剂老化力学性能的变化趋势与高温老化不尽相同,造成这种差异的原因可能是老化机理不同所致。     

不同瓦斯压力下煤体力学特性试验研究

为研究瓦斯对煤体力学特性的影响,设计不同瓦斯压力条件下煤体单轴压缩试验,研究煤样力学参数及变形特征随瓦斯压力的变化趋势,探讨瓦斯对煤体力学性质的影响机制,得出单轴压缩下煤样力学参数,并记录煤样的破坏形态.研究结果表明:随瓦斯压力增大,应力-应变曲线压实阶段增大,弹性阶段缩小,失稳破坏后曲线缓慢下降,抗压强度和弹性模量单...