镧铝改性凹凸棒粘土对富营养化湖泊有机磷控制效果

通过吸附与原位模拟实验,研究了镧铝改性凹凸棒粘土（La/Al@ACP）对水体有机磷的吸附性能及其覆盖对沉积物磷释放的影响,并通过沉积物磷分级、DGT技术、扫描电镜能谱技术探讨材料覆盖对沉积物磷形态影响机制.结果显示,La/Al@ACP添加后,上覆水及底泥间隙水中磷含量显著下降,并伴随沉积物有效磷通量的减少.有机磷形态分析表明,添加La/Al@ACP后活性态的Lab-P_o不断向稳定态的Hum-P_o转化,有效控制了底泥磷向上覆水释放的风险.La/Al@ACP作为一种控制湖泊富营养化的有效材料,可用于底泥内源磷的固定与控制.     

AT－SS复合颗粒吸附剂的制备和除铅性能研究

通过颗粒吸附剂在含铅溶液中的振荡实验．研究了凹凸棒石粘土（ＡＴ）和钢渣（ＣＳ）、水泥（ＳＮ）、石英砂（ＳＳ）制得的多种复合颗粒吸附剂的除铅性能及制备条件．确定出最佳颗粒吸附剂为ＡＴ－ＳＳ，混合比为５：１，７００℃下焙烧１２０ｍｉｎ．对铅的静态吸附容量高达５００ｍｇ／ｇ以上，动态吸附容量为６０ｍｇ／ｇ．在１．５ｍｌ／ｍｉｎ的流速下，穿透时间为２０ｈ，洗脱回收率为４８．３％．当Ｐｂ进样量为２００ｍｇ／Ｌ时，ＡＴ－ＳＳ吸附剂在２３６倍床体积之内，流出液浓度低于排放标准．     

改性凹凸棒土对染料废水脱色初步实验

以凹凸棒土为原料,通过复配造粒、热处理的方法对凹凸棒土进行改性,并用改性后的凹凸棒土对染料废水进行处理。考察了pH值、凹凸棒土用量及吸附时间等因素的影响,探索了最佳工艺条件。结果表明,改性后的凹凸棒土吸附性能有了明显改善,对染料废水进行处理,脱色率可达99%以上,处理废水量与吸附剂比为670颐1,且其原料价廉易得、工艺简单、成本低,是一种较好的脱色吸附剂。     

Effect of sorbed and desorbed Zn(Ⅱ) on the growth of a green alga (Chlorella pyrenoidosa)

Toxic effect of Zn(Ⅱ)on a green alga(ChloreUa pyrenoidosa)in the presence of sepiolite and kaolinite was investigated.The Zn-free clays were found to have a negative impact on the growth of C.pyrenoidosa in comparison with control samples(without adding any clay or Zn(Ⅱ)).When Zn(Ⅱ)was added,the algae in the presence of clays could be better survived than the control samples,which was actually caused by a decrease in Zn(Ⅱ)concentration in the solution owing to the adsorption of Zn(Ⅱ)on the clays.When the solution system was diluted,the growth of algae could be further inhibited as compared to that in a system which had the same initial Zn(Ⅱ)concentration as in the diluted system.This in fact resulted from desorption of Zn(Ⅱ)from the zinc-contaminated clays,although the effect varied according to the different desorption capabilities of sepiolite and kaolinite.Therefore the adsorption and desorption processes of Zn(Ⅱ)played an important part in its toxicity,and adsorption and desorption of pollutants on soils/sediments should be well considered in natural eco-environmental systems before their risk of toxicity to aquatic organisms was assessed objectively.     

氯化磁性凹土树脂的制备与表征研究

利用表面负载的方法将有机化磁性凹土与苯乙烯、二乙烯苯等制备磁性凹土树脂;对磁性凹土树脂进行氯甲基化改性,制备出氯化磁性凹土树脂.表征了样品的形貌、结构以及表面积,研究了树脂对天然有机物(腐殖酸)的吸附性能.结果表明:氯化后的磁性凹土树脂的比表面积是原有的1.9倍,对附腐殖酸的饱和吸附能力也从原有的41.84 mg/g提高到了51.02 mg/g,这表明改性后的树脂增强了其对腐殖酸的去除能力.     

2,2′-二硝基联苄生产废水的处理研究

对十六烷基三甲基溴化铵改性凹凸棒土、凹凸棒土负载TiO2采用XRD、FTIR以及TG等手段进行了分析和表征,对比了改性凹凸棒土、活性炭、大孔树脂等不同吸附剂和凹凸棒土负载TiO2对二硝基联苄生产废水的处理效果。结果表明:十六烷基三甲基溴化铵改性凹凸棒土的废水中污染物的去除率比凹凸棒土提高了2.5倍;凹凸棒土负载TiO2在波长λ=254 nm下光照0.5 h,对废水中污染物的去除率是凹凸棒土的2.0倍;投加量为3%活性炭在pH为2.0⁵.0时,对该类废水中污染物的去除率可达80%以上。     

Remediation of copper polluted red soils with clay materials

Attapulgite and montmorillonite were utilized to remediate heavy metal polluted red soils in Guixi City, Jiangxi Province, China. The e ects of clay minerals on availability, chemical distribution, and biotoxicity of Cu and Zn were evaluated. The results provided a reference for the rational application of clay materials to remediate heavy metal contaminated soils. From the sorption experiment, the maximum adsorbed Cu2+ by attapulgite and montmorillonite was 1501 and 3741 mg/kg, respectively. After polluted red soil was amended with attapulgite or montmorillonite and cultured at 30 and 60 days, soil pH increased significantly compared to the control. An 8% increase in the amount of montmorillonite in soil and 30 days incubation decreased acid exchangeable Cu by 24.7% compared to the control red soil. Acid exchangeable Cu decreased with increasing amounts of attapulgite and montmorillonite, with best remediation e ect reached at a dose of 8%. Results also showed that the Cu poisoning e ect on earthworms was reduced with the addition of attapulgite and montmorillonite. Montmorillonite showed the best e ect, with the addition of a 2% dose the mortality of earthworms decreased from 60% to zero compared to the control. Our results indicated that the bioavailability of Cu in soils was reduced more e ectively with the application of montmorillonite than attapulgite.     

Adsorptive property of Cu^2＋-loaded montmorillonite clays for Escherichia coli K_（88） in vitro

The Cu²⁺-loaded montmorillonite clays (MMT-Cu) may be a good material for the adsorbed and eliminated pathogenic bacteria from aqueous solution.     

腐殖酸修饰凹凸棒对U(Ⅵ)的吸附性能及机理

采用腐殖酸(HA)修饰凹凸棒(ATP)制备得到腐殖酸/凹凸棒(HA/ATP),用于去除废水中的U(Ⅵ).通过静态吸附实验,研究了溶液初始pH、投加量、吸附时间和初始浓度对吸附的影响,并用扫描电镜(SEM),X射线能谱图(EDS),傅里叶红外光谱仪(FITR)分析吸附机理.实验结果表明,去除率随时间的增大而增大,在120 min内可以达到平衡;吸附剂投加量越大,溶液pH =6左右时越有利于U(Ⅵ)的去除;HA/ATP能多次重复使用,且经过5次吸附解吸后对U(Ⅵ)的去除率仍能达到96％.吸附过程均符合Langmuir和Frendlich等温方程.较之准一级动力学,准二级动力学模型能更好地拟合实验数据.SEM-EDS、FITR分析结果表明,U(Ⅵ)被成功地吸附到了HA/ATP的表面,吸附机理为络合作用.     

Fe-pillared clay as a Fenton-type heterogeneous catalyst for cinnamic acid degradation

Fe-pillared montmorillonite has been used as a Fenton-type heterogeneous catalyst for the removal of cinnamic acid in water. The influences of the cinnamic acid, catalyst and H2O2 concentrations and pH on the removal rate of cinnamic acid have been studied. The results show that the efficiency of Fe-pillared montmorillonite is higher than that of the Fe ions in the homogeneous phase, and less sensitive to pH.