不同方法制备LaCu0.8Zn0.2Al11O19-δ催化剂及其催化分解N2O活性研究

采用共沉淀法、溶胶-凝胶法和反相微乳液法制备了六铝酸盐催化剂LaCu0.8Zn0.2Al11O19-δ,进行了X射线衍射(XRD)和BET表征.并考察了它们对N2O催化分解反应的活性,研究了制备方法对催化剂LaCu0.8Zn0.2Al11O19-δ的结构、粒径、比表面积和催化分解N2O活性的影响.结果表明,3种方法制备的催化剂经1200℃焙烧4 h后.都能形成六铝酸盐晶相,其中反相微乳液法制备的催化剂具有较小的粒径和较大的比表面积,其催化分解N2O的活性表现最佳,起始反应温度(T10%)为494℃,完全反应温度(T99%)为678℃.     

安全新型长余辉发光材料的应用研究

新型长余辉光致发光材料是以铝酸盐为主体成分 ,再添加微量稀土元素成分进行激活 ,吸收光能后进行蓄光而后发光的物质。目前所用的主要是以碱土金属铝酸盐为基体 ,用稀土元素 Eu为主要激活剂 ,再加入另一种稀土元素 ( Nd、Dy、Tm等 )改善发光性能。新型长余辉发光材料性能稳定 ,安全无毒 ,不含放射性物质 ,发光强度高 ,余辉时间长 ,在水中长时间浸泡也不影响发光效果。新型长余辉光致发光材料白天利用太阳光能蓄光 ,夜晚发光 ,可用于发光的钟表 ,轮船、飞机的仪表盘 ,道路照明 ,建筑标志物等 ,是一种绝好的“绿色”光源。特别是在安全防护…     

金属掺杂的镧锰六铝酸盐催化还原NO

采用共沉淀法制备了以LaMnAl11O19-δ为基础的不同金属元素掺杂的六铝酸盐催化剂LaMnMAl10O19-δ（其中M分别为Fe、Co、Ni、Cu、Zn、Y、Ag、Ce）,对样品进行了XRD、H2-TPR和BET表征,在CH4存在下,考察了催化剂对NO的还原反应活性.实验结果表明,以（NH4）2CO3作沉淀剂制备的...     

六铝酸盐催化剂的催化还原脱硫脱硝性能

采用共沉淀法制备Cu和Fe掺杂的六铝酸盐催化剂(SrCuxFe1-xAl11O19-δ,x为0,0.2,0.4,0.5,0.6,0.8,1),通过XRD、TPR、BET等技术方法对催化剂的结构及性质进行了研究,并考察了以CO为还原剂的催化脱硝活性。结果表明,用碳酸铵作为沉淀剂在1 200℃焙烧4 h可以形成完整的六铝酸盐晶型,Cu和Fe能够取代Al3+,很好地促进六铝酸盐晶体结构的形成;SrCuxFe1-xAl11O19-δ催化剂有很好的脱硫脱硝催化活性,此类型的催化剂均使SO2、NO的转化率在空速为6 000 h-1下达到了80%和90%以上。向体系中加入氧气会对催化活性有较大影响。     

尖晶石型铝酸盐光催化还原CO_2

采用有机物前驱法制备了3种尖晶石型铝酸盐催化剂(CoAl_2O_4,ZnAl_2O_4,CoAl_2O_4)。采用FTIR,XRD,UV-Vis DRS等技术对催化剂进行表征,并将催化剂应用于CO_2的光催化还原。表征结果显示:除CoAl_2O_4外,CoAl_2O_4和ZnAl_2O_4在煅烧时均直接形成尖晶石相;CoAl_2O_4,CoAl_2O_4,ZnAl_2O_4的平均粒径分别为25.21,21.35,23.26 nm,禁带宽度分别为1.77,1.45,3.82 eV。分别以煅烧温度为900℃、煅烧时间为4 h时制得的ZnAl_2O_4,CoAl_2O_4,CoAl_2O_4为催化剂,在催化剂加入量为1.5 g/L、CO_2流量为200 mL/min、反应温度为60℃的条件下光催化反应8 h,甲酸产生量分别为443.54,365.65,241.39μmol/g。     

高强度铝酸盐粉煤灰无机人造理石的研制

为解决二次资源的浪费和环境污染问题 ,该课题组应用了大量高需水量比的粉煤灰及其它工业废渣 ,采用双搅拌二次复合成型工艺 ,在常温下 ,制成了物理力学性能优良的高强度铝酸盐粉煤灰无机人造大理石 ,为粉煤灰等 :工业废渣的综合利用开辟了新的道路     

铜铈掺杂六铝酸盐的脱硝性能

用共沉淀法制备用于脱除NO的六铝酸盐催化剂LaMxAl12-xO19(M =Cu,Ce,CuCe).用XRD、H2-TPR和BET对催化剂进行了结构和物性表征.用微型催化反应装置考察了催化剂在CO选择性催化还原NO中的活性.结果表明,Cu离子易于进入六铝酸盐晶格内,形成完整的六铝酸盐结构.Ce离子不易于进入六铝酸盐晶格内,主要以CeO2的形式存在.在CO+ NO条件下,3种催化剂都表现出较好的脱硝活性,LaCuCeAl10O19中由于Cu离子与Ce离子间产生协同作用,该催化剂的脱硝活性有所增加.加入SO2后,3种催化剂都有不同程度的失活现象发生,其中LaCuAl11O19催化剂受SO2中毒影响最严重,LaCuCeAl10O19催化剂的脱硝活性在三者中最好.     

Factors effecting aluminum speciation in drinking water by laboratory research

Effects of aluminum on water distribution system and human health mainly attribute to its speciation in drinking water. Laboratory experiments were performed to investigate factors that may influence aluminum speciation in water supply system. The concentration of soluble aluminum and its transformation among other aluminum species were mainly controlled by kinetics processes of related reactions. Total aluminum concentration had a notable e ect on the concentrations of mononuclear and soluble aluminum in the first 4 day; then its e ect became weak. At pH above 7.50, both fluoride and orthophosphate had little e ect on aluminum speciation; while, when the solution pH was below 7.50, the concentrations of mononuclear and soluble aluminum were proportional to the concentration of fluoride and inversely proportional to the concentration of orthophosphate. Both mononuclear and polynuclear silicic acids could complex with mononuclear aluminum by forming soluble aluminosilicates. In addition, the adding sequence of orthophosphate and aluminum into drinking water would also a ect the distribution of aluminum species in the first 4 day. In order to minimize aluminum bioavailability in drinking water, it was suggested that orthophosphate should be added prior to coagulant process, and that the concentrations of fluoride and silicic acids should be controlled below 2.0 and 25 mg/L, respectively, prior to the treatment. The solution pH in coagulation and filtration processes should be controlled in the range of 6.50–7.50.     

六铝酸盐负载CuO催化还原NO性能

采用共沉淀法制备了LaAl12O19六铝酸盐载体,采用等体积浸渍法制备了不同负载量的CuO/LaAl12O19催化剂,并对其进行了XRD、H2-TPR和BET表征,考察了催化剂对CH4选择催化还原NO的性能.结果表明,CuO的负载并未改变六铝酸盐载体的结构,Cu在载体上以Cu2+的形式存在,活性组分CuO与载体LaAl12O19之间存在协同作用;CuO/LaAl12O19催化剂对CH4选择催化还原NO表现出良好活性,所制备的催化剂均能使NO的转化率达到99%;其中负载量为1.0 wt%的CuO/LaAl12O19催化剂的活性最好,完全反应温度T99%为560℃,且在80 h稳定性试验中表现出了良好的高温活性和热稳定性.     

软锰矿烟气脱硫渣制备硫铝酸盐水泥熟料

以软锰矿烟气脱硫尾渣、石灰石、铝矾土为原料烧制硫铝酸盐水泥熟料可以变废为宝,实现废物的资源化利用。考察了该方法制备硫铝酸盐水泥熟料的可行性,研究了生料配比、烧制温度及保温时间对水泥熟料矿相的影响。采用X射线衍射仪(XRD)对水泥熟料中各矿相的生成过程进行了分析。实验结果表明:生料配比对水泥熟料矿相有很大的影响,当体系中加入铝制组分时水泥熟料的主要矿相无水硫铝酸钙(C4A3S)的形成比较好。随着温度的提高,一些过渡相的产物逐渐消失,但温度太高会使已生成的C4A3S逐渐分解,减少熟料中的早强矿物。保温时间为30 min时得到比较理想的硫铝酸盐水泥熟料。XRD分析结果表明,生石灰∶铝矾土∶尾渣的配比为48∶23∶29,温度为1 280℃,保温时间为30 min得到比较理想的硫铝酸盐水泥熟料。