The Thermal Discharges From Nuclear Power Plants in Taiwan

The increasing use of sea water for industrial cooling presents a real threat to the ecological environment in the ocean. in Taiwan where many electric power plants along the coast take sea water for cooling, people are concerned seriously about nuclear power plants. There are three nuclear power plants in Taiwan. Each plant has two units for generating power. the first two are located along the northern coast of Taiwan. the third is located in Kenting National Park along the coast of southernmost Taiwan. the plants take sea water for cooling, and discharge their heated effluents to the ocean surface from the coast. the thermal effluents have variable effects on the ecological environment near the plants. Fishermen living near the power plants complain that the heated water affects the inshore fishery catch. in addition, the thermal water from the second plant is easily accumulated near the coastal zone to influence the nearby swimming area in the summer-time. the thermal water from the third plant bleaches or kills some corals in shallow water near the outlet, and this conflicts with the interests of Kenting National Park.     

内质网应激在氟暴露致小鼠睾丸损伤中的作用

探讨了内质网应激在亚慢性氟暴露致小鼠睾丸损伤中的作用及分子机制.选用健康初断乳ICR雄性小鼠30只,随机分为对照组（C）、低氟组（LF）和高氟组（HF）,分别饮用自来水、5、30 mg·L^-1氟化钠水溶液90 d.亚慢性氟暴露结束后,以睾丸脏器系数、睾丸组织氧化/抗氧化酶和形态结构、精子质量、睾丸细胞凋亡、葡萄糖调节蛋白78（GRP78）、CCAAT/增强子结合蛋白同源蛋白（CHOP）、半胱氨酸天冬氨酸蛋白酶12（CASPASE-12）、半胱氨酸天冬氨酸蛋白酶3（CASPASE-3）为观测点.结果表明,与对照组比,LF组和HF组LDH、SOD、T-AOC活性下降,MDA含量上升,HF组GSH-PX活性下降,差异有统计学意义（p<0.05或p<0.01）;LF组可见细胞层次减少、间隙变大,成熟精子数量减少,HF组细胞溶解、层次紊乱,空泡化严重,少见成熟精子;LF组和HF组小鼠的精子活力降低,HF组小鼠精子数量下降,畸形率上升,差异有统计学意义（p<0.05或p<0.01）;LF组和HF组睾丸细胞凋亡指数上升,差异有统计学意义（p<0.01）;LF组和HF组Grp78、Caspase-12、Caspase-3基因表达水平上升,差异有统计学意义（p<0.05或p<0.01）.结果提示,除氧化应激以外,Caspase-12和Caspase-3基因表达异常可能是氟暴露致小鼠睾丸细胞凋亡异常的分子机制之一.     

Effects of SO2 and H2O on low-temperature NO conversion over F-V2O5-WO3/TiO2 catalysts

F-V_2 O_5-WO3/Ti02 catalysts were prepared by the impregnation method.As the content of F ions increased from 0.00 to 0.35 wt.%,the NO conversion of F-V_2 O_5-WO_3/TiO_2 catalysts initially increased and then decreased.The 0.2 F-V_2 O_5-WO_3/TiO_2 catalyst(0.2 wt.% F ion)exhibited the best denitration(De-NOx) performance,with more than 95% NO conversion in the temperature range 160-360℃,and 99.0% N2 selectivity between 110 and 280℃.The addition of an appropriate amount of F ions eroded the surface morphology of the catalyst and reduced its grain size,thus enhancing the NO conversion at low temperature as well as the sulfur and water resistance of the V_2 O_5-WO3/Ti02 catalyst.After selective catalytic reduction(SCR) reaction in a gas flow containing SO_2 and H_2 O,the number of NH3 adsorption sites,active component content,specific surface area and pore volume decreased to different degrees.Ammonium sulfate species deposited on the catalyst surface,which blocked part of the active sites and reduced the NO conversion performance of the catalyst.On-line thermal regeneration could not completely recover the catalyst activity,although it prolonged the cumulative life of the catalyst.In addition,a mechanism for the effects of S02 and H_2 O on catalyst NO conversion was proposed.     

短期干旱胁迫对马尾松排放挥发性有机物的影响

为探究干旱环境对BVOCs排放的影响,应用动态封闭式采样系统和热脱附-气相色谱-飞行质谱仪,对短期干旱胁迫作用下马尾松的BVOCs排放进行了实验室测量,定量分析BVOCs排放速率和排放组成的变化.结果表明,干旱胁迫时异戊二烯的排放受到抑制,排放速率降低约50%;单萜烯和倍半萜烯的排放水平增强,排放速率分别为137.85和0.98μg/（m²·h）,是未受胁迫时的2.9和2.0倍.除反式-α-香柠檬烯外,干旱胁迫促进各单萜烯和倍半萜烯化合物的排放,是未受胁迫时的1.3~42.4倍,其中3-蒈烯排放的响应最敏感,α-葑烯、α-水芹烯和石竹烯的响应最弱.干旱胁迫时单萜烯和倍半萜烯的排放组成有所变化,但主导的化合物种类不变,单萜烯以α-蒎烯、香桧烯和β-蒎烯为主,占比分别为48%、17%和17%;倍半萜烯以石竹烯和长叶烯为主,占比分别为57%和34%.     

石英灯辐射加热条件下低密度碳/酚醛复合材料高温响应及分析

目的研究低密度碳/酚醛复合材料在不同地面加热实验测试响应的差异性,指导材料在实际应用环境下的高温响应分析。方法对低密度碳/酚醛复合材料开展了热流为400 kW/m~2的单侧石英灯辐射加热实验,利用热电偶测温系统测量试件在加热过程中不同位置的温度时间历程,并对试件的烧蚀形貌和微观结构进行观测。同时与热流为464k W/m~2的氧乙炔加热陶瓷板辐射加热实验结果进行对比分析,并且采用有限元方法对材料的传热传质多场耦合计算进行分析。结果对于石英灯辐射加热,在测量点升温到接近200℃时,温度响应拐点都依次出现。由于加热的辐射热源不同,在不同的辐射波段下,多孔材料吸收和发射的热量不同,短时间内氧乙炔加热陶瓷板辐射加热使材料内部升温速率比石英灯辐射加热实验的要快,但长时间加热时现象刚好相反。结论进行传热传质多场耦合计算材料高温响应时,合理确定材料宏观性能随温度的变化至关重要。     

纤维增强气凝胶复合材料高温结构转变及热稳定性研究

目的研究高温受热条件下纳米复合隔热材料的结构转变特征及热稳定性。方法采用扫描电镜、X射线衍射仪、红外光谱仪及热重仪等检测方法。结果纤维增强气凝胶材料从室温到650℃存在连续的质量损失,从室温到放热前,质量损失为1.66%;365℃开始出现放热,温度升至398℃时达到峰值,整个放热过程对应质量损失约为1.3%;从435℃放热结束开始到650℃的质量损失为1.46%。经过400℃热处理后,试样比表面积从268m~2/g增加到437m~2/g;当试样热处理温度达到600℃时,试样的比表面积明显随之降低至198m~2/g。结论 SiO_2气凝胶复合材料以无定形结构为主,存在少量的二氧化钛晶体。在400℃左右,SiO_2气凝胶结构中硅甲基Si—CH_3发生氧化,产生明显的放热峰,之后硅羟基Si—OH之间发生缩聚反应,使600℃热处理后气凝胶中Si—O—Si网络骨架强度有所提高。未处理的纤维增强气凝胶材料试样上气凝胶纳米颗粒构成的块体较为良好地包裹在玻璃纤维表面,而经过600℃的高温热处理1 h后,块体气凝胶脱离了光滑的纤维表面,气凝胶纳米粒子发生收缩,致使材料比表面积下降。     

海水中阴极极化对X80钢应力腐蚀及氢脆敏感性的影响

目的研究不同p H值海水中阴极极化对X80管线钢应力腐蚀及氢脆的抑制作用。方法采用慢应变速率拉伸试验、电化学测试、微观组织观察等分析方法。结果 X80钢在天然海水中的析氢电位约为-940m V(vs.SCE,下同),海水p H为3.5时析氢电位发生正移。其应力腐蚀敏感性与极化电位有很大关系,随着极化电位负移,X80钢的氢脆敏感性增加。天然海水中当极化电位负于-950 m V时,断口出现准解理断裂特征形貌。在-1050 m V极化电位下,钢材进入氢脆断裂区发生脆性断裂。海水p H为3.5时,-900 m V钢材有发生氢脆的危险。结论与天然海水相比,X80钢在p H为3.5的酸性海水中具有较高的应力腐蚀敏感性,两种海水介质中X80钢的应力腐蚀敏感性均随极化电位负移而增加。     

玻璃纤维-铝合金层合板氙灯老化性能研究

目的研究氙灯环境对玻璃纤维-铝合金层合板性能的影响。方法通过研究玻璃纤维-铝合金层合板在氙灯老化后的力学性能、基体红外光谱、铝合金表面形貌及元素变化,分析层合板的氙灯老化机理。结果随氙灯老化时间的延长,树脂基体老化降解程度越高,树脂与纤维、铝合金的界面强度下降,使材料拉伸及弯曲性能降低,拉伸强度受老化影响最为显著的是正交结构层合板,老化84 d后强度降低13.7%,正交结构0°方向层合板的弯曲强度受氙灯老化影响降低4.6%,其他试样的弯曲强度降幅均低于5%,氙灯老化后的铝合金层表面的微凹坑数量及尺寸无明显变化,但凹坑氧元素随老化周期延长略微增加。结论氙灯环境主要影响玻璃纤维-铝合金层合板中的复合材料层及各界面,树脂基体的降解导致力学性能的衰退,而对于铝合金的影响并不明显。     

包装箱用碳纤维增强复合材料贮存寿命研究

目的研究碳纤维增强复合材料贮存条件下的性能变化趋势和寿命评估。方法对碳纤维增强复合材料开展四个不同温度条件下的热氧老化试验,按试验周期定期取样开展冲击性能测试,对试验数据采用寿命预估方法进行处理,对材料性能进行预估。结果通过数据计算分别得到我国热带海洋、干热沙漠等典型气候条件下的碳纤维增强复合材料贮存寿命分别为17.21~35.89年。结论碳纤维增强复合材料具有较好的贮存性能,在较为严酷的热带海洋气候和给定的失效判据条件下,寿命预计为17.21年。试验和数据处理方法可以较好地预计材料的性能变化趋势和开展寿命评估。     

铍青铜弹簧片应力腐蚀断裂研究

目的研究传感器微动开关弹簧片应力腐蚀的机理,找到断裂原因。方法对弹簧片进行断口形貌观察、能谱成分分析,并进行产品模拟腐蚀实验。结果传感器内部意外进入雨水,在工作温度下形成湿热环境,开关盒中的游离氨在此环境下释放出来,在开关盒内部形成潮湿氨气氛,铍青铜弹簧片工作时凹面一侧承受静拉应力作用,从而在潮湿氨和拉应力共同作用下发生应力腐蚀开裂。结论通过采用无氨酚醛塑料制备开关盒,弹簧片的应力腐蚀得到了有效预防。