Cr3+掺杂对TiO2薄膜光催化活性的影响

采用溶胶-凝胶法制备了TiO2粉末和以釉面瓷砖为载体的TiO2薄膜,讨论了不同Cr3+掺杂浓度对TiO2光催化活性的影响,并采用UVVIS对其光学性能进行了检测.结果表明,Cr3+掺杂和釉面瓷砖的交互作用能够显著提高TiO2薄膜的光催化活性,最佳掺杂浓度为6.04×1017个·cm-3,且随着TiO2光催化活性的提高,薄膜的吸收带边发生了明显的红移,提高了可见光的利用率.     

硅胶载钴基催化剂对乙醇废液的催化制氢研究

以硅胶负载Co-Ce-B为催化剂,通过催化NaBH4在乙醇中醇解生成氢气来处理利用乙醇废液。研究了催化剂的量、反应温度和乙醇浓度对NaBH4醇解产氢速率的影响。结果表明:产氢速率随着催化剂的量增加而增加;随着温度的升高,产氢速率逐渐增快,根据醇解反应动力学方程,计算得反应活化能为48.54 kJ/mol;随着乙醇浓度的增加,产氢速率逐渐增加,当乙醇质量分数为90%时,产氢速率达0.417 L/(min·g)。     

氮氟掺杂二氧化钛(N,F-TiO2)的制备及可见光催化活性的研究

以氨水为氮源,氢氟酸为氟源,采用溶胶-凝胶法制备了氮氟掺杂二氧化钛(N,F-TiO2)光催化剂,并通过X-射线衍射(XRD)和扫描电镜(SEM)技术对其晶型和形态进行表征.最后以酸性红B为模型污染物,探讨了N和F加入量、焙烧温度、焙烧时间、照射时间、催化剂用量、溶液初始浓度和照射功率等因素对N,F-TiO2可见光催化活性的影响.结果表明,制备的N,F-TiO2以锐钛型为主,N和F的掺杂对TiO2的晶相没有明显改变,但可以扩大TiO2的可见光响应范围.当N和F的加入量均为2.0%,且在500℃下焙烧40 min时,得到的N,F-TiO2的可见光催化活性明显高于单N或单F掺杂的TiO2(N-TiO2或F-TiO2).对于50 mL浓度为10.0 mg·L-1的酸性红B溶液,当催化剂加入量为1.5 g·L-1,128W光照3.0 h,溶液pH=5.6时,去除率为85.40%.适当延长光照时间至4.0 h,降解率几乎可达100%.另外,研究还证明了N,F-TiO2催化可见光降解过程中有.OH自由基生成.     

La3+掺杂对吸附相反应制备TiO2复合催化剂的结晶过程及弱紫外光下活性的影响

利用吸附相反应技术制备弱紫外光响应的高效催化剂,并通过XRD、XPS以及HRTEM探索了不同焙烧温度下La3+掺杂量对TiO2结晶过程的影响.结合弱紫外光下甲基橙的降解反应,深入研究催化剂结晶过程的变化对弱紫外光下催化剂活性的影响.结果表明,La3+掺杂会抑制TiO2的结晶过程.当焙烧温度或者掺杂量较低时,La3+不能进入TiO2的晶格结构但会轻微地抑制TiO2的结晶过程;未进入晶格结构的La3+存在会引入光生载流子的浅能级捕获中心,在弱光体系中极大提升了催化剂的活性.当La3+的掺杂量为0.05%(原子分数)时,经过900℃焙烧后催化剂降解能力最高,其活性超过商用P25的2倍多.在较高La3+掺杂量(超过0.20%)时,900℃焙烧后一定量La3+进入TiO2的晶格结构而大大抑制了TiO2结晶;这种强烈的抑制作用使得催化剂中存在大量无定形结构TiO2,无定形TiO2甚至多于700℃焙烧后的催化剂,反而大大抑制了弱光体系中催化剂活性.     

Photocatalytic activity of Fe-doped CaTiO3 under UV-visible light

The photocatalytic degradation of methylene blue（MB） over Fe-doped CaTiO3 under UV-visible light was investigated. The as-prepared samples were characterized using X-ray diffraction（XRD）, scanning electron microscope（SEM） equipped with an energy dispersive spectrometer（EDS） system, Fourier transform infrared spectra（FT-IR）, and UV-visible diffuse reflectance spectroscopy（DRS）. The results show that the doping with Fe significantly promoted the light absorption ability of CaTiO3 in the visible light region. The Fe-doped CaTiO3 exhibited higher photocatalytic activity than CaTiO3 for the degradation of MB.However, the photocatalytic activity of the Fe-doped CaTiO3 was greatly influenced by the calcination temperature during the preparation process. The Fe-doped CaTiO3 prepared at500°C exhibited the best photocatalytic activity, with degradation of almost 100% MB（10 ppm）under UV-visible light for 180 min.     

Non-UV based germicidal activity of metal-doped TiO2 coating on solid surfaces

A stain-based screening method was developed to screen different catalyst coatings for their germicidal activity. A Baclight dead/live bacteria viability kit （invitrogen, molecular probes） was used for staining the cell. The screening was carried out following a standard procedure. This included loading cell suspension to solid surface and maintaining contact for 30 min, then staining with a mixture containing dyes. The stained cells were observed using an epifluorescent microscope and photographed with a CCD camera under UV. Metal-doped TiO2 coatings on AI plates were prepared and tested for non-UV germicidal activity without using UV. It was tested using model microorganisms such as Bakers Yeast （Saccharomyces cerevisiae）, Bacillus subtilis, Pseudomonas putida, and Escherichia coli. On the basis of the germicidal activity of catalyst and the degree of damage caused to the cells, the stained cells may appear green （viable）, green with red or yellow nuclei and yellow （compromised） or red （nonviable）. According to their stained color, cells were counted to calculate the percentage of dead, live, and compromised cells. Compromised cells are cells that grow very slowly after reculturing indicating a degree of reversible cell damage. Screening the germicidal activity using this staining method is accurate and efficient, and requires less time than the culture-based method. A modification to the procedure for measuring germicidal activity of rough surfaces or fibrous coatings was developed. Both TiO2 and metal-doped TiO2 （Ag, Pt, Au, Cu） possess non-UV based germicidal activity. The germicidal activity of TiO2 was found to be related with its wetting property and can be improved by UV irradiation before testing. It is not greatly affected by contact time, indicating a fast acting germicidal activity.     

氮掺杂氧化钛的简易制备及可见光催化活性的研究

为开发对可见光响应的催化剂,以尿素为氮掺杂剂,采用简易溶胶-凝胶法制备氮掺杂氧化钛,并以2,4-DCP的降解检验其光催化活性。XRD、BET、XPS和UV-Vis漫反射光谱分析表明,随着氮/钛原子比（N/Ti)的增大,各催化剂晶粒尺寸减小,比表面积增大,锐钛矿相向金红石相的转变得到抑制,除0#样品出现金红石相外,其他催化剂均只出现锐钛矿相;掺入催化剂的N位于晶格O位点和晶格间隙,替代N和间隙N掺杂使催化剂的光吸收发生明显的红移。荧光光谱分析表明,当N/Ti在0～6范围内增加时,反应体系中·OH自由基的产生速率增加,当N/Ti增大至8时,速率则下降。相似的规律也表现在氮掺杂量对光催化活性的影响。适量氮掺杂能增强氧化钛的可见光催化活性,该改性催化剂可用于有机污染物的太阳光激催化降解。     

N掺杂TiO_2光催化剂的制备及其H_2O_2改性的研究

以钛酸四丁酯为前驱物,采用水解沉淀法制备了N掺杂TiO_2光催化剂和H_2O_2改性的N掺杂TiO_2光催化剂.实验表明,H_2O_2改性的N掺杂TiO_2光催化剂的最佳制备条件为:氨水(质量分数28%)加入量20 mL,焙烧温度500 ℃,H_2O_2(质量分数30%)加入量2.0 mL.日光下,N掺杂TiO_2光催化剂及H_2O_2改性的N掺杂TiO_2光催化剂在反应90 min时的活性红紫去除率达99%,它们对活性红紫的去除率远高于P_(25)TiO_2光催化剂.H_2O_2改性的N掺杂TiO_2光催化剂中N质量分数比改性前明显提高,制备的两种催化剂中不仅含有N元素,同时还含有C和H元素.     

复合型CoO/TiO2光催化剂降解亚甲基蓝动力学研究

以钛酸四丁酯为前驱体,采用溶胶凝胶法,制备了CoO掺杂的TiO2光催化剂。利用X射线衍射（XRD）、扫描电镜（SEM）、透射电镜（TEM）、紫外可见漫反射（UV-vis DRS）对催化剂进行了分析、表征。以中压汞灯为光源,研究了亚甲基蓝（MB）在CoO/TiO₂微粒水悬浮液中的降解动力学。结果表明：所制备的催化剂活性组分主要是锐钛矿型的二氧化钛和CoO固溶体,粒径为25～30 nm,分布均匀。亚甲基蓝的光催化降解动力学满足一级动力学,在一定的浓度范围内,反应速率常数随初始浓度增大而减少,适当的掺钴量可以有效地提高TiO₂光催化活性,其最佳掺杂量重量百分比为0.25%。     

低温等离子体联合光催化技术降解甲苯的实验研究

采用低温等离子体联合光催化技术降解甲苯,从电压、电源频率、甲苯气体流量、初始浓度和Mn2+掺杂量等方面考察其对甲苯降解率的影响,并对比γ-Al2O3、TiO2/γ-Al2O3和Mn1.0/TiO2/γ-Al2O3(Mn2+摩尔分数为1.0%)3种填料的甲苯降解能量利用效果.结果表明,在相同电压和频率条件下,3种填料的甲...