Shape-dependent bactericidal activity of TiO2 for the killing of Gram-negative bacteria Agrobacterium tumefaciens under UV torch irradiation

This paper demonstrated the relative bactericidal activity of photoirradiated (6W-UV Torch, λ?>?340 nm and intensity?=?0.64 mW/cm²) P25–TiO₂ nanoparticles, nanorods, and nanotubes for the killing of Gram-negative bacterium Agrobacterium tumefaciens LBA4404 for the first time. TiO₂ nanorod (anatase) with length of 70–100 nm and diameter of 10–12 nm, and TiO₂ nanotube with length of 90–110 nm and diameter of 9–11 nm were prepared from P-25 Degussa TiO₂ (size, 30–50 nm) by hydrothermal method and compared their biocidal activity both in aqueous slurry and thin films. The mode of bacterial cell decomposition was analyzed through transmission electron microscopy (TEM), Fourier transform-infrared (FT-IR), and K⁺ ion leakage. The antimicrobial activity of photoirradiated TiO₂ of different shapes was found to be in the order P25–TiO₂?>?nanorod?>?nanotube which is reverse to their specific surface area as 54?<?79?<?176 m² g^?1, evidencing that the highest activity of P25–TiO₂ nanoparticles is not due to surface area as their crystal structure and surface morphology are entirely different. TiO₂ thin films always exhibited less photoactivity as compared to its aqueous suspension under similar conditions of cell viability test. The changes in the bacterial surface morphology by UV-irradiated P25–TiO₂ nanoparticles was examined by TEM, oxidative degradation of cell components such as proteins, carbohydrates, phospholipids, nucleic acids by FT-IR spectral analysis, and K⁺ ion leakage (2.5 ppm as compared to 0.4 ppm for control culture) as a measure of loss in cell membrane permeability.