| 土壤中SRB对钢设备的腐蚀 |
| |
| 引用本文： | 朱绒霞.土壤中SRB对钢设备的腐蚀[J].装备环境工程,2005,2(3):67-69. |
| |
| 作者姓名： | 朱绒霞 |
| |
| 作者单位： | 空军工程大学理学院,陕西,西安,710051 |
| |
| 摘 要： | 通过模拟实验，研究得出SRB对钢设备的腐蚀特征为点蚀。同时，对SRB的点蚀坑的形成过程进行了分析，发现钢点蚀的形成包括：萌生过程和发展过程：并且腐蚀介质中的Cl^-是点蚀坑进一步发展的主要因素。
|
| 关 键 词： | SRB 点蚀 Cl- |
| 文章编号： | 1672-9242(2005)03-0067-03 |
| 修稿时间： | 2005年3月22日 |
SRB Corrosion of Steel Equipment in Soils |
| |
| ZHU Rong-xia.SRB Corrosion of Steel Equipment in Soils[J].Equipment Environmental Engineering,2005,2(3):67-69. |
| |
| Authors: | ZHU Rong-xia |
| |
| Abstract: | With simulating tests,it was concluded that the characteristics of sulfate reduction bacteria(SRB)corrosion to steel equipment is pitting. With analyzing process of SRB pitting,it was discovered that process of corrosion pitting exists beginning period and growing period. At the same time, it was inferred that Cl- is the key factor of growing period of pitting. |
| |
| Keywords: | SRB pitting corrosion Cl- |