某型武器复合材料漆层开裂原因分析及试验研究

对某型武器进行环境试验考核时，碳纤维复合材料出现了不同程度的漆层开裂现象，针对这些问题，进行了技术性分析，并进行措施改进。通过确定合理的喷漆环境、表面质量、喷漆工艺及油漆厚度等，某型武器碳纤维复合材料顺利通过环境试验，漆层无开裂现象，取得了良好的效果。

Cause Analysis and Test Research on Composites Paint Cracking of Certain Weapon

During the environmental test of a certain weapon, different extents of cracking occurred in a paint layer on carbon fiber composite material. Aiming at such problems, technical analysis and measure improvement were carried out. By determining reasonable paint spraying environment, surface quality, painting technology and paint thickness, the carbon fiber composite material used in the certain weapon smoothly passed the environmental test. The paint layer has no cracking phenomenon and achieves good effect.