Ecotoxicity assessment of slag generated in the process of recycling lead from waste batteries

The aim of this study was to evaluate the possible toxicity of the leachate produced by the residues generated in the process of recycling lead from waste batteries. These residues are slag, which once formed, is characterised by its content in ferrous sulphide, sodium carbonate as well as residual coke from the process. It also contains, as minor components, lead and other heavy metals. The slag was stored and watered periodically over a period of 6 months, its composition changing until finally becoming inert, with no exothermal activity. The slag was leached, and its ecotoxicity was determined by means of the bioluminescence test, along with its content in heavy metals. The results obtained indicate a greater degree of toxicity in the residues with a shorter storage period than the established one, and which were therefore still in the phase of decomposition. However, in the samples taken on completing 6 months of storage, the EC₅₀ value of the leachate was found to be higher than 3000 mg/l. Hence, a storage period under suitable environmental conditions which leads to inactivity of the residue as well as a decrease in its ecotoxicity, is considered absolutely essential. At the same time, a direct relationship was observed between the lead content and the ecotoxicity value.