基于地聚合反应的生活垃圾焚烧飞灰资源化利用实验研究
引用本文:李春林. 基于地聚合反应的生活垃圾焚烧飞灰资源化利用实验研究[J]. 工业安全与环保, 2021, 47(2): 97-100
作者姓名:李春林
作者单位:西南科技大学固体废物处理与资源化教育部重点实验室 四川绵阳 621010
摘    要:为了实现对城市生活垃圾焚烧飞灰的资源化利用,本实验以城市生活垃圾焚烧飞灰为原材料,通过碱激发法制备出力学性能优异的地聚合物固化体.当碱激发剂的模数为1.0,垃圾焚烧飞灰含量为60%,碱激发剂和固体质量比为1:1.2时垃圾焚烧飞灰基地聚合物的抗压强度最佳.XRD分析结果表明所制备的地聚合物中存在少量碳酸钙和沸石结晶相,S...

关 键 词:城市生活垃圾  焚烧飞灰  资源化利用  地聚合物

Experimental Study on Resource Utilization of Municipal Solid Waste Incineration Fly Ash Based on Geopolymerization
LI Chunlin. Experimental Study on Resource Utilization of Municipal Solid Waste Incineration Fly Ash Based on Geopolymerization[J]. Industrial Safety and Dust Control, 2021, 47(2): 97-100
Authors:LI Chunlin
Affiliation:(Key Laboratory of Solid Waste Treatment and Resource Recycle, Ministry of Education, Southwest University of Science and Technology Mianyang,Sichuan 621010)
Abstract:Geopolymer solidified bodies was prepared by alkali excitation method to realize the purpose of resource utilization of municipal solid waste incineration(MSWI)fly ash,using MSWI fly ash as raw materials.The effects of the modulus of alkali activator modulus,the mass content of metakaolin,and the mass ratio of alkali activator to solid were investigated.The experimental results revealed that the optimum parameters were as follows:the modulus of the alkali activator was 1.0,the content of MSWI fly ash was 60%,and the mass ratio of the alkali activator to the solid was 1∶1.2.The microstructure characterization of XRD indicated that there were a small amount of calcium carbonate and zeolite crystals in the as-prepared geopolymers.SEM displayed that the structure of the solidified body was compact.In addition,a large number of Si(Al)-O-Si groups existed in the product,which contributed to enhance the compressive strength of solidified body.
Keywords:municipal solid waste  incineration fly ash  resource utilization  geopolymer