Effect of Hybrid Tackifiers on Adhesion Properties of Epoxidized Natural Rubber-Based Pressure-Sensitive Adhesives

Viscosity, peel and shear strength of epoxidized natural rubber (ENR)-based pressure-sensitive adhesive was studied by using hybrid tackifiers consisting of a mixture of coumarone-indene resin and petro resin. The coumarone-indene resin concentration was fixed at 40 parts per hundred parts of rubber (phr). The concentration of petro resin, however, was varied from 20 to 80 phr. Toluene and polyethylene terephthalate (PET) film were used as the solvent and coating substrate respectively throughout the experiment. Viscosity of adhesive was determined by a HAAKE Rotary Viscometer whereas peel and shear strength was measured by a Lloyd Adhesion Tester. Results show that viscosity and shear strength decreases with increasing petro resin concentration. However, peel strength exhibits a maximum value at 40 phr petro resin, an observation which is attributed to maximum wettability and compatibility of adhesive on the substrate. ENR 25-based adhesive exhibits higher viscosity and peel strength but lower shear strength compared to the ENR 50 adhesive system.