F108氟橡胶湿热老化影响双因素方差分析

目的 研究湿热因素对F108氟橡胶老化的影响.方法 采用χ2检验的方法 ,对氟橡胶圆柱形试样的初始高度进行假设检验,推断F108氟橡胶材料压缩永久变形服从正态分布.采用方差分析的方法 ,结合湿热老化试验数据,对F108氟橡胶湿热老化不同时间的压缩永久变形进行湿热双因素方差分析.结果 在开始阶段(即老化1 d后),温度和...

Double Factor Variance Analysis of Hygrothermal Aging for F108 Fluororubber

A hypothetical test is carried out on the initial height of the cylindrical sample of fluororubber using the method ofχ2 inspection,and it is inferred that the compression permanent deformation of the F108 fluororubber materials follows a normal distribution.Using variance analysis method,combined with the data of Hygrothermal aging test,the double factor variance analysis of hydrothermal aging has been carried out on the compression deformation of F108 fluororubber at different aging time.At the initial stage(after 1 day of aging),the F values of temperature and humidity were 77.25 and 9.34,respectively,which were greater than Fα(α=0.05),and the F value of temperature humidity interaction was 14.19,which was bigger than Fα.In the middle and late stage of the test(after aging for 6,12 and 16 days),the F values corresponding to temperature increased sharply,reaching 365.38,458.03 and 354.13,respectively,and the F values corresponding to humidity also increased to 31.69,34.03 and 31.02,respectively,which were far bigger than Fα.The results show that the effects of temperature and humidity on the performance of F108 fluororubber are significant at the initial stage of aging,with significant:temperature>temperature and humidity interaction>humidity;with increase of aging time,the effects of temperature and humidity are enhanced to different degrees,and the effect of temperature is dominant.The temperature and humidity interaction changes from significant to insignificant.