Comparison on surface properties and desulfurization of MnO2 and pyrolusite blended activated carbon by steam activation

In this study, MnO₂ and pyrolusite were used as the catalysts to prepare modified activated carbon, that is, AC-Mn and AC-P, respectively, from coals by blending method and steam activation. The Brunauer–Emmett–Teller (BET) results indicated that the AC-P had higher surface areas and micropore volumes than the AC-Mn with the same blending ratio. The relative contents of basic functional groups (i.e., C = O, π-π*) on AC-P were slightly lower than those on AC-Mn, while both contained the same main metal species, namely, MnO. The desulfurization results showed that with 3 wt% of blending ratio, AC-Mn3 and AC-P3 had higher sulfur capacities at 220 and 205 mg/g, respectively, which were much higher than for the blank one (149.6 mg/g). Moreover, the AC-P had relatively higher sulfur capacity than the AC-Mn with the same contents of Mn, which might be attributed to the existence of other metals in pyrolusite. After the desulfurization process, MnO were gradually transferred into MnSO₄, and the relative contents of basic functional groups decreased evidently for both AC-Mn3 and AC-P3. The results demonstrated that pyrolusite could be one good alternative to MnO₂ to prepare modified activated carbon for desulfurization.

Implications: MnO₂ and pyrolusite were used as the additives to prepare modified activated carbon from coals by a blending method and by steam activation, that is, AC-Mn and AC-P, respectively. The AC-P had higher surface areas and micropore volumes than the AC-Mn with the same blending ratio. The AC-Mn and AC-P had higher sulfur capacities than a blank one. Moreover, the AC-P had relatively higher sulfur capacity than the AC-Mn with the same contents of Mn. The results demonstrated that pyrolusite could be one good alternative to MnO₂ to prepare modified activated carbon for desulfurizatio.