| 氧化铝厂蒸发器发生应力腐蚀的原因分析与防治 |
| |
| 引用本文： | 时淑宏. 氧化铝厂蒸发器发生应力腐蚀的原因分析与防治[J]. 工业安全与环保, 2001, 27(9): 15-18 |
| |
| 作者姓名： | 时淑宏 |
| |
| 作者单位： | 中国长城铝业公司 |
| |
| 摘 要： | 对氧化铝厂蒸发器发生应力腐蚀的危害性作了介绍 ,描述了应力腐蚀裂纹的特征 ;对应力腐蚀产生的原因进行了分析 ,并提出了防治措施
|
| 关 键 词： | 材质 介质 应力 应力腐蚀 裂纹 |
| 修稿时间： | 2001-05-24 |
Analysis of causes and prevention of stress corrosion of evaporator at alumina plant |
| |
| Shi Shuhong. Analysis of causes and prevention of stress corrosion of evaporator at alumina plant[J]. Industrial Safety and Dust Control, 2001, 27(9): 15-18 |
| |
| Authors: | Shi Shuhong |
| |
| Abstract: | The paper has introduced the harmfulness of stress corrosion of evaporator at alumina plant and described the features of stress corrosive cracks. The analysis of causes has been made and the preventive measures have been put forward. |
| |
| Keywords: | material medium stress stress corrosion crack |