| 蒙脱土/聚丙烯酰胺杂化絮凝剂制备及絮凝性能研究 |
| |
| 引用本文： | 董永全,邓安民,郭桦冰,唐星华. 蒙脱土/聚丙烯酰胺杂化絮凝剂制备及絮凝性能研究[J]. 环境科学学报, 2009, 29(11): 2385-2392 |
| |
| 作者姓名： | 董永全 邓安民 郭桦冰 唐星华 |
| |
| 作者单位： | 南昌航空大学环境与化学工程学院,南昌330063,南昌航空大学环境与化学工程学院,南昌330063,南昌航空大学环境与化学工程学院,南昌330063,南昌航空大学环境与化学工程学院,南昌330063 |
| |
| 基金项目： | 国家自然科学基金(No.20866007)；江西省教育厅项目(No.GJJ09488)；南昌市重点科技攻关项目(No.DA200902109) |
| |
| 摘 要： | 利用十六烷基三甲基溴化铵(CTAB)与钠基蒙脱土(Na-MMT)的阳离子交换反应制得有机化蒙脱土(O-MMT)，通过硝酸铈铵引发丙烯酰胺单体在有机化蒙脱土片层间原位插层聚合制得蒙脱土/聚丙烯酰胺(MMT/PAM)杂化物. 同时，研究了引发剂用量、聚合反应时间和蒙脱土含量对杂化物特性粘数的影响，并用XRD、FTIR、TEM对Na-MMT、O-MMT和MMT/PAM杂化物进行结构表征. 最后实验对比了MMT/PAM杂化物与PAM对三氧化二铬悬浮液的絮凝效果. XRD、TEM结果显示，纳米尺寸大小的蒙脱土均匀地分散在PAM基体中. 絮凝实验结果显示，添加质量分数0.5％~5.0％MMT的MMT/PAM杂化物的絮凝效果优于纯PAM.
|
| 关 键 词： | 无机-有机杂化 絮凝剂 聚丙烯酰胺 蒙脱土 |
| 收稿时间： | 2009-02-20 |
| 修稿时间： | 2009-06-21 |
Preparation and flocculation performance of a polyacrylamide/montmorilonite hybrid flocculant |
| |
| DONG Yongquan,DENG Anmin,GUO Huabing and TANG Xinghua. Preparation and flocculation performance of a polyacrylamide/montmorilonite hybrid flocculant[J]. Acta Scientiae Circumstantiae, 2009, 29(11): 2385-2392 |
| |
| Authors: | DONG Yongquan DENG Anmin GUO Huabing TANG Xinghua |
| |
| Affiliation: | College of Environmental & Chemical Engineering Nanchang Hangkong University, Nanchang 330063,College of Environmental & Chemical Engineering Nanchang Hangkong University, Nanchang 330063,College of Environmental & Chemical Engineering Nanchang Hangkong University, Nanchang 330063 and College of Environmental & Chemical Engineering Nanchang Hangkong University, Nanchang 330063 |
| |
| Abstract: | Organophilic-montmorillonite (O-MMT) was prepared by a eation exchange reaction between inorganic ions of montmorillonite and annmonium cations of cetyl trimethyl ammonium bromide ( CTAB ). Montmorilonite/polyacrylamide ( MMT/PAM ) hybrid was then prepared via intercalation polymerization of acrylamide among the lamellae of O-MMT initiated by cerium ammonium nitrate, ( NH_4 )_2Ce( NO_3 )_6. The effects of initiator dosage, polymerization time and MMT content on the intrinsic viscosity of the MMT/PAM hybrid were investigated. The structures of Na-MMT,O-MMT and MMT/ PAM hybrid were characterized by means of X-ray diffraction ( XRD) ., FTIR, transmission electron microscopy (TEM) , and the flocculating effects of MMT/PAM hybrid and pure PAM on chromium trioxide suspension were compared. The results showed that nano-sized MMT was dispersed evenly in the polyaciylamide matrix, and the flocculating effect of MMT/PAM hybrid was better than that of pure PAM for 0. 5% chromium trioxide suspension when the MMT content was kept at 0.5%～5.0%. |
| |
| Keywords: | inorganic-organic hybrid flocculant polyaciylamide montmorilonite |