Study on Photocatalytic Oxidation of Micro Acetone by Nano-TiO2 |
|
| XU Hong-juan,LIU Jian-zhou,JIANG Jing-liang,LU Fu-sheng,WU Jie,CHEN Juan,ZHUANG Ying,LIU Tao,XU Zheng-xin,DAI Xin-lian,TONG Min-ming. Study on Photocatalytic Oxidation of Micro Acetone by Nano-TiO2[J]. Jiangsu Environmental Science and Technology, 2008, 21(6): 17-19 | |
| Authors: | XU Hong-juan LIU Jian-zhou JIANG Jing-liang LU Fu-sheng WU Jie CHEN Juan ZHUANG Ying LIU Tao XU Zheng-xin DAI Xin-lian TONG Min-ming |
| Affiliation: | XU Hong-juan, LIU Jian-zhou, JIANG Jing-liang, LU Fu-sheng, WU Jie, CHEN Juan, ZHUANG Ying, LIU Tao, XU Zheng-xin, DAI Xin-lian, TONG Min-ming |
| Abstract: | The nano-TiO2 films were prepared with sol-gel method. The photocatalytic oxidation reaction performances of these photocatalysts in the micro acetone mixed with air were tested. The catalyst samples were characterized by TG, XRD and TEM etc, and the effect of preparation conditions on their structure and reaction activities were studied, and the photocatalytic oxidation mechanism were explored. The results showed that the average particle diameter of these photocatalysts was 20 nm. The nano-TiO2 films calcined at 550 ℃ had two crystal phases, anatase and rutile. When the content of the rutile was 13.6 %, the nano--TiO2 photocatalysts had better activity, and the conversion of acetone was 45.26 %. |