Photocatalytic decomposition of acrylonitrile with N–F codoped TiO2/SiO2 under simulant solar light irradiation

The solid acid catalyst, N–F codoped TiO₂/SiO₂ composite oxide was prepared by a sol–gel method using NH₄F as nitrogen and fluorine source. The prepared materials were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), UV–Visible diffuse reflectance spectroscopy (UV–Vis), ammonia adsorption and temperature-programmed desorption (NH₃-TPD), in situ Fourier transform infrared spectroscopy (FT-IR) and N₂ physical adsorption isotherm. The photocatalytic activity of the catalyst for acrylonitrile degradation was investigated under simulant solar irradiation. The results showed that strong Lewis and Brønsted acid sites appear on the surface of the sample after N–F doping. Systematic investigation showed that the highest photocatalytic activity for acrylonitrile degradation was obtained for samples calcined at 450°C with molar ratio (NH₄F to Ti) of 0.8. The degradation ratio of 71.5% was achieved with the prepared catalyst after 6-min irradiation, demonstrating the effectiveness of photocatalytic degradation of acrylonitrile with N–F codoped TiO₂/SiO₂ composite oxide. The photocatalyst is promising for application under solar light irradiation. Moreover, the intermediates generated after irradiation were verified by gas chromatography–mass spectrometry (GC–MS) analysis and UV–Vis spectroscopy to be simple organic acids with lower toxicity, and the degradation pathway was also proposed for acrylonitrile degradation with the prepared catalyst.     

Effect of MoO3 on vanadium based catalysts for the selective catalytic reduction of NOx with NH3 at low temperature

The selective catalytic reduction(SCR) activities of the MoO_3 doped V/WTi catalysts prepared by the incipient wetness impregnation method at low temperature were investigated.The results showed that the addition of MoO_3 could enhance the NO_ xconversion at low temperature and the best SCR activity was obtained when the dosage of MoO_3 reached5 wt.%. The NH3-TPD and DRIFTS experiments indicated that the addition of MoO_3 changed the type and number of acid sites on the surface of catalysts and reaction activities of acid sites were altered at the same time. The redox capacity and amount of active oxygen species got improved for V3Mo5/WTi catalyst, which could be confirmed by the H_2-TPR and transient response experiments. Water vapor inhibited the NO_xconversion at low temperature. Deposition of ammonium sulfate or bisulfate might be main reason for the loss of catalytic activity in the presence of SO_2 at low temperature. Choosing the suitable NH_3/NO ratio and elevation of reaction temperature both could weaken the influence of SO_2 on the SCR activity of the V3Mo5/WTi catalyst. Thermal treatment of the deactivated catalyst at350°C could get the low temperature activity recovered. The decrease of GHSV improved the de NO_x efficiency at low temperature and we speculated that the rational technological process and operation parameters could contribute to the application of this kind of catalysts in real industrial environment.     

Effect of Cu loading content on the catalytic performance of Cu-USY catalysts for selective catalytic reduction of NO with NH3

Series of Cu-USY zeolite catalyst with different Cu loading content were synthesized through simple impregnation method. The obtained catalysts were subjected to selective catalytic reduction of NO_x with NH₃ (NH₃-SCR) performance evaluation, structural/chemical characterizations such as X-ray diffraction (XRD), N₂ adsorption/desorption, H₂ temperature-programmed reduction (H₂-TPR), NH₃ temperature-programmed desorption (NH₃-TPD) as well as detailed in situ diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) experiments including CO adsorption, NH₃ adsorption and NO+O₂ in situ reactions. Results show that Cu-USY with proper Cu loading (in this work 5Cu-USY with 5 wt.% Cu) could be promising candidates with highly efficient NH₃-SCR catalytic performance, relatively low byproduct formation and excellent hydrothermal stability, although its SO₂ poisoning tolerability needs alleviation. Further characterizations reveal that such catalytic advantages can be attributed to both active cu species and surface acid centers evolution modulated by Cu loading. On one hand, Cu species in the super cages of zeolites increases with higher Cu content and being more conducive for NH₃-SCR reactivity. On the other hand, higher Cu loading leads to depletion of Brønsted acid centers and simultaneous formation of abundant Lewis acid centers, which facilitates NH₄NO₃ reduction via NH₃ adsorbed on Lewis acid centers, thus improving SCR reactivity. However, Cu over-introduction leads to formation of surface highly dispersed CuO_x, causing unfavorable NH₃ oxidation and inferior N₂ selectivity.     

Interactions of sulfuric acid with common atmospheric bases and organic acids: Thermodynamics and implications to new particle formation

Interactions of the three common atmospheric bases, dimethylamine ((CH₃)₂NH), methylamine (CH₃NH₂), ammonia (NH₃), all considered to be efficient stabilizers of binary clusters in the Earth's atmosphere, with H₂SO₄, the key atmospheric precursor, and 14 common atmospheric organic acids (COAs) (formic, acetic, oxalic, malonic, succinic, glutaric acid, adipic, benzoic, phenylacetic, pyruvic, maleic acid, malic, tartaric and pinonic acids) have been studied using the density functional theory (DFT) and composite high-accuracy G3MP2 method. The thermodynamic stability of mixed (COA)(H₂SO₄), (COA)(B1), (COA)(B2) and (COA)(B3) dimers and (COA)(H₂SO₄)(B1), (COA)(H₂SO₄)(B2) and (COA)(H₂SO₄)(B3) trimers, where B1, B2 and B3 refer to (CH₃)₂NH, CH₃NH₂ and NH₃, respectively, have been investigated and their impacts on the thermodynamic stability of clusters containing H₂SO₄ have been studied. Our investigation shows that interactions of H₂SO₄ with COA, (CH₃)₂NH, CH₃NH₂ and NH₃ lead to the formation of more stable mixed dimers and trimers than (H₂SO₄)₂ and (H₂SO₄)₂(base), respectively, and emphasize the importance of common organic species for early stages of atmospheric nucleation. We also show that although amines are generally confirmed to be more active than NH₃ as stabilizers of binary clusters, in some cases mixed trimers containing NH₃ are more stable thermodynamically than those containing CH₃NH₂. This study indicates an important role of COA, which coexist and interact with that H₂SO₄ and common atmospheric bases in the Earth atmosphere, in formation of stable pre-nucleation clusters and suggests that the impacts of COA on new particle formation (NPF) should be studied in further details.     

Fe2O3添加对钛基SCR催化剂表面硫酸氢铵分解行为的影响规律

采用共沉淀法合成了TiO_2及TiO_2-Fe_2O_3载体,并对硫酸氢铵与上述载体之间的相互作用及硫酸氢铵的具体分解行为进行了研究.结果表明,催化剂载体表面含硫官能团主要以双齿硫酸盐的形式存在,含氮官能团以铵根离子的形式存在.当硫酸氢铵沉积于催化剂载体表面时,由于硫酸根离子具有较强的电负性,Ti原子及Fe原子处于电子缺失状态.对于TiO_2载体,硫酸根离子主要与Ti原子相连;而对于TiO_2-Fe_2O_3载体,Ti原子及Fe原子均为硫酸根离子主要的附着位点.采用热分析方法及原位红外对硫酸氢铵在TiO_2及TiO_2-Fe_2O_3载体表面的分解行为进行了研究,发现铁氧化物的添加显著促进了硫酸氢铵在低温区间内的分解行为;与铵根离子相比,硫酸根离子具有更高的热稳定性.催化剂稳定性测试结果表明,铁氧化物的添加显著提高了低温抗硫抗水性能,为实现低温SCR技术的工业应用提供了理论基础.     

硅铝比和NiO对ZSM-5协同低温等离子体降解甲苯的影响

研究了不同硅铝比的ZSM-5与Ni/ZSM-5分子筛协同低温等离子体技术对甲苯降解性能的影响.以Ni O(Nickel Oxide)为活性组分,采用浸渍法对ZSM-5分子筛进行改性,利用氮气吸附脱附(BET)、X射线衍射仪(XRD)、X射线光电子能谱分析(XPS)、H_2程序升温还原(H_2-TPR)、NH_3程序升温脱附(NH_3-TPD)、Toluene程序升温脱附(Toluene-TPD)等技术表征样品的物理化学性质.考察了硅铝比对ZSM-5与Ni/ZSM-5分子筛体系中甲苯的吸附性能,研究了不同放电电压下硅铝比对甲苯降解率、碳平衡及二氧化碳选择性的影响,并采用气相色谱-质谱联用仪(GC-MS)分析了催化剂表面的有机产物.结果表明:硅铝比不但影响分子筛本身的物理化学特性(比表面积、氧化还原性能、表面酸性、疏水性等),还会影响Ni的负载形态和方式,更高的硅铝比与Ni O的负载能促进甲苯深度氧化,减少副产物,提高碳平衡和二氧化碳选择性.     

Remarkable promotion effect of trace sulfation on OMS-2 nanorod catalysts for the catalytic combustion of ethanol

OMS-2 nanorod catalysts were synthesized by a hydrothermal redox reaction method using MnSO₄ (OMS-2-SO₄) and Mn(CH₃COO)₂ (OMS-2-AC) as precursors. SO₄^2 −-doped OMS-2-AC catalysts with different SO₄^2 − concentrations were prepared next by adding (NH₄)₂SO₄ solution into OMS-2-AC samples to investigate the effect of the anion SO₄^2 − on the OMS-2-AC catalyst. All catalysts were then tested for the catalytic oxidation of ethanol. The OMS-2-SO₄ catalyst synthesized demonstrated much better activity than OMS-2-AC. The SO₄^2 − doping greatly influenced the activity of the OMS-2-AC catalyst, with a dramatic promotion of activity for suitable concentration of SO₄^2 − (SO₄/catalyst = 0.5% W/W). The samples were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), inductively coupled plasma optical emission spectroscopy (ICP-OES), NH₃-TPD and H₂-TPR techniques. The results showed that the presence of a suitable amount of SO₄^2 − species in the OMS-2-AC catalyst could decrease the Mn–O bond strength and also enhance the lattice oxygen and acid site concentrations, which then effectively promoted the catalytic activity of OMS-2-AC toward ethanol oxidation. Thus it was confirmed that the better catalytic performance of OMS-2-SO₄ compared to OMS-2-AC is due to the presence of some residual SO₄^2 − species in OMS-2-SO₄ samples.     

Density functional theory (DFT) studies of vanadium-titanium based selective catalytic reduction (SCR) catalysts

Based on density functional theory (DFT) and basic structure models, the chemical reactions on the surface of vanadium-titanium based selective catalytic reduction (SCR) denitrification catalysts were summarized. Reasonable structural models (non-periodic and periodic structural models) are the basis of density functional calculations. A periodic structure model was more appropriate to represent the catalyst surface, and its theoretical calculation results were more comparable with the experimental results than a non-periodic model. It is generally believed that the SCR mechanism where NH₃ and NO react to produce N₂ and H₂O follows an Eley-Rideal type mechanism. NH₂NO was found to be an important intermediate in the SCR reaction, with multiple production routes. Simultaneously, the effects of H₂O, SO₂ and metal on SCR catalysts were also summarized.     

Effects of WOx modification on the activity, adsorption and redox properties of CeO2 catalyst for NOx reduction with ammonia

A series of WO₃/CeO₂ (WOx/CeO₂) catalysts were synthesized by wet impregnation of ammonium metatungstate on a CeO₂ support. The resulting solid acid catalysts were characterized by X-ray diffraction (XRD), UV-Vis spectroscopy (UV-Vis), Raman spectroscopy (Raman), in-situ Fourier transform infrared spectroscopy (in-situ FT-IR) of ammonia adsorption, NH₃-TPD, H₂ temperature-programmed reduction (H₂-TPR), NH₃/NO oxidation and activity measurements for NOx reduction by NH₃ (NH₃-SCR). The results show that polytungstate (WOx) species are the main species of tungsten oxide on the surface of ceria. The addition of tungsten oxide enhances the Brönsted acidity of ceria catalysts remarkably and decreases the amount of surface oxygen on ceria, with strong interaction between CeO₂ and WOx. As a result, the N₂ selectivity of NH₃ oxidation and NH₃-SCR at high temperatures (> 300℃) is enhanced. Therefore, a wide working temperature window in which NOx conversion exceeds 80% (NOx conversion > 80%) from 200 to 450℃, is achieved over 10 wt.% WOx/CeO₂ catalyst. A tentative model of the NH₃-SCR reaction route on WOx/CeO₂ catalysts is presented.     

Fe2O3 particles as superior catalysts for low temperature selective catalytic reduction of NO with NH3

Fe203 particle catalysts were experimentally studied in the low temperature selective catalytic reduction （SCR） of NO with NH3. The effects of reaction temperature, oxygen concentration, [NH3]/[NO] molar ratio and residence time on SCR activity were studied. It was found that Fe203 catalysts had high activity for the SCR of NO with NH3 in a broad temperature range of 150-270℃, and more than 95% NO conversion was obtained at 180℃ when the molar ratio [NH3]/[NO] = 1, the residence time was 0.48 seconds and 02 volume fraction was 3%. In addition, the effect of SO2 on SCR catalytic activity was also investigated at the temperature of 180℃. The results showed that deactivation of the Fe2O3 particles occurred due to the presence of SO2 and the NO conversion decreased from 99.2% to 58% in 240 min, since SO2 gradually decreased the catalytic activity of the catalysts. In addition, X-ray diffraction, Thermogravimetric analysis and Fourier transform infrared spectroscopy were used to characterize the fresh and deactivated Fe2O3 catalysts. The results showed that the deactivation caused by SO2 was due to the formation of metal sulfates and ammonium sulfates on the catalyst surface during the de-NO reaction, which could cause pore plugging and result in suppression of the catalytic activity.     

酸碱改性活性炭及其对甲苯吸附的影响

分别用酸溶液(H_2SO_4、HNO_3、H_3PO_4)和碱溶液(NaOH或NH_3·H_2O)浸渍方法对活性炭进行改性,并对酸改性活性炭进行碱溶液二次改性处理,通过表征改性前后活性炭BET比表面积、孔结构、表面官能团等理化特征和测定其对甲苯蒸气的饱和吸附量,研究了影响活性炭吸附甲苯蒸气的关键因素.结果表明,酸改性使BET比表面积、微孔面积、微孔容积减少、表面酸性官能团增加,而碱改性呈现相反的理化特征变化.活性炭理化特征的变化可能与改性溶液的酸碱性、氧化还原性有关,并且这种相反的变化直接关系到活性炭对甲苯蒸气的吸附.3种酸改性的活性炭对甲苯蒸气饱和吸附量相对于原活性炭减少9.6%~20.0%,而两种碱改性的活性炭则增加29.2%~39.2%.相关性分析显示甲苯吸附量与BET比表面积、微孔面积、微孔容积正相关,而与表面酸性官能团负相关;多元回归分析进一步表明微孔容积和酸性官能团数量是影响活性炭甲苯吸附的关键因素.二次改性活性炭甲苯吸附量与表面含氧酸性官能团拟合结果则表明,—COOH、C＝O和—OH都对活性炭甲苯吸附能力有影响,其中—COOH影响较大.研究结果表明有效提高活性炭对甲苯吸附能力,改性宜以提高活性炭微孔容积和减小活性炭表面酸性官能团数量,特别是—COOH数量为目标导向.     

SO2对MnOx/PG催化剂低温脱硝的影响机理研究

采用等体积浸渍法制备了锰氧化物负载凹凸棒石(MnO_x/PG)低温SCR催化剂,通过SO₂暂态响应、程序升温表面反应(TPSR)等实验技术研究了烟气中SO₂对催化剂SCR脱硝活性的影响行为.采用程序升温脱附(TPD)、BET比表面及孔径分布测定、XPS等表征技术对催化剂硫中毒的机理及化学本质进行了深入分析.结果表明,低温下烟气中SO₂对MnO_x/PG催化剂的SCR脱硝活性存在显著的抑制作用,催化剂中毒主要由烟气中SO₂的催化氧化引起.一方面SO₂氧化为SO₃后与NH₃及H₂O竞争反应形成复杂的硫酸铵盐堵塞催化剂孔道,另一方面与活性组分MnO₂结合形成MnSO₄使得部分活性组分形态发生变迁.其中硫酸铵盐的形成可通过适当的热处理得以去除,而MnSO₄则不可恢复,但催化剂SCR活性却显著增加,表明MnSO₄的形成不是催化剂失活的主要因素.吸附态的硫可显著增加催化剂表面酸性,因此对SCR活性有促进作用.催化剂失活主要机理为:由气相SO₂的连续氧化并与NH₃相结合形成硫酸铵盐,并且在低温下难以分解,以致堵塞催化剂活性中心.     

Effect of preparation methods on the performance of CuFe-SSZ-13 catalysts for selective catalytic reduction of NOx with NH3

CuFe-SSZ-13 catalyst showed excellent performance in the selective catalytic reduction of NO_x with NH₃ (NH₃-SCR) for diesel engine exhaust purification. To investigate the effect of preparation methods on NH₃-SCR performance, Fe was loaded into one-pot synthesized Cu-SSZ-13 catalysts through solid-state ion-exchange (SSIE), homogeneous deposition precipitation (HDP) and liquid ion-exchange (IE), respectively. Three CuFe-SSZ-13 catalysts showed similar SO₂ resistance, which was better than that of Cu-SSZ-13. The improvement was attributed to the protection of Fe species. Hydrothermal stability of three CuFe-SSZ-13 catalysts was significantly different, which was attributed to the state of active species caused by different preparation methods. Compared with the other two catalysts, more active species existed inside the zeolite pores of CuFe-SSZ-13_SSIE. During hydrothermal aging, the aggregation of these active species in the pores caused the collapse of catalyst structure, ultimately leading to the deactivation of CuFe-SSZ-13_SSIE. In contrast, Fe species was dispersed better on the surface over CuFe-SSZ-13_IE, enhancing the hydrothermal stability of catalysts. Consequently, Fe loading effectively improved the resistance of SO₂ and H₂O over Cu-SSZ-13. For CuFe-SSZ-13, large amounts of active species located inside the zeolite pores are not beneficial for the hydrothermal stability.     

Novel CeO2@TiO2 core–shell nanostructure catalyst for selective catalytic reduction of NOx with NH3

The CeO₂@TiO₂ core–shell nanostructure catalyst prepared by a two-step hydrothermal method was used for selective catalytic reduction (SCR) of NOx with NH₃ in this study. The catalyst presented the obvious core–shell structure, and the shell was amorphous TiO₂ which could protect the active center from the SO₂ erosion. The catalyst showed high activity and stability, excellent N₂ selectivity and superior SO₂ resistance and H₂O tolerance. Characterizations such as TEM, HR-TEM, XRD, BET, XPS, NH₃-TPD, and H₂-TPR were carried out. The results indicated that the catalyst had large surface area and the active sites were well dispersed on the surface. The NH₃-TPD, H₂-TPR and XPS results implied that its increased SCR activity might be due to the enhancement of NH₃ chemisorption and the increase of active oxygen species, both of which were conductive to NH₃ activation. The excellent catalytic performance suggests that it is a promising candidate for SCR catalyst.     

SO2对Mn-Cu-Ce/TiO2低温选择催化还原NO的影响

研究了SO2对Mn-Cu-Ce/TiO2选择催化还原 NO 的影响,并采用傅立叶变换红外光谱、x射线衍射光谱及暂态响应技术对Mn-Cu-Ce/TiO2催化剂的SO2中毒机理进行了探讨.结果表明,SO2 可强吸附在Mn-Cu-Ce/TiO2表面的 CuO 活性位上.并生成 CuSO4,由于 CuSO4 在低温时对SCR 反应有抑制作用,因而,催化剂的活性下降;暂态响应实验结果表明,Mn-Cu-Ce/TiO2催化剂上的SCR反应主要遵循 Langmuir-Hinshelwood机理.通过对催化剂进行硫酸化或 NO 预吸附,可以消除SO2对 Mn-Cu-Ce/TiO2的毒害作用.     

Investigation of the common intermediates over Fe-ZSM-5 in NH3-SCR reaction at low temperature by in situ DRIFTS

The surface species formed in the reaction of NO and NO₂ with pre-adsorbed NH₃ over a Fe-ZSM-5 catalyst (1.27 wt.% Fe, SiO₂/Al₂O₃ = 25) at low temperature (140°C) were studied by in situ diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS). Through using a background spectrum of NH₃-saturated Fe-ZSM-5, we clearly observed the formation of common intermediates resulting from the reaction of NO₂ or NO + O₂ with pre-adsorbed NH₃. This presents strong evidence that the oxidation of NO to form surface nitrates and nitrites is the key step for standard SCR at low temperature. In addition, the results suggest that in the SCR reaction at low temperature, the NH₄⁺ ions absorbed on Brønsted acid sites are less active than NH₃ adsorbed on Lewis acid sites related to Fe species.     

Ultrasound-assistant preparation of Cu-SAPO-34 nanocatalyst for selective catalytic reduction of NO by NH3

The influence of the various preparation methods of Cu-SAPO-34 nanocatalysts on the selective catalytic reduction of NO with NH₃ under excess oxygen was studied. Cu-SAPO-34 nanocatalysts were prepared by using four techniques: conventional impregnation (IM), ultrasound-enhanced impregnation (UIM), conventional deposition precipitation (DP) using NaOH and homogeneous deposition precipitation (HDP) using urea. These catalysts were characterized in detail by various techniques such as N₂-sorption, XRD, TEM, H₂-TPR, NH₃-TPD and XPS to understand the catalyst structure, the nature and the dispersed state of the copper species, and the acid sites for NH₃ adsorption. All of the nanocatalysts showed high activities for NO removal. However, the activities were different and followed the sequence of Cu-SAPO-34 (UIM) > Cu-SAPO-34 (HDP) > Cu-SAPO-34 (IM) > Cu-SAPO-34 (DP). Based on the obtained results, it was concluded that the NO conversion on Cu-SAPO-34 nanocatalysts was mainly related to the high reducibility of the isolated Cu^2 + ions and CuO species, the number of the acid sites and the dispersion of CuO species on SAPO-34.     

冶炼厂SO2烟气化学催化吸收扩大试验研究

在单层塔板泡沫吸收塔中的ＳＯ２液相催化氧化进行了扩在试验研究,当ＳＯ２净化效率（单板效率）为５０％时,得到１６％（Ｗｔ）Ｈ２ＳＯ４,硫酸生成速率为１８％／ｈ,ＳＯ２吸收最佳敢化５Ｌ／Ｎｍ＾３,添加表面活性剂Ａｌ２（ＳＯ４）３及鼓氧操作对ＳＯ２液相催化氧化有明显促进作用,冶炼烟气ＳＯ２浓度波动吸收效率影响不大。     

Speciation of ammonium-containing species in atmospheric aerosols

A method for the speciation and separate determination of inorganic ammonium salts in atmospheric aerosols has been developed. It is based on sampling by an annular denuder-filter-pack system, in order to avoid chemical artifacts followed by thermal dissociation of NH₄NO₃ and NH₄Cl from the Teflon pre-filter, and collection of evolved gases on back-up filters. The predominant form of thermostable sulfate partially or totally neutralized by NH₃ is then identified and quantified from pH and [H⁺]/[SO₄²⁻] ratio measurements. Results of field experiments performed near Rome show that NH₄NO₃ and (NH₄)₂SO₄ constitute the major species of the fine particle fraction.NH₄Cl represents approximately one-fifth of NH₄NO₃ and one-tenth of the total ammonium species in terms of mass concentration.     

邯郸市PM_(2.5)中水溶性无机离子污染特征及来源解析

本研究通过对邯郸市环境空气中PM2.5样本进行采集和成分检测,分析了该地区PM2.5中水溶性无机离子的污染特征,并结合气象要素(风速、温度)、气态污染物(O3、NO2、SO2、CO)、SOR(硫氧化率)、NOR(氮氧化率)对其主要来源进行了解析.研究结果表明:总水溶性无机离子(TWSII)浓度季节变化特征明显,秋、冬季高于春、夏季.SO2-4、NO-3、NH+4是PM2.5中主要的水溶性无机离子,在TWSII中所占的比例为夏(93.2%)冬(85.6%)秋(85.5%)春(84.0%).春、夏、秋三季PM2.5呈酸性,冬季显碱性.此外还分析得到,SO2-4在四季中均以(NH4)2SO4的形式存在.NO-3在冬季以NH4NO3的形式存在,其余季节中以NH4NO3、HNO3等共存.绝大部分Cl-在冬季以NH4Cl的形式存在,其它季节中以NH4Cl、KCl等的形式存在.均相反应是SO2-4的主要生成途径,夏、冬季也伴随有非均相反应.NO-3的生成以均相反应为主(春、夏、秋),在冬季均相反应与非均相反应同时存在.应用因子分析法解析出4个主因子,其中,工业、燃煤、交通、生物质燃烧等综合源是PM2.5中水溶性无机离子的主要来源.