固体浓度对污染底泥中重金属生物沥浸去除效果的影响

采用序批式摇床,研究了固体浓度为3%~13%的底泥浓度对生物沥浸法去除污染底泥中重金属(Zn、Cu和Cr)的影响.结果表明,随着固体浓度增加,底泥pH值下降和ORP上升速率减缓,重金属的沥浸去除速率相应降低;沥浸过程中,当底泥pH值由5.0降至2.0,ORP由200 mV升至520 mV时,重金属的去除率增加最为迅速;不同浓度的处理,沥浸12 d,Zn、Cu和Cr的去除率分别为60%~85%、65%~100%和17%~35%.试验发现,底泥沥浸中pH值随时间的变化符合Boltzmann方程,此方程可估算底泥酸化进程.连续提取法对脱毒(沥浸)底泥中残留Zn、Cu和Cr的形态分级显示,底泥中未沥浸去除的重金属绝大部分以残渣态存在,环境风险较低.从经济角度考虑,固体浓度10%在底泥沥浸的实际应用中较为合适.     

生物沥浸对自然干化污泥重金属去除效果研究

重金属的去除是污泥农用需要解决的关键问题之一.本研究采用摇瓶实验,将氧化硫硫杆菌为功能微生物的生物沥浸技术应用于干化污泥重金属的去除,对山西省不同污水处理厂11个干化污泥样品进行了为期15 d的生物沥浸处理.分析了生物沥浸体系p H及SO2-4的变化情况,并对生物沥浸前后污泥中Cu、Zn、As、Cd、Cr等重金属去除率及有机质、全氮、全磷、全钾等养分的损失率进行了分析.结果表明,干污泥直接进行生物沥浸过程较为缓慢,无机酸对体系的酸化能够快速启动干化污泥的生物沥浸过程.无机酸酸化后,体系S0的生物氧化率逐渐提高,酸化速率加快,且污泥重金属去除率随着p H的降低而提高,生物沥浸过程结束后,供试污泥样品Cu、Zn、As、Cd和Cr的去除率分别为23.69%~77.62%、89.67%~97.80%、30.24%~84.31%、18.18%~97.05%和28.55%~67.11%,而污泥有机质、全氮、全磷和全钾的含量损失率分别为3%、1%、44%和8%,污泥剩余养分含量满足农用泥质标准(CJ/T309-2009)的限定值.Cu、Zn、As、Cd和Cr去除率与污泥有机质含量呈显著负相关关系(r=0.935、0.895、0.932、0.516、0.847,n=11).     

生物沥浸去除污泥重金属及改善脱水性能研究

从天然矿山酸性废水中富集制备了3种嗜酸性细菌混培物,开展了污泥生物沥浸实验,研究了沥浸去除污泥重金属(Cu、Zn、Cd)同时改善脱水性能的效果.结果表明,3种嗜酸性细菌混培物均可有效去除污泥中的重金属(P<0.01).沥浸12d后,改进型Starkey培养基富集的嗜酸性细菌混培物对Cu和Cd的去除率分别达到82.0%和82.9%,9K培养基富集的嗜酸性细菌混培物进行生物沥浸处理对Zn的去除率可达到87.5%.同时,生物沥浸还可以显著改善污泥的脱水性能(P<0.01).经过12d沥浸,污泥的离心脱水率可由73.1%上升到90.0%.显微观察和能谱分析结果显示,污泥脱水性能的改善是因为生物沥浸能使污泥结构由絮体状变成明显的颗粒状,并可形成以铁、氧和硫为主要元素组成的次生矿物规则晶体.     

苏州河底泥中重金属的烧结无害化研究

采用有氧烧结法和还原烧结法处理苏州河底泥,研究了底泥中重金属的无害化效果.结果表明,有氧烧结温度900℃以上时,对Cu、Pb、Zn、Cd去除率达40%～65%;烧结温度为500～900℃时,尽管对Cu、Pb、Zn、Cd去除效果不明显,但能有效抑制其溶出.有氧烧结法不仅不能实现Cr的去除,而且会增加Cr的溶出,这是由于有氧烧结过程中Cr(III)被转化为Cr(VI),而底泥对Cr(VI)的吸附能力很有限.还原烧结法则能有效防止底泥中Cr(III)向Cr(VI)的转化,从而抑制包括Cr在内的重金属的溶出.     

生物沥浸法去除不同初始pH值猪粪中的重金属

试验研究了不同初始pH值下猪粪中Cu、Zn和Cd的生物沥浸效果,结果表明猪粪生物沥浸对初始pH值的要求并不严格,具有较广的适用范围。猪粪粪液即使在初始pH值为8的弱碱性条件下,其pH值也可随沥浸时间快速降低,生物沥浸12天降到1.37,Cu、Zn和Cd沥出率可达到90.76%、97.97%和80.45%。初始pH值对重金属的沥浸速率有一定影响,降低初始pH值可以缩短生物沥浸周期,重金属的沥浸周期受不同初始pH值的影响程度从大到小依次为:CuZnCd。初始pH值为5的猪粪粪液可以在9天内完成生物沥浸,Cu、Zn和Cd沥出率可达到93.83%、99.24%和70.98%     

生物沥浸预处理改善污泥脱水性能和去除重金属研究

通过生物沥浸预处理改善污泥脱水性能和去除其中的重金属,有利于降低后续污泥处理和处置过程中的成本和潜在的生态环境风险。以城市污水厂剩余污泥为研究对象,采用驯化所得的嗜酸性硫杆菌混合菌群为接种物,通过添加不同浓度的底物(FeSO4·7H2O)对污泥进行生物沥浸预处理试验,考察生物沥浸过程中污泥比阻(SRF值)和污泥中重金属含量的动态变化。结果表明:生物沥浸预处理可改善污泥的脱水性能并去除其中的重金属,污泥比阻降低率的变化范围为5.73%～79.53%,污泥中重金属去除率的变化范围为0.38%～90.84%,且底物浓度的改变对改善污泥脱水性能和提高污泥中重金属的去除率有一定的影响;当底物浓度为6g/L、生物沥浸5d时,可获得污泥最佳的脱水性能和污泥中重金属最佳的去除效果,在此条件下生物沥浸预处理后污泥的SRF值为0.52×1013 m/kg,污泥中重金属Zn、Cd、Cu、Ni、Pb和Cr的去除率分别为80.36%、76.89%、80.93%、86.04%、58.37%和58.52%。     

复合硫杆菌生物浸出污泥中重金属的效果及与pH和ORP的关系

利用复合嗜酸性硫杆菌(氧化硫硫杆菌和氧化亚铁硫杆菌)在不同接种量下(5%,10%,20%)对城市污泥进行生物沥浸,探讨了沥浸过程中不同重金属的浸出效果及其与pH值和氧化还原电位(ORP)的相关关系.结果表明,该方法能有效地浸出污泥中的重金属,生物沥浸处理10d后.污泥中Cu、Zn和Ni的浸出率可分别达到98%、99%和90%,硫杆菌接种量越大,沥浸反应速率越快,20%接种处理10%接种处理5%接种处理未接种处理.污泥生物沥浸过程中pH的下降和ORP的上升,是促进污泥重金属溶出的主要驱动力,但其中Cu的浸出同时受pH下降和ORP上升的双重影响,而zn和Ni的浸出则主要受pH影响.污泥中Cu、Zn和Ni开始大幅度浸出的pH阈值大约为4、5和5左右.研究还发现,生物沥浸处理虽可使污泥中有机质、全氮、全磷和全钾含量有所下降,但并不影响其农业利用价值.     

生物沥浸法去除猪粪中重金属和提高其脱水性能研究

采用复合嗜酸性硫杆菌,通过摇瓶试验研究了不同Fe2+添加量下生物沥浸对含固率为3%的猪粪中重金属的去除和脱水性能的影响.同时,考察了不间处理的pH、氧化还原电位(ORP)、Fe2+、Fe3+、总Fe、Cu、Zn、比阻和毛细吸水时间(CST)的变化.结果表明,采用生物沥浸技术能有效地去除猪粪中的重金属,随着Fe2+添加量...     

采用电动修复增强技术去除电镀污泥中重金属

为提高电动修复技术去除电镀污泥中的重金属(Cu, Pb, Zn , Cr, Ni)的效率,采用污泥预酸化处理及阴极pH值控制处理2种途径进行强化,反应过程中电压为32V,处理时间为7d,结果表明,电镀污泥酸化pH值至4.5时,污泥中重金属的可移动性明显提高了,依次为Cr>Ni>Zn>Cu>Pb;污泥预酸化加阴极pH值控制处理能使电镀污泥中Zn、Ni、Cu和Pb交换态、碳酸盐结合态和有机硫化物态转化为可溶离子态,转化量大小依次为Ni>Zn>Cu>Pb,且该处理Zn、Ni、Cu和Pb的去除率分别达到74.02%、68.38%、39.22%、21.37%;但污泥预酸化及阴极pH值控制处理都不利于Cr的去除,对照处理Cr去除率为77.83%,污泥预酸化处理去除率降为40.65%,污泥预酸化加阴极pH值控制处理降至12.80%.     

底泥调控剂对感潮河涌沉积物中重金属的影响

以典型的电器工业区重污染感潮河道——佛山市顺德区容桂街道内河涌为研究对象,选取一段河道,投加含硝酸钙的调控剂,采用BCR形态提取法研究调控剂对感潮河涌沉积物中重金属的影响,以评价调控剂对重金属的稳定化效果.结果表明,①调控剂使得重金属Cu、Zn、Pb和Cr的可还原态和可氧化态占总量的百分比降低;②调控剂能有效促进底泥中的重金属Cu、Zn、Pb和Cr向残渣态转化,投加调控剂处理22 d后,重金属Cu、Zn、Pb和Cr的残渣态占总量的质量分数分别升高了4%、20%、21%和23%,这在不同程度上降低了底泥Cu、Zn、Pb和Cr的可生物利用性;③调控剂能使Cu、Pb和Cr的弱酸提取态增加,而使Zn的弱酸提取态下降,即增加了Zn的稳定度而降低了Cu、Pb和Cr的稳定度.总体上,调控剂对底泥重金属Cu、Pb和Cr的稳定化效果并不理想,而对底泥重金属Zn有一定的稳定化效果,但效果不明显.     

Effect of sediment size on bioleaching of heavy metals from contaminated sediments of Izmir Inner Bay

The effect of sediment size on metals bioleaching from bay sediments was investigated by using fine (< 45 μm), medium (45-300 μm), and coarse (300-2000 μm) size fractions of a sediment sample contaminated with Cr, Cu, Pb, and Zn. Chemical speciation of the metals in bulk and size fractions of sediment were studied before and after bioleaching. Microbial activity was provided with mixed cultures of Acidithiobacillus thiooxidans and Acidithiobacillus ferrooxidans. The bioleaching process was carried out in flask experiments for 48 days, by using 5% (W/V) of solid concentration in suspension. Bioleaching was found to be efficient for the removal of selected heavy metals from every size fraction of sediments, where the experiments with the smaller particles resulted in the highest solubilization ratios. At the end of the experimental period, Cr, Cu, Pb and Zn were solubilized to the ratios of 68%, 88%, 72%, and 91% from the fine sediment, respectively. Higher removal efficiencies can be explained by the larger surface area provided by the smaller particles. The changes in the chemical forms of metals were determined and most of the metal releases were observed from the reducible and organic fractions independent from grain size. Higher concentrations were monitored in the residual fraction after bioleaching period, suggesting they are trapped in this fraction, and cannot be solubilized under natural conditions.     

黄铁矿与硫粉配合提高污泥重金属的淋滤效果

通过接种嗜酸性硫杆菌复合菌株(氧化亚铁硫杆菌与氧化硫硫杆菌)并采用序批式试验,研究了黄铁矿与硫粉2种底物配合使用对污泥中重金属生物淋滤效果的影响.结果表明,2种底物配合可加速污泥中重金属(Zn, Cu)的浸出,显著提高其去除率.经过18d的生物淋滤,在2种底物配合并接种的处理中,Zn和Cu的去除率分别可达89.2%,56.5%;而在单独加黄铁矿并接种的处理中两者的去除率分别为12.0%, 0.9%;单独添加硫粉并接种处理中分别为85.2%,37.6%,进一步验证了生物淋滤技术去除污泥中重金属的可行性.     

太湖北部小流域沉积物重金属污染特征与评价

近几十年来重金属的沉积记录、来源及污染水平受到了广泛关注.为探明太湖北部小流域重金属的污染来源和环境质量状况,本研究分析了柱状沉积物中8种重金属（Mn、Cr、Zn、Cu、As、Pb、Ni和Co）含量.运用主成分分析法判定污染源,富集因子法表征重金属富集特征,通过熵权模糊模型对沉积物中重金属污染状况进行评价.结果显示,所有重金属含量均较高,高低依次为Mn > Cr > Zn > Cu > As > Pb > Ni > Co.其中Mn含量最高,为380.06~767.69μg/g.沉积物重金属污染的主要贡献因子为交通排放、农业污染和煤炭燃烧.As的富集指数最大（2.89~15.61）.其中77.59%的沉积层属于显著富集,受人类活动影响最为显著.熵权模糊综合评价结果表明,Cu（0.483）和As（0.352）的权重值最大,是沉积物中的首要污染物,且65.52%的沉积层重金属含量处于中度污染水平.     

北江中上游底泥重金属污染及其潜在生态危害评价

为全面了解北江中上游底泥沉积物中重金属含量及其潜在生态危害程度,在北江干流及支流共采集了25个底泥样品,测试了Cu、Pb、Zn、Cd、Ni、Cr、As、Hg共8种重金属元素,采用地积累指数法和潜在生态危害指数法对北江中上游底泥重金属污染进行分析和评价.结果表明,北江中上游无论是干流还是支流其底泥受多种重金属污染而且污染程度相当严重,各种重金属的污染程度由强至弱依次为:Cd HgZnAsPb≈CuNiCr;金属污染物对北江中上游构成的潜在生态危害由强至弱依次为:Cd HgPb≈AsCuZnCr,其中Cd的影响占绝对主导地位.总体而言,北江干流由于纳污量最大,长期的积累使得北江干流段的重金属污染程度较支流严重;支流中马坝河的污染程度最高,其次是浈江和江.     

基于总量和形态的表层沉积物重金属污染及来源——以马鞍列岛海域为例

为了解马鞍列岛海域沉积物特征及重金属污染状况,于2017年6月采集了该海域表层沉积物样品,并对表层沉积物pH值、氧化还原电位（Eh）、粒度（D_[3,2]）等地球化学指标进行了同步原位调查,采用改进后的沉积物重金属形态分析的连续提取法（European Community Bureau of Reference （BCR））分析了7种重金属（Cr、As、Ni、Zn、Pb、Cu、Cd）各形态含量,并结合富集因子系数（EF）、地累积指数法（I_geo）等方法初步探索了马鞍列岛海域沉积物中重金属的污染特征及其来源.结果显示,马鞍列岛海域沉积物呈中性-弱碱性,属还原环境;近岛礁区以粉砾和粘粒为主,而远岛礁区以砂砾和粉砾为主;7种重金属总量均满足我国海洋沉积物质量I类标准;Cr、As、Ni以原生相为主,而Zn、Pb、Cu、Cd均以次生相为主;Cd以可交换态及碳酸盐结合态（F1）以及有机物及硫化物结合态（F3）为主要赋存形态,Zn、Pb、Cu以铁锰氧化物结合态（F2）为主要赋存形态,而Cr、As、Ni以残渣态为主要赋存形态;以Fe作为参比,7种重金属的富集程度顺序为Cd > Cu > Ni > Zn > Pb > Cr > As;通过空间污染状况分析发现,Cu、Cd在受人为活动影响较大的近岛礁区存在富集污染现象,其他重金属则主要表现为天然来源,除Ni外,Cu、Pb、Cd、As、Cr、Zn含量均呈近岛礁区>远岛礁区的空间分布特征.总体上,马鞍列岛国家级特别海洋保护区沉积物重金属污染程度较低,生态环境保护与底质修复效果较好.     

氧化亚铁硫杆菌生物浸出铅锌硫化矿尾矿及浸出过程中重金属形态分析研究

研究嗜酸性氧化亚铁硫杆菌(Acidithiobacillus ferrooxidans,A.f)对铅锌硫化矿尾矿重金属离子的生物浸出和重金属形态变化有助于了解生物浸出作用的过程变化.通过考察生物浸出体系中不同的矿浆浓度对pH值和浸出尾矿重金属的影响,探究生物浸出过程的重金属形态变化情况.结果表明,生物浸出作用对pH值和尾矿重金属的浸出影响巨大,随着矿浆浓度的增加,pH值下降速率呈现先升高后降低、重金属浸出率也呈现先增加后降低的趋势,最佳的生物浸出矿浆浓度为50 g·L~(-1),Fe和Zn的最佳浸出率分别为85.45%和97.85%.重金属形态分析表明,生物浸出作用对尾矿重金属形态变化产生巨大的影响,随着浸出时间的延长,重金属形态逐渐改变,首先易迁移的重金属被生物浸出,然后稳定的重金属也逐渐被生物浸出.